• Journal of the Korean institute of surface engineering
• /
• v.32 no.1
• /
• pp.31-42
• /
• 1999

The effect was investigated that aluminium in the zinc bath has on the coating adhesion of Hot-rolled Galvanized Iron(HGI) manufactured without pickling process. It is thought that the coating adhesion of HGI manufactured without pickling process is good due to the fact that increasing aluminium content in the zinc bath makes zinc and aluminium diffuse to the cracks or pores in the scale formed through the reduction heat treatment, and Fe-Zn-Al compound with good ductility is formed in the scale layer and plays a role of anchor between zinc coating and substrate. It is possible that HGI with the good coating adhesion was produced without pickling treatment in the zinc bath with more that 3wt% of Al content even at the $550^{\circ}C$ of conventional reduction heating temperature. In creasing the temperature of heating section and aluminium content in the zinc bath prevents the Zn-Fe alloy. The corrosion resistance of HGI manufactured without pickling process is excellent because of the mixed reaction of zinc sacrifice and aluminium passivity film.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.30-30
• /
• 2018

스마트 도금공장을 구축하기 위해서는 도금액 내부의 화학 물질 농도 변화를 측정할 수 있는 화학 센서 기술이 필수적으로 요구된다. 와트욕은 대표적인 고속 니켈 도금액 중 하나로 기본적으로 황산니켈, 염화니켈, 보릭산의 염과 함께 케리어(type-1 광택제), 광택제(type 2-광택제), 응력 제어제 등의 유기 첨가제로 구성되어 있다. 이러한 유기 첨가제는 전차된 니켈층의 두께 균일도, 조도, 미세 구조, 내부 응력 등 다양한 특성을 제어하며, 정밀한 농도 관리가 필수적으로 요구되나, 분석 기술의 부재로 인하여 지금까지도 대부분의 액관리는 할셀법이나 작업자의 경험에 의존하고 있다. Cyclic voltammetry stripping(CVS) 방법은 전기화학 분석 과정에서 나타나는 첨가제의 가속, 감속 특성 등과 여기에 수반되는 stripping peak의 변화를 이용하여 개별 첨가제의 농도를 측정하는 방법이며, 지금까지 인쇄회로기판의 비아필 공정, 전해 동박 제조, 반도체 배선 등 구리도금 산업 전반에 걸쳐 첨가제 관리에 효과적으로 적용되고 있다. 그러나 수소 발생으로 인한 stripping 효율 문제로 인하여 니켈, 주석, 아연 등 표준 환원 전위가 높은 금속 도금액 내부 첨가제 농도 측정은 아직 어려운 상황이다. 본 연구에서는 이 문제를 극복하기 위해 염소를 과량 첨가한 구리 도금액을 CVS 분석의 base 용액으로 이용하여 니켈 도금액 내부 여러 광택제 (polyetylene glycol(PEG) 계열, thiourea 계열, 2-butyne-1,4-diol 등) 농도를 측정하는 법을 제시하였다. 제시된 방법은 CVS 분석 과정에서 구리-염소 사이의 상호 작용으로 인해 생성되는 3가지 stripping peak의 상대적인 크기 변화가 첨가제 농도에 따라 영향을 받는다는 사실에 기반하였다. 본 연구에서는 여기에 관한 원인에 대해 고찰하였으며, 제시된 방법을 통해 광택제 계열 첨가제 농도 측정을 선택적으로 할 수 있다는 것을 증명하였다.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.4
• /
• pp.547-554
• /
• 1999

The interfacial reaction, spangle and coating thickness of galvanized steel in Ni added Zn-0.18Al bath have been investigated. The size of spangle and thickness of reaction layer were observed under an optical microscope, SEM and EDS. Analysing the experimental results concerning spangle size of galvanized steel it was found that Ni addition in Zn-0.18Al bath tended to be minimized spangle size. For Zn-0.18Al bath, addition of 0.1Ni suppressed the formation of Fe-Zn intermetallic compounds but increased with Ni content above 0.1%. The coating thickness of galvanized steel was reduced with Ni addition in Zn-0.18Al bath, especially in Zn-0.18Al-0.05Ni bath. Addition of Al in Ni containing bath resulted in forming the Al-Ni intermetallic compounds such as $Al_3$Ni$_2$ and $Al_2$Ni which consist most of top precipitates.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.5
• /
• pp.387-397
• /
• 2000

Antimony in the galvanizing bath had greater effect on the growth of grains in the solidification of molten coating layer and on the decrease of its surface roughness than lead. Particularly 0.01 wt % antimony in the galvanizing bath showed much stronger effect than expected considering its low surface tension value. These effects were seemingly originated from the development of preferred orientation of (0002) plane parallel to steel surface. Antimony was found to be widely distributed in form of orderly arrangement throughout the coating layer unlike lead from the results of surface analyses on coating layers as received and on those as etched in chromating solution. In addition, supercooling in the 0.07 % antimony and the 0.2 % lead galvanizing bath was also measured to be in the range of$ 2~4^{\circ}C$ and $9~11^{\circ}C$ respectively, and it indicates that antimony forms fine dendrite expanded rapidly on the steel surface.

