• 한국해양공학회지
• /
• 제24권2호
• /
• pp.57-61
• /
• 2010

At present, welding technology is not only emphasized in the development of manufacturing technology but its application is also expanding. In these systems, attempts have been made to use SUS as a high-temperature material for special applications, and in improvements in manufacturing technologies bear watching, together with an increase in the use rate. Specifically, three-dimensional wings are often used for fasteners with the purpose of decreasing the weight (정해용, 2007). However, due to developments in welding technology, there has been a recent tendency to replace existing assembly methods with welding. Specifically, if laser welding techniques are applied, the heat-affected zone can be minimized compared toother welding techniques. However, in the case of these special welding techniques, there is an increase in residual stress, which fatally affects the fatigue life. In order to remove the residual stress and its effect on fatigue life, shot-peening is executed. The intention of this study was to obtain the optimal conditions for shot-peening.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 추계학술대회 논문집
• /
• pp.341-346
• /
• 2002

In this study, an effect that compressive residual stress formed by shot-peening the surface of spring steel(JISG SUP-9) at each shot velocity(1800, 2200, 2600, 3000rpm) on the fatigue crack growth property and threshold stress intensity factor, ${\Delta}K_{th}$, was examined. Followings are the result (1) Compressive residual stress on surface of specimen was determined at each -601 MPa(1800rpm), -638 MPa(2200rpm), -587 MPa (2600rpm), -550 MPa(3000rpm) by shot velocity of shot peening and threshold stress intensity factor, ${\Delta}K_{th}$, fatigue crack growth rate, da/dN, on fatigue crack growth is obstructed by the compressive residual stress was determined at each $5.619\;MPa\sqrt{m}$(Un-peening), $8.319\;MPa\sqrt{m}$(1800rpm), $8.797\;MPa\sqrt{m}$(2200rpm), $7.835\;MPa\sqrt{m}$(2600rpm), $7.352\;MPa\sqrt{m}$(3000rpm) (2) Existing compressive residual stress by effect of shot velocity of shot-peening on relation of crack length. a, and number of cycle, N, was 2 times progressed in case of 2200rpm than specimen of Un-peening on fatigue life. And fatigue life was 1.6 times progressed incase of 3000rpm by Over peening. (3) Fatigue life of Material on Paris' law, $da/dN=C({\Delta}K)^m$, that effect of material constant, C, and fatigue crack growth exponent, m, was influenced by effect of. C and m.

• 대한기계학회논문집A
• /
• 제27권1호
• /
• pp.200-207
• /
• 2003

In this paper, the effect of the compressive residual stresses which were obtained under the various shot velocities of shot balls on the fatigue behaviors of a spring steel, were investigated. The examination of CT specimen test were executed with the materials(JISG SUP9) which are being commonly used for the springs of automotive vehicles. As a result, the optimal shot velocity of shot balls were acquired considering the peak values of the compressive residual stresses on the surface of specimen and effect on the speed of the fatigue crack propagation da/dN in stage II and the threshold stress intensity factor range Δ$K_{th}$ in stage I. Also the material constant C and the crack propagation index m in the formula of paris law da/dN= C $({\Delta}K^m)$ were suggested in this work to estimate the dependency on the shot velocity.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.1601-1606
• /
• 2007

In order for high strength aluminum alloys to be used in transportation systems and the aerospace industry, excellent mechanical and physical properties are required. In particular, excellent anti-abrasion property is indispensable for parts that require driving force. In general, surface treatment technologies such as high frequency heat treatment, gas solid carburizing, surface rolling, shot peening are used as ways of improving anti-abrasion property. Among various surface treatment technologies, this research chose shot peening processing for Al7075-T6, which is well known as representative high-strength alloy steel. Wear characteristics were compared and analyzed after shot peening processing with shot ball velocities of 40m/s and 70m/s in order to investigate the effects of shot peening processing on wear characteristics.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2000년도 춘계학술대회 논문집(Proceeding of the KOSME 2000 Spring Annual Meeting)
• /
• pp.93-99
• /
• 2000

