Effect of Corrosion on Fatigue Life of Piping material under Repeating Load

반복하중을 받는 배관용 강재의 피로수명에 미치는 부식의 영향

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, it was not known that the effect of shot peening in corrosion environment. In this study, the effect of shot peening on corrosion fatigue crack growth of sping steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of spring steel are as follows; the fatigue crack growth rate of the shot peening material was lower than of the un peening material. And fatigue life shows more improvement in the shot peening material than un peening material. This is because the compressive residual stress of surface operate resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.