• The Journal of Korea Institute of Information, Electronics, and Communication Technology
• /
• v.16 no.4
• /
• pp.187-192
• /
• 2023

This paper deposited CdTe thin films on ITO glass substrates using sputtering equipment while changing RF power. As a result of measuring the thickness of the thin film, 1481Å at 100W, 2985Å at 150W, and 4684Å at 200W. And the mobility was measured as 8.43 cm2/Vs for 100W, 7.91 cm2/Vs for 150W, and 6.57 cm2/Vs for 200W. It can be seen that the thickness and mobility of the thin film are inversely proportional. As a result of confirming the transmittance, the transmittance was 84% at 905nm for 100W, the transmittance was 71% at 825nm for 150W, and 77% at 874nm for 200W. At 100 W, the thickness of the thin film was thin, so the transmittance was measured to be high. In other words, the correlation between transmittance and thickness can be seen. As a result of measuring the FHWM and particle size by changing the RF Power, 100W was calculated as 0.18, 150W was calculated as 0.19, and 200W was calculated as 0.73. The size of the particles was formed at 8.47Å at 100W, 7.98Å at 150W, and 8.7Å, which is the largest at 200W. In conclusion, it was found that the FHWM and particle size were inversely proportional.

• Journal of the Microelectronics and Packaging Society
• /
• v.31 no.1
• /
• pp.29-34
• /
• 2024

The heating element utilizing the Joule heating generated when current flows through a conductor is widely researched and developed for various industrial applications such as moisture removal in automotive windshield, high-speed train windows, and solar panels. Recently, research utilizing heating elements with various nanostructures has been actively conducted to develop flexible heating elements capable of maintaining stable heating even under mechanical deformation conditions. In this study, flexible polyurethane possessing excellent flexibility was selected as the substrate, and silver (Ag) thin films with low electrical resistivity (1.6 μΩ-cm) were fabricated as the heating layer using magnetron sputtering. The 2D heating structure of the Ag thin films demonstrated excellent heating reproducibility, reaching 95% of the target temperature within 20 seconds. Furthermore, excellent heating characteristics were maintained even under mechanically deforming environments, exhibiting outstanding flexibility with less than a 3% increase in electrical resistance observed in repetitive bending tests (10,000 cycles, based on a curvature radius of 5 mm). This demonstrates that polyurethane/Ag planar heating structure bears promising potential as a flexible/wearable heating element for curved-shaped appliances and objects subjected to diverse stresses such as human body parts.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.599-604
• /
• 1998

We have investigated Pt and $RuO_2$ as a bottom electrode for ferroelectric capacitor applications. The bottom electrodes were prepared by using an RF magnetron sputtering method. Some of the investigated parameters were a substrate temperature, gas flow rate, RF power for the film growth, and post annealing effect. The substrate temperature strongly influenced the surface morphology and resistivity of the bottom electrodes as well as the film crystallographic structure. XRD results on Pt films showed a mixed phase of (111) and (200) peak for the substrate temperature ranged from RT to $200^{\circ}C$, and a preferred (111) orientation for $300^{\circ}C$. From the XRD and AFM results, we recommend the substrate temperature of $300^{\circ}C$ and RF power 80W for the Pt bottom electrode growth. With the variation of an oxygen partial pressure from 0 to 50%, we learned that only Ru metal was grown with 0~5% of $O_2$ gas, mixed phase of Ru and $RuO_2$ for $O_ 2$ partial pressure between 10~40%, and a pure $RuO_2$ phase with $O_2$ partial pressure of 50%. This result indicates that a double layer of $RuO_2/Ru$ can be grown in a process with the modulation of gas flow rate. Double layer structure is expected to reduce the fatigue problem while keeping a low electrical resistivity. As post anneal temperature was increased from RT to $700^{\circ}C$, the resistivity of Pt and $RuO_2$ was decreased linearly. This paper presents the optimized process conditions of the bottom electrodes for memory device applications.