• Journal of the Korean institute of surface engineering
• /
• v.13 no.1
• /
• pp.3-7
• /
• 1980

The crystalline structure and leveling action on the deposit of zinc from the cyanide zinc electroplating bath containing organic additives, such as aldehydes, polymers, amines and condensed product, have been studied by microscope and X-ray diffraction methods. The crystalline structure of the deposit from the bath containing no-additive, polymers and aldehydes appeared very strong orientation on (101) plane and the surface was rough, while from condensed product having remarkable effects in brightness appeared very strong orientation on (110) and the crystallinity was very fine. In the leveling action, the effect of any additives except reaction product was not appreciable, whereas the effect of the reaction product obtained remarkably excellent result.

• Journal of the Korean institute of surface engineering
• /
• v.12 no.3
• /
• pp.174-179
• /
• 1979

The effects of brightness, electrochemical behaviour on the organic additives, such as aldehydes, polymers, amines and condensed product obtained from epichlorohydrin and nicotinamide, in cyanide zinc electrolplating bath have been studied by controlled potential electrolyser. The results were summerized as follows: (1) It was found that the addition of only one compound of these organic compounds in the bath was unsuitable but mixture of anisaldehyde or monoethanolamine and condensed product as suitable as brightener. (2) The cathodic polarization curve of polymers or aldehydes in cyanide zinc electroplating bath was almost the same but the cathodic polarization curve of condensed product remarkable shifted to noble potential more than non-additive curve.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.1
• /
• pp.27-32
• /
• 2015

Advanced high strength steels undergo recrystallization annealing in reducing gas atmosphere before galvanizing to improve mechanical properties. The selective oxidations of elements such as Mn, Si, Cr and Al during annealing decrease wettability of liquid zinc, resulting in bare spots and other defects. In this work, Fe-3wt%Mn steel sheet was annealed at $780^{\circ}C$ for 1200 sec. in 5% $H_2-N_2$ atmosphere and then dipped into zinc bath held at $460^{\circ}C$, which contained 0.2wt% dissolved Al. MnO crystallines in the average size of 200 nm were formed on the surface after annealing. It is estimated that MnO has been detached into bath with the formation and growth of inhibition layer with longer immersion time during galvanizing. No evidence of aluminothermic reduction of MnO has been found in this study.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.4
• /
• pp.204-210
• /
• 2000

The control of dissolved aluminum concentration in the hot dip zinc galvanizing bath is greatly important in producing galvannealed steel sheets. The purpose of present study is to provide basic data for measurement of the aluminum concentration in site in hot dip zinc bath at the temperature of $460^{\circ}C\~500^{\circ}C$ using $CaF_2$ solid electrolyte sensor with three kinds of reference electrode. Good workability and stability of the sensor were confirmed with the $Bi+BiF_3$ reference electrode from the emf measurement. In order to measure the aluminum concentration in Zn-Al bath, the galvanic cell of fluorine ion was constructed with $CaF_2$ solid electrolyte as follows; $$(-)W|Zn-Al,\;AlF_3|CaF_2|Bi,BiF_3|W(+)$$. The emf measurement was made at the temperature of $460\pm10^{\circ}C$ in the Zn-Al bath. The following correlationship between aluminum concentration and emf was obtained by the least square regression analysis; $$E/mV=56.795log[\%Al]+1881.7\;R=0.9704$$,$$0.026wt\%{\leq}[\%Al]{\leq}0.984wt\%$$

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.371-378
• /
• 1998

The zind bate contaminated in the hot dip galvannealed operation was successfully by appling the dross formation mechanism ; the Fe content was lowered from 0.028% to 0.011% and the dress size was decreased from 15~20$\mu\textrm{m}$ to under 3$\mu\textrm{m}$. The cooled metal from CGL zinc bath during operation of the galvannealed steel strip was remelted in graphite crucible at the lab and agitated after increasing Al content from 0.14% to 0.16% with decreasing the molten metal temperature from $470^{\circ}C$to $445^{\circ}C$. The agitating was done by agitator and nitrogen. The molten was analyed by SEM and EDS. It was considered that the Fe and the bottom dross($FeZN_7$) could react with aluminium to from the float dress($Fe_2Al_5$) according to the molten metal temperature down and the float dress rise to the surface of the zine bath. So the Fe and dross in the bath could be romoved out of the bath. It was confirmed that the proper purication conditions of GA zine bath is 0.02% of Al increasing, bath temperature down from $460^{\circ}C$ to $450^{\circ}C$and agitator and nitrogen.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.3
• /
• pp.206-214
• /
• 2001

The purpose of this study is to determine the effects of Ni on precipitate formation in a Ni added galvanizing bath, which has various Ni content from 0.03wt.% to 0.5wt.%. The addition of hi in the Ni containing galvanizing bath resulted in the formation of Al-Ni intermetallic compounds such as $Al_3$$Ni_2$ and $Al_2$Ni, which make up most of the top precipitates. At 0.07wt.%Ni, Al-Ni intermetallic compound formed sensitively with small amount of Al addition. By analysing the reaction thickness of galvanized steel, it was found that Ni addition in a Zn-0.18w1.%Al bath tended to suppress the formation of Fe-Zn intermetallic compounds but the formation of these compounds increased with increasing Ni concentration above 0.1wt.%.