• Polymer(Korea)
• /
• v.25 no.6
• /
• pp.855-865
• /
• 2001

The optimization condition of injection molding for a commercial product of TV speaker grille of A Company was induced using a CAE software of Moldflow. The flow and packing phase analysis was performed by using flow balance, runner balance, and the intermediate one by using the above two balances, which were used for controlling the amount of packing resins into the cavity, Later, the analysis performed by using the measured viscosity (local database) at various shear rates and the results were compared with the computer simulation using the standard database. Flow balance induced minimized weld line resulted in a better appearance and physical properties of the were line, but exhibited a disadvantage of large deformation and gas formation due to over-packing of the molten resin in the center of the speaker grille. Runner balance improved the disadvantage of the flow balance by controlling the amount of molten resin injected from the gate, however resulted reduced mechanical properties and poor appearance of the weld line. However, the modified method induced from the flow and runner balance improved the disadvantages by changing the runner size. In addition, the analyses based on the local database and the standard database were compared. Although the measured viscosity was slightly higher and the temperature distribution was broader than the standard database, no distinct difference was obtained from the analysis using the two different databases.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.1
• /
• pp.278-283
• /
• 2019

3 kinds of fine powder, Fe-2%Ni alloy powder(N Ltd.) and Fe+2%Ni mixed powder(B Ltd. and S Ltd.), were fabricated into sintered compacts of bending strength specimens and ring type specimens by metal injection molding, debinding and controlling sintering conditions (reduction and sintering atmospheres, sintering temperature, sintering time and cooling rates). Density and magnetic properties of the sintered compacts were evaluated with the following conclusions. (1) When each compact was hold at 1123K for 3.6ks in H2 and sintered at 1623K for 14.4ks in Ar, the density of N, B and S Ltd.'s sintered compacts were measured as 96, 99 and 99%, and oxygen/carbon contents were measured as 0.0041%O/0.0006%C, 0.0027%O/0.0022%C, and 0.160%O/0.0026%C, respectively. (2) Magnetic characteristics of B Ltd. compact in Ar with the best results showed $B_{25}=14.3KG$, $B_r=7.75KG$, and $H_c=2.1Oe$, but not enough as those made by melting process. (3) Magnetic properties of B Ltd. compact which were sintered at 1673K for 14.4ks in Ar gas, and cooled at $0.83Ks^{-1}$ to 1123K and then cooled at $0.083Ks^{-1}$ down to room temperature were measured as $B_{25}=14.8KG$, $B_r=8.3KG$, and $H_c=1.3Oe$, almost similar to those made by melting process. Objected soft magnetic materials properties were obtained through sintering process by controlling sintering conditions (reduction condition, sintering atmosphere, sintering temperature and sintering time) and cooling rates.

• Polymer(Korea)
• /
• v.36 no.6
• /
• pp.677-684
• /
• 2012

Injection molding process is a popular polymer processing involving plasticizing and enforcing the material flow into the mold. A polymer material shrinks according to temperature variations during the shaping process, and subsequently molding shrinkage developed. Developed deflections or warpages after molding process in part are caused by residual stress relaxation contained in the part. Adding inorganic materials or fibers such as glass and carbon to control shrinkage and enhance warpage resistance are common. In this study, warpages according to part design have been investigated through experiment. Warpages for molding conditions and mold designs such as gate locations were measured. Warpages along flow direction and perpendicular to the flow direction were also measured. Warpages near gate and far from gate were compared. Glass fiber reinforced crystalline polymers, PP and PA66 have been used in this experiment. Glass fiber reinforced crystalline polymers showed large warpage compared with glass reinforced amorphous polymers. Warpages in crystalline polymers were less influenced by molding conditions compared with amorphous polymers, however warpages of crystalline polymers significantly depend on part design.

• Polymer(Korea)
• /
• v.36 no.5
• /
• pp.555-563
• /
• 2012

Warpage of injection molded product is caused by non-uniform shrinkage during shaping operation and relaxation of residual stress. Robust part design and glass fiber reinforced reins have been adopted to prevent warpage of part. Warpages for part designs have been investigated in this study according to the injection molding conditions. Part design contains flat specimen and two different rib designs in the flat part. Resins used in this study were glass fiber reinforced amorphous plastics, PC and ABS. Different rib designs showed significant differences of warpages in the parts. Various warpages have been observed in the three regions of the part, near gate region, opposite region to the gate, and flow direction region. Results of computer simulation revealed that the warpages were strongly related to glass fiber orientation. Flat specimen showed the smallest warpage and the specimen with ribs to the flow direction showed a high resistance to warpage. Warpage highly depended upon part design rather than molding condition. It was concluded that the rib design and selection of gate location in injection molding would be the most important factors for the control of warpage since those are directly related to the fiber orientation during molding.

• Composites Research
• /
• v.26 no.4
• /
• pp.230-234
• /
• 2013

The continuous glass fiber reinforced poly-lactic acid (PLA) composite was manufactured by direct melt impregnation. The mechanical and thermal properties of continuous glass fiber reinforced PLA composite were observed. Measured properties were compared with the reference values of neat PLA and the injection molded glass fiber/ PLA composite. The continuous glass fiber reinforced PLA composite having a fiber volume fraction of 27.7% shows enhanced tensile strength of 331.1 MPa, flexural strength of 528.6 MPa, and flexural modulus of 24.0 GPa. The enhanced heat deflection temperature (HDT) and the increased cystallinity were also observed. The degree of impregnation as a function of pulling speed was also assessed. The degree of impregnation at the pulling speed of 5 m/min was over 90% in this research.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.8 no.3
• /
• pp.10-16
• /
• 2004

Untypical unstable burning with very low frequency was observed at firing test of a gas generator using bundle cylindrical grain. The pressure unbalance between inside and outside of cylindrical grain brought such a low unstable burning. The grains were radially holed so that the high pressure gas inside of grain could quickly moved outward of gain, resulting dissipation of the pressure unbalance However too many holes were required to let the burning be stable for all operation regime from low to high temperature of grain and resultantly deteriorate the Progressive increase of gas amount produced by a gas generator. So another idea using grids located both sides of a bundle grain was applied to dissipate actively large vorticities enhanced by unbalance pressure distribution in a combustor. Finally stable burning with progressively increase of gas was established by application of 5${\times}$5 grid slightly away bundle grain to move bundle gain freely in case pressure unbalance were occurred inside of combustor.