• Korean Journal of Materials Research
• /
• v.10 no.3
• /
• pp.199-203
• /
• 2000

$Ta_2_O5$ and $Sr_0.8Bi_2.4Ta_2O_9$ films were deposited on p-type Si(100) substrates by a rf-magnetron sputtering and the metal organic decomposition (MOD), respectively.The electrical characteristics of the $Pt/SBT/Ta_2O_5/Si$ structure were obtained as the functions of $O_2$ gas flow ratio during the $Ta_2_O5$ sputtering and $Ta_2_O5$ thickness. And to certify the role of $Ta_2_O5$ as a buffer layer, the electrical characteristics of $Pt/SBT/Ta_2O_5/Si$ were compared. $Pt/SBT/Ta_2O_5/Si$ capacitor with 20% $O_2$ gas flow ratio during the $Ta_2_O5$ sputtering did now show typical C-V curve of metal/ferroelectric/insulator/semiconductor (MFIS) structure. The capacitor with 20% $O_2$ gas flow ratio during the $Ta_2_O5$ sputtering had the largest memory window. And the memory window was decreased as the $Ta_2_O5$ gas flow ratio during the $Ta_2_O5$ sputtering was increased to 40%, 60%. In the C-V characteristics of the $Pt/SBT/Ta_2O_5/Si$ capacitors with the different $Ta_2_O5$ thickness, the capacitor with 26nm thickness of $Ta_2_O5$ had the largest memory window. The C-V and leakage current characteristics of the Pt/SBT/Si structure were worse than those of $Pt/SBT/Ta_2O_5/Si$ structure. These results and Auger electron spectroscopy (AES) measurement showed that $Ta_2_O5$ films as a buffer layer tool a role to prevent from the formation of intermediate phase and interdiffusion between SBT and Si.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.368-370
• /
• 2013

