• Journal of the Korea Concrete Institute
• /
• v.14 no.5
• /
• pp.742-749
• /
• 2002

This study was performed to clarify the formation procedure of continuous voids in cellular concrete, and to examine the effect of a foaming agent on the manufacture of cellular concrete with continuous voids. By the experiments, it was determined that cellular concrete to be formed with continuous voids is influenced by temperature, viscosity and flowability of cement paste, and stability of air voids, and is formed in accordance with cohesion of air voids. It was also found that separate voids are formed at an added amount of air voids corresponding to 2 ％ or less of the amount of cement, whereas an antifoaming phenomenon occurs when the added amount of air voids exceeds 9 ％ of the amount of cement. In products with respective cement fineness of 3,000, 6,000, and 8,000㎠/g, a higher compressive strength was exhibited at a higher cement fineness. The continuous void ratio depending on a variation in fineness was 38 ％, 52 ％, and 22 ％ in those products, respectively. That is, a highest continuous void ratio was exhibited at a cement fineness of 6,000㎠/g. When the water-cement ratio was reduced from 45％ to 25％, the compressive strength of the cellular concrete was increased from 15 kgf/㎠ to 20 kgf/㎠ Thus, the reduction in water-cement ratio was effective in achieving an increase in strength without any variation in the specific gravity of the cellular concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.6
• /
• pp.727-738
• /
• 2023

In concrete, the interface between the aggregate and cement paste is often the most critical factor in determining strength, representing the weakest zone. Lightweight aggregate, produced through expansion and firing of raw materials, features numerous surface pores and benefits from low density; however, its overall aggregate strength is compromised. Within concrete, diminished aggregate strength can lead to aggregate fracture. When applying lightweight aggregate to concrete, the interface strength becomes critical due to the potential for aggregate fracture. This study involved coating the surface of the aggregate with blast furnace slag fine powder to enhance the interfacial strength of lightweight aggregate. The impedance of test specimens was measured to analyze interface changes resulting from this surface modification. Experimental results revealed a 4% increase in compressive strength following the coating of the lightweight aggregate surface, accompanied by an increase in resistance values within the impedance measurements corresponding with strength enhancement.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.3
• /
• pp.93-100
• /
• 2005

The purpose of this study is to investigate the physical properties of porous concrete according to the aggregate shape and size which is produced by con crusher and impact crusher. For this purpose, the selected test variables were the aggregate size and shape, the ratio of water to cement and the ratio of paste to aggregate. The results of this study showed that its economic performance and physical properties were improved using the aggregate made by impact crusher. The coefficient of permeability and compressive strength of porous concrete had a close correlationship with the void ratio, and it was suggested as a function of void ratio.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.1
• /
• pp.96-100
• /
• 2009

The properties of recycled fine aggregates which had different source concrete were examined by mortar test. With higher strength of source concrete, specific gravity of recycled fine aggregate was higher and absorption of recycled fine aggregate was lower due to reduction of the volume of adhered cement paste. The compressive strength and flexible strength of mortar with recycled fine aggregate were affected by the interface boundary of new mortar and the strength of adhered mortar. Strength development of mortar with recycled fine aggregate reduced because recycled fine aggregate become a porous material with the smaller strength of source concrete. The drying shrinkage of mortar was about$800{\sim}2000{\mu}m/m$. It was about 1.5 times than that of mortar with natural fine aggregate. Relative dynamic modulus of elasticity was a similar level with that of mortar with natural fine aggregate.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.4
• /
• pp.1-9
• /
• 2020

This study conducted to understand effects of CA (CaAl₂O₄) and CA₂ (CaAl₄O₇) ratio on chloride binding ability and compressive strength and pore structure of cement mortar incorporating mixture of CA and CA₂. The Portland cement based specimens were mixed with the clinkers CA and CA₂, and these calcium aluminate clinker mixture were replaced 0, 5, 10% by weight of cement. After all the test specimens were cured for 28 days under water curing, they were immersed in the distilled water and NaCl solution. As a result, 28 days compressive strength of all specimens was similar, and As the replacement ratio of calcium aluminate clinker in the specimen increased, Friedel's salt production tended to increase. However, it was dependent on the amount of Al₂O₃ in the level of 5% replacement and CA ratio in the level of 10% replacement. Through equilibrium isotherm result, it was also indicated that as replacement ratio of calcium aluminate clinker in cement matrix increased, chloride binding capacity was improved, and chloride penetration was suppressed. In this study, the specimen replaced with 10% of the calcium aluminate clinker mixture (CA 39%, CA₂ 60%) was remarkable to control chloride attack. We figured out necessity to understand optimal CA/CA₂ ratio to effectively apply CA₂ as a sustainable building material by improving the chloride binding ability in Portland cement based system.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.2
• /
• pp.219-226
• /
• 2020