• Microbiology and Biotechnology Letters
• /
• v.9 no.1
• /
• pp.35-44
• /
• 1981

Whole cell penicillin amidase of Escherichia coli was immobilized by entrapment in gelatin followed by extrusion and crosslinking with glutaraldehyde. The immobilized engyme preparation demonstrated the recovery yield of activity up to 70% and good stability during storage and operation. The half life of activity decay during the operation was estimated to be about 50 days. The optimum pH and temperature for both of immobilized and soluble enzyme are 8.5 and 5$0^{\circ}C$, respectively. No significant change was demonstrated in the effect of pH and temperature, but the increase in heat stability at high temperature was observed in the case of the immobilized enzyme. It was found that the plug flow reactor could be operated favorably since the pH drop along the column path due to tile reaction product was minimized by employing substrate solution with moderate buffer strength. The optimal condition of reactor operation was discussed with regard to the effect of substrate concentration and the residence time on the conversion efficiency and productivity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05e
• /
• pp.40-43
• /
• 2003

전기방전에 대한 shed 재료의 열화내성과 우수한 발수성의 장기간 유지특성은 폴리머 애자의 장기성능에 있어서 가장 중요한 인자들이다. 애자 제조시 무결점 성형성 또한 중요한데 열화내성을 확보하기 위해 다량의 ATH의 첨가가 수반되기 때문에 적절한 process oil의 사용이 불가피하다. 사용하는 오일의 종류와 량에 따라 옥외절연물의 장기성능에 영향을 주는 표면발수성이나 방전내성은 크게 차이가 나는 것으로 밝혀지고 있다. 본 논문에서는 화학적 구조와 정도가 다른 몇 가지 실리콘 fluid들을 실리콘 고무에 처방하여 기본물성과 초고압 옥외절연물의 shed 재료로서 장기성능에 영향을 주는 방전열화내성과 표면발수성의 회복특성을 평가하였다. 실리콘 고무의 무결점 사출성형에 가소도가 중요한데 동일한 무기물 첨가조건에서 유사한 가소도를 갖게 하는데 필요한 량은 fluid들의 종류에 따라서 상당한 차이가 있었다. 특히 PDMS는 점도는 낮지만 분자량이 커서 많은 량이 첨가되어 기계적 특성저하가 크게 일어났다. 코로나 처리후 발수성 회복특성은 fluid들의 분자크기와 반응기의 종류에 따라 상당히 영향을 받았으며 분자가 클수록 초기회복속도는 다소 느려도 최종의 상시발수성은 다소 높게 유지되었으며 2일 이내에 거의 초기 접촉각으로 회복되었다. 내아크성은 무게손실이 적을수록 오차범위도 작은 안정된 특성을 보였으며 fluid들의 종류에 따른 무게손실의 차이는 크지 않았다. 트래킹 방전에 의한 무게 감소는 fluid의 분자가 크면서 페닐기를 가진 fluid들이 첨가된 고무가 우수한 특성을 보였다.

• Journal of Intelligence and Information Systems
• /
• v.7 no.1
• /
• pp.1-15
• /
• 2001

Recently, Internet based Electronic Commerce is recognized as one of the alternatives for strengthening sales power of small and medium companies. However, small and medium manufacturers can't adjust properly to the new environment because they are in short of money, personnel, and technology. To cope with this problem, this paper deals with the development of virtual manufacturing agent to support sales agent. The sales activity of most of parts manufacturing companies is based on orders of buyers. The process of promotion, receipt and selection of orders of the parts manufacturing is closely coupled with the load status of the production lines. On deciding whether to accept an order or not, as well as negotiating with buyers, sales person needs information such as load and schedule of production lines, manufacturability of the order. Therefore, the functions of virtual manufacturing agents manufacturability analysis, process planning, and scheduling are key features in developing an agent of sales activity for the parts manufacturing business. While most of research on virtual manufacturing system so far is focused on the simulation of each product, this paper deals with the development of agent assisting internet-based product sales by supporting production information promptly. The pilot system of virtual manufacturing agent is implemented using KQML-based agent template and Java-based expert system shell for a small molding company.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.10
• /
• pp.115-120
• /
• 2018

This study examined the cast quality of small-sized induction motor rotors during the die casting process. Numerical analyses with 3-dimensional half models were performed to investigate the filling patterns of aluminum molten metals into a mold after high-speed injections. The following were obtained from numerical analyses and experimental results. First, molten metals started to fill the lower end ring, then moved horizontally to fill the core slot and upper end ring, and finally stopped to fill the rotor core slot. Second, circulation of molten metals occurred at the lower end ring, resulting considerable porosity at the section of lower end ring from the experimental results. Third, further work for obtaining sound quality of rotor core cast is required to develop a new shape of the rotor core cast or improve the die casting conditions.