투명 전극은 전기전도도를 갖는 동시에 가시광선을 투과하는 소재를 말하며, 구체적으로는 빛의 파장이 400~700 nm 영역대의 가시광선을 80% 이상 투과하며 전기전도도가 비저항으로 $10^{-3}{\Omega}cm$이하이거나 면저항이 $10^3{\Omega}$/${\Box}$소재를 의미한다. 투명 전극은 전기전도도에 따라 사용되는 용도가 다양하다. LCD, PDP, OLED 와 같은 평판디스플레이 및 3D 디스플레이의 투명전극으로 사용되는 핵심재료일 뿐만 아니라 터치스크린, 투명필름, 대전방지막, 열반사막, EMI 방지막, 태양전지 분야에 광범위하게 이용되고 있다. 일반적으로, 투명전극 박막에 가장 많이 사용되고 있는 소재는 ITO (indium tin oxide)이나, 주성분인 In의 사용량 증가로 상용 ITO 타겟 가격이 급등하고 있음으며, 고가의 ITO 타겟을 대체하기 위한 저가의 투명전극 소재 개발이 절대적으로 요구되며, 신규 소재 개발을 통한 기술력 우위 선점이 필수적으로 요구되는 상황이다. 본 연구에서는 기존에 디스플레이 분야에서 널리 활용되는 고가의 ITO를 대체하기 위한 다성분 금속산화물 투명전극 스퍼터링 타겟 제조기술을 개발하기 위한 연구로서, Metal이 첨가된 In-Ga-Zn-O기반의 3성분계 투명도전성 소재를 조성설계, 고밀도 균질 타겟 제조 및 투명전극 박막을 형성하는 연구를 실시하였다. 고체산화물 산화인듐(In2O3)분말, 산화갈륨(Ga2O3) 분말그리고 산화아연(ZnO)분말과 Metal을 몰비로 칭량한 후 분말을 폴리에틸렌제 포트에 넣고 에탄올을 충분히 채운 후 지르코니아(ZrO2) 볼(ball)을 이용하여 24 h 동안 볼 밀링(ball milling) 방법으로 혼합한 뒤, $120^{\circ}C$의 플레이트위에서 마그네틱 바로 stirring하면서 건조하였다. 이 분말을 건조기에서 완전히 건조한 후 알루미나 유발을 이용해서 pulverizing한 후 sieving기를 이용하여 분말의 조립화를 하였다. 이 분말을 금형에 넣고 300 kg/$cm^2$의 압력으로 press하여 성형한 뒤 대기중에서 소결하였다 소결을 위한 승온 온도는 $10^{\circ}C$/min이었고 소결은 $1,450^{\circ}C$에서 6 h 동안 하였다. IGZO target의 조성 비율은 1:1:12 (mol%)를 사용하였으며, 첨가한 Metal은 Boron (B), Germanium (Ge), Barium (Ba)을 사용하여 타겟을 제작하였다. M-IGZO 박막은RF magnetron Sputter를 이용하여 증착하였으며, 앞선 실험에서 제작한 타겟을 사용하여 M-IGZO박막을 투명전극으로 사용하기 위한 각각의 특성을 파악하였다. 모든 박막은 상온에서 증착을 하였으며, 증착된 박막두께를 측정하기 위해 ${\alpha}$-step IQ를 사용하였고, 광학적 특성을 분석하기 위해 UV-Visible spectrophotometer 로 투과율을 측정하였다. 그리고 전기적 특성을 측정하기 위해 Hall effect measurement 및 4-probe를 사용하였으며, 결정성 분석을 위하여 XRD를 이용하여 분석하였다. 표1은 M-IGZO타겟을 사용하여 증착시간에 따른 면저항 특성을 나타내었다. Ge, B, Ba이 첨가된 IGZO 박막은 증착시간이 증가할수록 면저항이 낮아짐을 알 수 있었다. 또한, Ge이 첨가된 IGZO 박막이 다른 금속이 첨가된 IGZO 박막의 면저항보다 현저히 낮음을 알 수 있었다. Fig. 1(a), (b), (c)는 각 타겟을 동일한 조건으로 증착을 하여 광학적특성을 나타내는 그래프이다. GZO 박막의 광학적 특성을 보면 가시광 영역에서 평균 투과율은 모두 80% 이상으로 우수한 광투과 특성을 보여 투명전자소자로 사용가능하다. 특히, 자외선 영역을 모두 차단하는 UV cut 능력이 우수함을 알 수 있었다. 따라서, 금속이 첨가된 IGZO 박막을 태양전지용 투명전극으로 사용할 경우, 자외선에 의하여 수명이 단축되는 현상을 줄여줄 수 있음을 기대할 수 있으며 내구성 향상에 크게 기여할 것으로 보인다. Fig. 2는 Ge=0, 0.5, 5%인 IGZO 투명전극을 총 40회 반복하여 증착을 실시한 후 각각의 면저항을 측정한 결과이다. 실험결과에 따르면 Ge가 0%, 5%인 IGZO 투명전극은 증착을 거듭할수록 면저항이 증가하는 결과를 나타내었으며, 0.5%인 IGZO 투명전극은 점차 안정화되어가는 결과를 나타내었다. 따라서 안정화 되었을 때 평균 면저항은 26ohm/sq.로 나타났으며, 광투과율은 Fig. 3과 같이 가시광영역에서 평균 80%이상의 결과를 보였으며, 550 nm에서는 86.36%의 우수한 특성을 나타내었다. 본 연구에서는 Metal이 첨가된 In-Ga-Zn-O기반의 3성분계 투명도전성 소재 target을 제작하여 RF magnetron sputter로 박막을 형성한 후 특성을 비교하였다. M-IGZO target 중 Ge (0.5%)을 첨가한 IGZO 타겟을 사용한 투명전극이 가장 우수한 특성을 보였으며, 제작된 M-target의 In 비율이 30% 정도로 기존의 ITO (90%) 대비하여 투명전극 제작 단가를 절감할 수 있다.

• Korean Journal of Optics and Photonics
• /
• v.18 no.5
• /
• pp.351-361
• /
• 2007