This study deals with the evaluation of bending fatigue strength in shaving gears, We manufactured gears using manufacture processes that are currently used in most gears manufacturing companies. The test gears are hobbed then the tooth surface are treated by a combination of shaving carbonizing and shot peening. The constant stress amplitude fatigue test is performed by using an electrohydraulic servo-controlled pulsating tester. The S-N curves are obtained and illustrated. In this study we investigated the effect of shaving process and shot peening on fatigue strength, The effect of shaving process ad shot peening on the fatigue strength is evaluated quantitatively,. The enhancement of fatigue strength due to shaving process and shot peening is clarified

• 한국안전학회지
• /
• 제19권4호
• /
• pp.20-24
• /
• 2004

Antifatigue failure technology take an important the part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. Therefore in this paper the effect of compressive residual stress by shot peening on fatigue crack growth characteristics in stress ratio(R=0.1, 0.3, 0.6)was investigated with considering fracture mechanics. There is difference between shot peening specimen and unpeening specimen. Fatigue crack growth rate of shot peening specimen was lower than that of unpeening specimen. Fatigue lift shows more improvement in the shot peening material than in the unpeening material. And compressive residual stress of surface on the shot peening processed operate resistance force of fatigue crack propagation. That is the constrained force about plasticity deformation was strengthened by resultant stress, which resulted from plasticity deformation and compressive residual stress in the process of fatigue crack propagation.

• 한국해양공학회지
• /
• 제16권5호
• /
• pp.73-79
• /
• 2002

In this paper, the effect of the compressive residual stresses was obtained at the test conditions of the higher temperature than the ambient temperature. The examination was performed with the CT specimen result of the material(JISG SUP9) which is being commonly used for the marine engine parts and the ocean structures. As a result, the test conditions at the higher temperature were acquired considering the peak values of the compressive residual stresses of the specimens and the effect on the fatigue crack propagation speed da／dN in stage II and the threshold stress intensity factor range Δth in stage I. Also the material constant C and the fatigue crack propagation index m in the formula of Paris Law da／dN＝C (ΔK)$^{m}$ were suggested to estimate the dependence on the test temperature.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2005년도 후기학술대회논문집
• /
• pp.228-229
• /
• 2005

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, it was not known that the effect of shot peening in corrosion environment. In this study, the effect of shot peening on corrosion fatigue crack growth of sping steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of spring steel are as follows; the fatigue crack growth rate of the shot peening material was lower than of the un peening material. And fatigue life shows more improvement in the shot peening material than un peening material. This is because the compressive residual stress of surface operate resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1996년도 춘계학술대회 논문집
• /
• pp.697-703
• /
• 1996

Fatigue strength of high strengthsteels are variable with many different surface treatment. It is well known that residual compressive stress retard fatigue crack growth rate(or arrest crack). High strngth steels are manufactured by following process. Heat treatment, shot peening and chromium plating process. High strength steel(HRC40 or above) which are subjected to fatigue load and dynamic load, chromium plated parts shall be peened in accordance with requirements and baked after plating. The purpose of this paper is to compare and discuss the influence of surface treatment and hydrogen embrittlement on fatigue strength of high strength steel. Therefore, fatigue test was performed to investigate influence of surface treatment. The results shows that shot peening is very effect method in creasing fatigue life and after plating, baking process is essential to prevent hydogen failure. In this paper, the experimental investigation is made to clarify the influence of shot peening conditions and baking process on fatigue strength of high strength steel.

• 한국표면공학회지
• /
• 제47권1호
• /
• pp.25-32
• /
• 2014

The effects of shot peening pressure on electrochemical and surface morphological characteristics of ALBC3 alloy were investigated in this work. The surface hardness of ALBC3 alloy was improved by shot peening process under all shot peening pressures between 2 and 5 bar, and the hight value of surface hardness was observed to be about 420 Hv at 4 bar of the shot peening pressure. The shot peened surface presented very rough surface due to shot ball collision. The result of anodic potentiodynamic polarization in seawater revealed that there is no significant difference between the shot peened and non-shot peened specimen in terms of corrosion characteristics. Therefore, the optimum projection pressure is determined to be 4 bar.