• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.481-486
• /
• 1999

According to results of this research Fly-ash Cement permanent-form production was found to be possible by fly-ash mortal. The compress strength 350kg/$\textrm{cm}^2$, banding strength 120kg/$\textrm{cm}^2$ were possible material separting and bleeding by excessive W/C rate was decreased permanent-form made by polymer solved high price of polymer by fly-ash. Model material was made by result of first research. There were no minute-crack on beam form and out surface of form was very smooth, So filling degree seemed desirable length of form after steaming curing was maintained as expected. with these results production of form seemed possible. In the banding load test, fly-ash showed increase of maxim load 12% than RC. in the case of minute-crack, comparing with RC, fly-ash showed no crack at connect. at the first stage under continuing loading size of crack increased. These phenomena seemed to be based on contribution of stress of inner bars in permanent-form. in the test of defection, fly-ash shower about 10% beam load increase than RC. in the case of beam defection, RC showed sudden decrease of tolerance at maxim load and total breaking, but permanent-form showed breaking of bending maintaining defection with contribution of steel stress ($\Phi$6 wire-mash). There phenomenic seemed to be attributed to increase of surface and steel tolerance of form. According to construction explacemaion, it was guessed that each panel was constructed by conner-steels in form edge. so cohesiveness was small. on these bases. keeping width of horizontal band 30cm, form-panel of 20mm width was found to be of use. Permanent-form was found to be efficient in compressibleness, defection, safety and use of Fly-ash mortal.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.725-728
• /
• 2008

Most of shrinkage is mainly caused by autogenous shrinkage in Ultra high strength steel-fiber reinforced cementitious composites(UHSFRC). water to binder ratio is very low, about 0.2. It occurs faster hydration and cause a large amount of autogenous shrinkage in early ages. the large autogenous shrinkage can cause harmful cracks in a structure and deteriorate the designed structural performance. therefore it is very important to predict the autogenous shrinkage accurately. The study about the autogenous shrinkage of UHSFRC was carried out in this paper. through comparing with JSCE recommendations for UHSFRC, it was found out that UHSFRC in this study showed higher autogenous shrinkage than that of JSCE. And Applicability of early proposed models by some researchers was also investigated. the analytical results let us know that Miyazawa's model showed the best agreement with the experimentally obtained autogenous shrinkage of UHSFRC.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.223-230
• /
• 2002

The main intent of this research was to determine the feasibility of utilizing recycling bottom ash as CLSM (controlled low-strength material). CLSM is a cementitious material, commonly a blend of portland cement, fly ash, sand, and water, that is usually flowable and self-leveling at the time of placement. The durability characteristics of mixtures made bottom ash we compared with those of fly ash CLSM in order to evaluate the effectiveness and suitability of bottom ash as material in CLSM. A comprehensive evaluation of the bottom ash in CLSM and mix proportions indicated that the bottom ash are capable of performing as CLSM mixtures. The durability characteristic of CLSM incorporating the bottom ash under various physical and chemical causes of deterioration were investigated. Test results indicated that CLSM using bottom ash has acceptable durability performance. CLSM incorporating with bottom ash were also found to be environmentally safe.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.395-402
• /
• 2017

Recently, many researches on crack healing and repairing technique using bacteria which can produce vital-reacted calcite have been proposed. This study is for a basic research on repair material with slime formation through bacteria and deals with durability evaluation for coating materials containing bacteria-forming slime. For the work, 4 types of bacteria (Rhodobacter capsulatus, Rhodopseudomonas palustris, Bacillus thuringiensis, and Bacillus subtilis) and 2 types of nutrient conditions are considered, and several tests covering strength evaluation under sulfate condition, accelerated chloride diffusion, and UV (Ultrasonic Velocity) measurement are performed. Strength improvement in coating materials containing bacteria is evaluated in spite of even exposure to sulfate attack to 7 days. Chloride diffusion coefficient and UV properties are also improved except for the case of Rhodopseudomonas palustris. With resistance of slime to long term exposure and aerobic conditions for bacteria longevity, the proposed bacteria shows an engineering feasibility for repair material of RC structure exposed harsh environment.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.32 no.6A
• /
• pp.419-426
• /
• 2012

Fresh concrete has 10~20% extra water in it. As those water remain entrapped air in the concrete, life span of structures is reduced. For that reason, if extra water is eliminated, it will be useful to improve the durability of the structures. Though there were many reports about permeable formwork, the study on the properties of permeable liner itself has been insufficient. In addition, making holes on the form causes lowering of workability. Therefore, this study reviewed the properties of woven and non-woven permeable liner and formwork which has no holes on the form. For the woven and non-woven permeable liner, they showed great application with W/C decrease, lowering roughness, increased compressive strength of surface area and slight loss of cement paste, when the were applied to concrete. In addition, they showed different performance according to the density of woven liner or thickness of non-woven liner. Furthermore, when using the draining non-woven permeable liner which has drainage path inside, concrete surface showed required performance with high workability, without drilling the holes on the form.