The samples composed of a GST thin film and the protective layers of $ZnS-SiO_2$ or $Al_2O_3$ coated on c-Si substrate were prepared by using the magnetron sputtering method. Samples of three different structures were prepared, that is, i) the GST single film on c-Si substrate, ii) the GST film sandwiched by the protective $ZnS-SiO_2$ layers on c-Si substrate, and iii) the GST film sandwiched by $Al_2O_3$ protective layers on c-Si substrate. The ellipsometric constants in the temperature range from room temperature to $700^{\circ}C$ were obtained by using the in-situ ellipsometer equipped with a conventional heating chamber. The measured ellipsometric constants show strong variations versus temperature. The variation of ellipsometric constants at the temperature region higher than $300^{\circ}C$ shows different behaviors as the ambient medium is changed from in air to in vacuum or the protective layers are changed from $ZnS-SiO_2$ to $Al_2O_3$. Since the long heating time of 1-2 hours is believed to be the origin of the high temperature variation of ellipsometric constants upon the heating environment and the protective layers, a PRAM (Phase-Change Random Access Memory) recorder is introduced to reduce the heating time drastically. By using the PRAM recorder, the GST samples are heated up to $700^{\circ}C$ decomposed preventing its partial evaporation or chemical reactions with adjacent protective layers. The surface image obtained by SEM and the surface micro-roughness verified by AFM also confirmed that samples prepared by the PRAM recorder have smoother surface than the samples prepared by using the conventional heater.

• Journal of the Korean Magnetics Society
• /
• v.13 no.2
• /
• pp.53-58
• /
• 2003

Annealing effects of exchange bias fields ($H_{2ex}$(top), $H_{lex}$ (bottom)) on composite type NiFe/[FeMn/Mn]$_{80}$/NiFe multilayers have been studied. Three samples with ultra-thin Mn inserted layers on glass/Ta(50 $\AA$)/NiFe(150 $\AA$)/[F $e_{53}$M $n_{47}$(1.25 $\AA$)/Mn(0 $\AA$, 0.11 $\AA$, 0.3 $\AA$)]$_{80}$/NiFe(90 $\AA$)/Ta(50 $\AA$) were prepared by ion beam sputtering. The average x-ray diffraction peak ratios NiFe(111) of FeMn (111) fcc textures for the Mn inserted total thicknesses of 0 $\AA$, 9 $\AA$, and 24 $\AA$ were about 0.65, 0.90, and 1.5, respectively. For the sample without Mn inserted layer, the $H_{2ex}$ of 260 Oe up to 300 $^{\circ}C$ disappeared at 350 $^{\circ}C$. For two multilayer samples with ultra-thin Mn layers of 0.11 $\AA$ and 0.3 $\AA$, the $H_{2exs}$ of 310 Oe and 180 Oe up to 300 $^{\circ}C$ endured of 215 Oe and 180 Oe at 350 $^{\circ}C$, respectively. The $H_{ex}$ (bottom)s of three samples decreased from 100 Oe to 70 Oe up to 250 $^{\circ}C$, while these values increased beyond 300 $^{\circ}C$. This observation can be attributed to less diffusive path of Mn atoms in bottom NiFe than top NiFe layer. The top and bottom coercive fields slightly varied about 5 Oe∼10 Oe. From these results, we could obtain the enhancement of exchange coupling intensity and thermal stability by an ultra-thin Mn inserted layer on NiFe/[FeMn/Mn]$_{80}$/NiFe Multilayers.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.375-375
• /
• 2010

CdTe as an absorber material is widely used in thin film solar cells with the heterostructure due to its almost ideal band gap energy of 1.45 eV, high photovoltaic conversion efficiency, low cost and stable performance. The deposition methods and preparation conditions for the fabrication of CdTe are very important for the achievement of high solar cell conversion efficiency. There are some rearranged reports about the deposition methods available for the preparation of CdTe thin films such as close spaced sublimation (CSS), physical vapor deposition (PVD), vacuum evaporation, vapor transport deposition (VTD), closed space vapor transport, electrodeposition, screen printing, spray pyrolysis, metalorganic chemical vapor deposition (MOCVD), and RF sputtering. The RF sputtering method for the preparation of CdTe thin films has important advantages in that the thin films can be prepared at low growth temperatures with large-area deposition suitable for mass-production. The authors reported that the optical and electrical properties of CdTe thin film were closely connected by the thickness-uniformity of the film in the previous study [1], which means that the better optical absorbance and the higher carrier concentration could be obtained in the better condition of thickness-uniformity for CdTe thin film. The thickness-uniformity could be controlled and improved by the some process parameters such as vacuum level and RF power in the sputtering process of CdTe thin films. However, there is a limitation to improve the thickness-uniformity only in the preparation process [1]. So it is necessary to introduce the external or additional method for improving the thickness-uniformity of CdTe thin film because the cell size of thin film solar cell will be enlarged. Therefore, the authors firstly applied the chemical mechanical polishing (CMP) process to improving the thickness-uniformity of CdTe thin films with a G&P POLI-450 CMP polisher [2]. CMP process is the most important process in semiconductor manufacturing processes in order to planarize the surface of the wafer even over 300 mm and to form the copper interconnects with damascene process. Some important CMP characteristics for CdTe were obtained including removal rate (RR), WIWNU%, RMS roughness, and peak-to-valley roughness [2]. With these important results, the CMP process for CdTe thin films was performed to improve the thickness-uniformity of the sputtering-deposited CdTe thin film which had the worst two thickness-uniformities of them. Some optical properties including optical transmittance and absorbance of the CdTe thin films were measured by using a UV-Visible spectrophotometer (Varian Techtron, Cary500scan) in the range of 400 - 800 nm. After CMP process, the thickness-uniformities became better than that of the best condition in the previous sputtering process of CdTe thin films. Consequently, the optical properties were directly affected by the thickness-uniformity of CdTe thin film. The absorbance of CdTe thin films was improved although the thickness of CdTe thin film was not changed.

