• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.331-335
• /
• 2018

The purpose of this study is to investigate the feasibility of CFBC artificial fine aggregate as a substitute for natural aggregate used in dry mortar. The basic performance of the flow, compressive strength and dry shrinkage of the dry mortar was evaluated. Four types of test dry mortar specimens using natural aggregate without expansion admixture, a specimen with modified CaO expansion admixture and natural aggregate, a specimen with modified CaO expansion admixture and CFBC artificial fine aggregate, and a specimen using CFBC artificial fine aggregate without modified CaO expansion admixture were evaluated respectively. As a result of evaluation of drying shrinkage performance at 20th day of age, the dry shrinkage performance of the specimen using modified CaO expansion admixture was found to be the highest at $250{\times}10^{-6}$. On the other hand, the specimen containing the modified CaO expansion admixture with CFBC artificial aggregate exhibited a shrinkage of $410{\times}10^{-6}$, and the drying shrinkage of specimen using natural fine aggregate without expansion admixture was $450{\times}10^{-6}$. When the modified CaO expansion material was used, and exhibited performance equal to or higher than that of the shrinkage-drying property.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.2
• /
• pp.193-199
• /
• 2015

As a solution of both environmental issue of reducing carbon dioxide emission and sustainable issue of exhausting natural resources, in concrete industry, many research on recycling various by-products or industrial wastes as the concrete materials has been conducted. The aim of this research is feasibility analysis of additional reaction with ordinary Portland cement and flue gas desulfurization gypsum based on the blast furnace slag and recycled fine aggregate based mortar to achieve the normal strength range. Consequently, in the case of mortar replaced 10% FGD and 30% OPC for BS, 80% of plain OPC mortar's compressive strength was achieved. Furthermore, when the water-to-binder ratio is decreased to keep the practically similar level of flow, it is expected to be achieve the equivalent compressive strength to plain OPC mortar.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.221-222
• /
• 2016

The replacement ratio of waste EPS was varied, and its effect on compressive strength and absorption capacity was investigated. According to the experimental results, The 28th day compressive strengths for the W/C 50% specimens were 17.5~21.2MPa, which was relatively low compared to the 13.6~22.2MPa of the W/C 70%.

• Cement Symposium
• /
• s.35
• /
• pp.159-166
• /
• 2008

• Magazine of RCR
• /
• v.14 no.2
• /
• pp.28-34
• /
• 2019

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.473-476
• /
• 2008

The use of the recycled fine aggregate to the material of structural concrete is not easy currently because there are some problems, such as the difficulty of quality control and the badness of chemical and physical property other than river sand, crushed fine aggregate. To use of recycled fine aggregate, many researches on the recycling of recycled fine aggregate have been studying until today. However, the result of the research is little except for some results. Therefore, the purpose of this study is to confirm the possibility of use of recycled fine aggregate for raw material of plaster mortar. In this study, various tests were performed such as flow, air content, unit weight, bond strength, and compressive strength test to evaluate the effect according to the substitution of recycled concrete aggregate. The results of strength test showed that the concrete strength improved with the increase of replacement ratio of recycled fine aggregate. In the other side, flow and air content are decreased according to replacement ratio of recycled fine aggregate. The result of this study could be used as the basic data for the recycling of recycled fine aggregate.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.12
• /
• pp.785-792
• /
• 2017

In recent times, the lack of good quality natural aggregate has led to the alternative use of recycled aggregate. However, the adhered mortars in recycled aggregate lower the performance of the concrete, such as by reducing its strength and causing deterioration and cracking. In this study, the effects of nylon fiber (NF) on the mechanical and durable performance of recycled coarse aggregate concrete (RAC) were experimentally examined. Concrete specimens with natural coarse aggregate (NA) or RA were produced by adding 0, 0.6 and $1.2kg/m^3$ of NF. Various mechanical properties and the durability of the RAC were measured and compared with those of the NAC. In addition, in order to observe the hydrates and ITZ, SEM observations were made of the 28-day concrete samples. From the test results, as expected, it was found that the RAC exhibited lower performance than the NAC. However, the addition of NF to the concrete was effective in significantly enhancing the performance of the RAC due to the bridge effect of the NF.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.3
• /
• pp.247-252
• /
• 2017

The aim of this research is the feasibility analysis of the reject ash premixed cement mortar with combined aggregate. Namely, for the combined aggregate with two different qualities of aggregates, a fundamental properties of cement mortar was evaluated depending on various replacing ratios of reject ash(Ri). According to the experimental results, the combined aggregate consisted with low-quality aggregate and sea sand did not change the flow value depending on the reject ash while the combined aggregates consisted with low quality aggregate and sea sand; and consisted exploded debris sand and sea sand the increasing reject ash increased the air content with increased replacing ratio of reject ash. In the case of compressive strength, as the replacing ratio of reject ash was increased, the compressive strength was increased. It is considered that when 5% of reject ash replacing ratio made similar quality of cement mortar with favorable quality aggregate, hence, it can be suggested that 5% replacement of reject ash for desirable fluidity and compressive strength of concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.1
• /
• pp.33-40
• /
• 2021

The objective of this work is to prove a possibility of void f illing through a carbonation f or the purpose of improving the quality of recycled aggregate. Carbonation can permanently immobilize CO2, which is a greenhouse gas, and thus provides additional benefit on environment. In this work, recycled fine aggregate was reacted using gaseous CO2 and supercritical CO2(scCO2) in a closed chamber, and the changes in physical properties of the recycled f ine aggregate bef ore and af ter carbonation were analyzed using the apparent density, skeletal density, pH, and FE-SEM measurements. Thereafter, a mortar specimen was prepared and a compressive strength was measured. According to the experimental results, it was found that the increase in the apparent density and the true density was higher by the reaction with scCO2, which was conducted at high temperature and high pressure compared to the reaction with gaseous CO2. In addition, the pH of the eluted water was found to have a larger initial decrease than that observed with samples from reaction by gaseous CO2. The shape and amount of calcium carbonate crystals were also found to be larger than that from gaseous CO2. The increase in compressive strength was the largest when using recycled fine aggregate reacted with scCO2. It was clear that quality improvement of recycled fine aggregate was higher with scCO2 than with gaseous CO2.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.6
• /
• pp.561-567
• /
• 2015

The research, in order to enhance the quality of recycled aggregate, was carried out the quality characteristics test of the recycled aggregates by applying the four kinds of surface treatment using a colloidal suspension of approximately 5nm~60nm particle size with the alkalinity of pH 10.2. The quality tests of recycled aggregate have been processed by specific gravity, water absorption, porosity, surface properties, and the compression and tensile tests. The colloidal suspension was coated effectively the surface of the old cement mortars of recycled aggregate with a constant thickness by colloidal suspension is being applied to the recycled aggregate surface under constant pressure of 100kpa and then it was dried in at $60^{\circ}C$. The surface treatment method by the Method C out of 4 kinds of surface treatment improved effectively the quality of the recycled aggregates, whereby it obtained the best compressive strength and tensile strength of the recycled aggregate concrete.