Over the last decades, great efforts have been devoted to reuse industrial wastes and by-products from various industries as supplementary cementitious materials in order to reduce carbon dioxide(CO₂) emission by reducing the use of Portland cement in construction. Oyster shell waste, originating from the fishery industry, is available in huge quantities in certain areas, and is generally discarded or landfilled. In this study, we aimed to reuse oyster shell as an alternative to limestone in limestone calcined clay cement(LC³). The oyster shell calcined clay cement(OC³) paste were produced and were characterized via X-ray diffraction, isothermal calorimetry, compressive strength tests, and thermogravimetry. The results revealed that OC³ pastes exhibited similar strength development and reactivities by pozzolanic reaction with LC³, which implies that oyster shell could be used as a substitute for limestone in LC³.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.6
• /
• pp.489-495
• /
• 2020

Whereas the control of the hydration heat in mass concrete has been important as the concrete structures enlarge, many conventional strategies show some limitations in their effectiveness and practicality. Therefore, In this study, as a solution of controling the heat of hydration of mass concrete, a method to reduce the heat of hydration by controlling the hardening of cement was examined. The reduction of the hydration heat by the developed Phosphate Inorganic Salt was basically verified in the insulated boxes filled with binder paste or concrete mixture. That is, the effects of the Phosphate Inorganic Salt on the hydration heat, flow or slump, and compressive strength were analyzed in binary and ternary blended cement which is generally used for low heat. As a result, the internal maximum temperature rise induced by the hydration heat was decreased by 9.5~10.6% and 10.1~11.7% for binder paste and concrete mixed with the Phosphate Inorganic Salt, respectively. Besides, the delay of the time corresponding to the peak temperature was apparently observed, which is beneficial to the emission of the internal hydration heat in real structures. The Phosphate Inorganic Salt that was developed and verified by a series of the aforementioned experiments showed better performance than the existing ones in terms of the control of the hydration heat and other performance. It can be used for the purpose of hydration heat of mass concrete in the future.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.5
• /
• pp.131-139
• /
• 1994

The min aim of thls study was to evaluate the effect of particle slze of the fly ash as a cement additive. Experimental work was carried out with three different sizes of fly ash. 18.58, 8.95 and 4.02{$mu}m$ in average radius. Namely, the effect of particle size variation of fly ash on the physical properties of cement paste was investigated. The jluidity was decreased with increasing the addition of fly ash to cement paste regardless of the particle size variation. The decrement of the fluidity of the pulverized fly ash was higher than that of the spherical fly ash. On the other hand, the pozzolan reactivity increased with lowering particle size. In the case of specimens with 5% up to 10% addition of fly ash having a particle size of 4.02{$mu}m$. the compressive strength was increased as compared with the plain specimens before curing for 28 days and showed higher value above 800kg /$cm^2$ when cured for 60 days.This increased compressive strength was ascribed to both the closer packlng of fine particles and the pozzolan reactivity of fly ash. These results were comfirmed by measuring both the porosity of the specimens and Ca(OH ), contents remained in specimens. This work showed that could be effectively ut~lized as a blending material without any de crease in the strength of early hydration stage if we can control the particle size of fly ashes by sizing or pulverizing.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.490-497
• /
• 2020

This work has been initiated to find possibility whether recycled fine aggregate can be used as a source of aggregate for structural concrete or not. Two-stage mixing approach was chosen in order to maximize strength potential from recycled fine aggregate. Moisture content of the recycled fine aggregate was changed, and two different types of two-stage mixing approaches were applied to produce cement mortar. The strength of mortar made of 100% recycled fine aggregate by two-stage mixing approaches was compared to that of mortar made of 100% washed sea sand. According to the results, the effect of moisture content on compressive strength was observed from low water cement mortar(W/C 0.3). In case of W/C 0.5 cement mortar, no clear relationship was observed between moisture content and strength development. It was found that two-stage mixing approach has a potential to increase the strength of mortar made of 100% recycled fine aggregate. In case of modified version of two-stage mixing approach which first prepares cement paste and pours recycled fine aggregate into the cement paste, was more effective to increase the strength of mortar made of 100% recycled fine aggregate.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.203-210
• /
• 2018

Corrosion of the rebar is one of the main factors affecting the durability of reinforced concrete in the world which lead to the failure of the reinforced concrete structures. In this research, a new method of fixing $CO_2$ is practiced to improve the carbonation resistance of the concrete. Brucite($Mg(OH)_2$), a kind of common $CO_2$ fixation materials, was added into ordinary Portland cement paste. Samples containing 0%, 5%, 10%, and 15% $Mg(OH)_2$ were exposed to an accelerated carbonation curing regime with 20% concentration of $CO_2$, 60% relative humidity, and a temperature of $20^{\circ}C$ until tested at 3d, 7d, 14d and 28d. After 28d of $CO_2$ accelerated curing, in the paste containing $Mg(OH)_2$, magnesian calcite was detected by SEM-EDX. Meanwhile, the paste containing $Mg(OH)_2$ exhibit the better pore distribution than ordinary Portland cement paste and the compressive strength of the cement paste containing $Mg(OH)_2$ were more than 50Mpa.