• Journal of the Korean Magnetics Society
• /
• v.10 no.2
• /
• pp.62-66
• /
• 2000

Annealing cycle number and nonmagnetic layer thickness dependences of interlayer coupling field ( $H_{inf}$ ) and coercivity ( $H_{cf}$ ) of free magnetic layer on NiMn alloy-spin valve films (SVF) were investigated. The SVF is Glass (7059)/N $i_{81}$F $e_{l9}$(70 $\AA$)/Co(10 $\AA$)/Cu(t $\AA$)/Co(15 $\AA$)N $i_{81}$$Fe_{19}$(35 $\AA$)/N $i_{25}$M $n_{75}$(250 $\AA$)Ta(50 $\AA$) films, it were fabricated using the dc sputtering method at different pinning layer thickness and nonmagnetic spacer thickness (Cu thickness; 30 $\AA$, 35 $\AA$, 40 $\AA$) of NiMn alloy with 25 at.%. Ni In case that Cu thickness of SVF is 35 $\AA$ and peak exchange coupling field ( $H_{ex}$) was 620 Oe, while coercivity $H_{c}$ = 280 Oe and MR ratio showed 2.5%. As for $H_{inf}$ and $H_{cf}$ , every SVF increased up to the stabilized values with the increase of annealing cycle number 15, which were $H_{inf}$ of 120 Oe and $H_{cf}$ of 75 Oe. The increase of $H_{cf}$ with the annealing cycle number seems to be caused by the effective reduction of Cu layer thickness due to the increase of interfacial mixing of Cu layer and Co layer. In addition, the $H_{inf}$ and $H_{cf}$ dependences of free NiFe layer by the interfacial mixing effect were appeared the different aspects when Cu layer becomes more thinner and thicker than Cu layer thickness of 35 $\AA$, respectively.ively....

• Journal of the Korean Vacuum Society
• /
• v.21 no.6
• /
• pp.333-341
• /
• 2012

Indium Tin Oxide (ITO) thin films were prepared by RF magnetron sputtering with different flow rates of $O_2$ gas from 0 to 12 sccm. Electrical and optical properties of these films were characterized and analyzed. ITO deposited on soda lime glass and RF power was 2 kW, frequency was 13.56 MHz, and working pressure was $1.0{\times}10^{-3}$ Torr, Ar gas was fixed at 1,000 sccm. The transmittance was measured at 300~1,100 nm ranges by using Photovoltaic analysis system. Electrical properties were measured by Hall measurement system. ITO thin films surface were measured by Scanning electron microscope. Atomic force microscope surface roughness scan for ITO thin films. ITO thin films secondary electron emission coefficient(${\gamma}$) was measured by ${\gamma}$-Focused ion beam. The resistivity is about $2.4{\times}10^{-4}{\Omega}{\cdot}cm$ and the weighted average transmittance is about 84.93% at 3 sccm oxygen flow rate. Also, we investigated Work-function of ITO thin films by using Auger neutralization mechanism according to secondary electron emission coefficient(${\gamma}$) values. We confirmed secondary electron emission peak at 3 sccm oxygen flow rate.