• International Journal of Highway Engineering
• /
• v.1 no.1
• /
• pp.85-96
• /
• 1999

This study was performed to evaluate performance of polymer-modified asphalt mixtures and specially designed reinforcement techniques against reflection cracking of the asphalt pavement overlay. Selected polymers were used for asphalt modification and polyester fiber, a polypropylene film (vinyl) and a grid were used for mixture reinforcement. Using the asphalt mixture with optimum asphalt content, a slab was made and cut into two pieces of specimen. A layer of grid or vinyl was placed at the bottom of specimen to strengthen the pavement layer against crack. A repeated loading was applied to the asphalt mixture specimen which is Placed on a cement concrete with a pseudo-crack. Crack propagation under repeated loading was monitored and effectiveness of the devised crack retarding techniques was evaluated. From the test results. a significant retardation of mode I crack progress was monitored from some of the modified and reinforced asphalt mixtures.

• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.577-584
• /
• 2012

Carbonation resistance is one of the most influencing factors on durability of concrete. Alkali activated slag (AAS) is known to have weaker resistance for carbonation than OPC due to the low calcium contents. In this paper, the carbonation characteristic of AAS mortar which is related to the basicity (CaO/$SiO_2$) was investigated. In order to give the various basicity conditions, SM (source material) was blended with quicklime (CaO) and silicon dioxide ($SiO_2$) by adopting mechano-chemical treatment method. Experiments including flow test, compressive strength test, carbonation depth test, together with XRD, FTIR and TGA were employed to evaluate the effects of basicity of SM on the carbonation characteristics. The test results showed that the carbonation resistance effectively increased with the increase of the basicity of SM.

• Journal of the Korea Concrete Institute
• /
• v.25 no.5
• /
• pp.565-572
• /
• 2013

Hydration and physical characteristics of chemically-bonded phosphate ceramic (CBPC) binder based on dead-burned Mg-O with six different blends are investigated for efficient repair construction material by retarding set phase with $H_3BO_3$. The test specimen of the blender with silica fume shows higher compressive strength after 75 days. The CBPC with silica fume results in higher modulus of rupture that others. The test specimens of CBPC eludes lower calcium ion than that of OPC (Ordinay Portland Cement). The X-ray diffraction pattern shows that hydration results in the formation of magnesium hydroxide, M-S-H gel and $MgCO_3$ for the specimen with silica fumes. Combination with calcium for MgO is not desirable due to no formation of chemical bond between two components. Based on the experimental program, the mixture of MgO and silica fume shows efficient performance in strength and durability.

• Resources Recycling
• /
• v.27 no.3
• /
• pp.86-92
• /
• 2018

The amount of construction waste generated is steadily increasing every year, and the Law for Promotion of Recycling is enacted. However, it is difficult to use it as a recycled aggregate for concrete, which is presented in the quality standard of recycled aggregate with high water uptake and low density due to low separation of aggregate between concrete and cement paste. Therefore, in this study, a multi-stage impact crusher was used to remove mortar, which is essential for improving the quality of recycled aggregate. In analyzing the characteristics of the equipment, the spectrum of energy generated in each part between the particle and the equipment was calculated by using DEM. In order to generate an effective separation phenomenon, it was confirmed that the operation condition of 900 RPM was appropriate based on the ratio of the number of collisions (L/H) of the low energy group (L) to the number of collisions of the high energy group (H).

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.2
• /
• pp.107-114
• /
• 2014

The objective of this study is to evaluate the strength development of blast furnace slag concrete in response to the use of recycled aggregate as alkali activator. The influence of the amount of recycled aggregate was evaluated depending on different ratios of replacement for each RFA and RCA to NFA and NCA, respectively. The results indicated that as replacement of RFA and RCA increased, their strength exhibited to be increased. This was due to the fact that the latent hydraulic properties of blast furnace slag was activated by the alkali in recycled aggregates. However, in case of 365-days, it showed lower compressive strength than using NA(natural aggregates) which could be explained as the exhaustively use of alkali containing in RA. The specimens using RA showed about 90% of compressive strength comparing with specimens using NA.