• Resources Recycling
• /
• v.28 no.1
• /
• pp.62-72
• /
• 2019

Generally, $H_2SO_4$ and Cu metal are used as raw materials for producing copper sulfate. The study relates to a method for producing copper sulfate using electrowinning from a waste solution of copper chloride. Uses are used for copper plating for industry, plating, feed, agriculture, electronic grade PCB. Conventional methods for producing copper sulfate have a problem of a large amount of waste water and a high energy cost. A study on the production method of copper sulfate ($CuSO_4$), which is the most used among copper (Cu) compounds, has a low process operation ratio, a small amount of waste water, and a simple manufacturing process. It is easy to remove Na, Ca, Mg, and Al as impurities by using a cationic membrane. At the same time, high purity copper powder could be recovered by an electrowinninng method. Using the recovered copper powder, high purity copper sulfate could be produced.

• Polymer(Korea)
• /
• v.34 no.2
• /
• pp.126-132
• /
• 2010

A cation-exchange nanofiber poly(vinylidene fluoride) (PVdF) membrane was prepared by a radiation-induced graft polymerization (RIGP) of sodium styrene sulfonate (NaSS) in the presence of the polymerizable access agents in methanol solution. The used polymerizable access agents include styrene, acrylic acid, and vinyl pyrrolidone. The anion-exchange nanofiber PVdF membrane was also prepared by RIGP of glycidyl methacrylate (GMA) and its subsequent chemical modification. The successful preparations of cation- and anion-exchange PVdF membranes were confirmed via SEM, XPS and thermal analysis. The content of the grafting yield, ion-exchange group, and water uptake was in the range of 30.0~32.3%, 2.81~3.01 mmol/g and 66.6~147%, respectively. The proton conductivity at 20$^{\circ}C$ was in the range of 0.020~0.053 S/cm. From the result, the prepared ionexchange PVdF membrane can be used as a separator in battery cells.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1997.10a
• /
• pp.137-138
• /
• 1997

1. 서론 : 이온교환막이란 합성 폴리머의 이온교환수지를 막상으로 만든 것으로 고분자 매트릭스에 특정 전하가 고정되어 있어 이러한 성질 때문에 보통의 격막에서는 볼 수 없는 특징을 가지고 있으며 바닷물의 농축에 의한 소금의 제조, 탈염에 의한 공업용수 및 음료수의 제조, 도금공장의 폐수처리, 식품과 의약품공업, 고체 고분자 전해질에 근거한 수소생성 등에서 폭넓게 이용되고 있다. 본 연구에서는 상용막에 대체가능한 이온교환막을 제조하기 위하여 내열성, 내약품성, 내산성과 우수한 기계적성질 등을 가지고 있어 membrane 소재로 널리 사용되는 polyethersulfone(PES)를 술폰화시켜 sulfonated PES를 합성한 후 양이온 교환막을 제조하여 특성을 분석하였다.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1998.10a
• /
• pp.118-119
• /
• 1998

이온교환막은 내부세공에 양이온이나 음이온이 막물질의 일부로서 고정된 구조를 가지고 있어 보통의 격막에서는 볼 수 없는 특징을 가지고 있으며 바닷물의 농축에 의한 소금의 제조, 탈염에 의한 공업용수 및 음료수의 제조, 도금공장의 폐수처리, 식품과 의\ulcorner품공자, 고체 고분자 전해질(solid polymer electrolyte)에 근거한 수소생성 등에서 폭넓게 응용되고 있다. 본 연구에서는 상용막에 대체가능한 이온교환막을 제조하기 위하여 내열성, 내약품성, 내산성과 우수한 기계적성질 등을 가지고 있어 membrane 소재로 널리 사용되는 polyethersulfone(PES)를 술혼화시켜 sulfonated PES를 합성한 후 양이온 교환막을 제조하여 특성을 분석하였다.

• Resources Recycling
• /
• v.26 no.6
• /
• pp.65-72
• /
• 2017

APT (Ammonium paratungstate) is widely used in various industries such as metal cutting tools, drill bits, mining tools, and military inorganic materials. In order to produce high purity APT(S), an impurity purification step in an aqueous $Na_2WO_4$ convert $H_2WO_4$ solution is required. It is difficult to remove impurity Na of 200 ppm or less when $H_2WO_4(S)$ is prepared by adding HCl(Aq) to an aqueous solution of $Na_2WO_4$, which is a well-known conventional wet method. However, in this study, a more economical and efficient method of removing Na through electrodialysis using a cationic membrane was studied. A large amount of Na in aqueous solution of $H_2WO_4$ due to $Na_2CO_3(S)$ which was added to dissolve waste tungsten carbide drill and scrap was removed to 20ppm or less through electrodialysis process, and it was confirmed that the effect of Na removal was great when using electrodialysis.

• Applied Chemistry for Engineering
• /
• v.4 no.2
• /
• pp.393-402
• /
• 1993

Redox flow secondary battery have been studied actively as one of the most promising electrochemical energy storage devices for a wide range of applications, such as electric vehicles, photovoltaic arrays, and excess power generated by electric power plants. In all-vanadium redox flow battery using solution of vanadium-sulfuric acid as a active material, the difficulty in developing an efficient ion selective membrane can still be identified. The asymmetric cation exchange membrane(M-30) as a separator of all-vanadium redox flow battery which were obtained by the reaction of chlorosulfonation for 30 minutes under the irradiation of UV, showed its superiority in the transport number of 0.94 and electrical resistivity of $0.5{\Omega}{\cdot}cm^2$. The base membrane were prepared by lamination a low density polyethlene film of $10{\mu}m$ thickness on polyolefin membrane(HIPORE 120). The electrical resistivity of M-30 membrane in real solution of vanadium-sulfuric acid was $3.79{\Omega}{\cdot}cm^2$ and it was similar to that of Nafion 117 membrane. Also the cell resistivity was $6.6{\Omega}{\cdot}cm^2$and lower than that of Nafion 117. In considertion of electrochemical properties and costs of membranes, M-30 membrane was better than that of Nafion 117 and CMV of Asahi glass Co. as a separator of all-vanadium redox flow battery.