• Economic and Environmental Geology
• /
• v.48 no.1
• /
• pp.89-101
• /
• 2015

The sour gas is natural gas containing components such as hydrogen sulphide and carbon dioxide that form acids when mixed with water. Element sulfur precipitates from sour gas when reservoir pressure and temperature decrease. According to the International Energy Agency, about 43% of the world's natural gas reserves(2,580 tcf or 73.057 tcm), excluding North America, are sour. The sour gas is often derived from the Germanic word 'sauer or acidic' and the etymology referred to as 'sour'. Sour gas requires special handling and infrastructure because it contains significant amounts of hydrogen sulphide, making it highly corrosive, flammable and explosive, and there fore more costly and dangerous to process. So the business of sour gas is affected by two important factors: the economic value of the gas, and the methods used in its production. According to be analyzed in the academic literature to sour gas(2000~2014) by the program of 'web of science', the research activities 145 papers in sour gas.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1991.11a
• /
• pp.34-37
• /
• 1991

Al계 베어링합금은 소착저항력등의 베어링특성이 우수하여 최근에 자동차의 엔진부품에 많이 사용되고 있다. Al계 베어링합금으로는 Al-Sn계, Al-Pb계, Al-Si계 합금이 개발되어 사용되어 왔다. Al-Si계 합금은 높은 강도, 우수한 부식성, 주조성이 향상되는 장점등을 갖고 있다. 또한 Al-Pb계 합금은 Pb가 고체윤활제로 작용하여 소착저항성이 높으며 가격도 저렴한 장점을 갖고 있다. Al과 Pb는 용융상태에서 넓은 용융간극을 갖어 중력편석을 일으키기 때문에 일반적인 주조방법으로 Al계 베어링합금을 제조할 수없다. 또한 Al에 Si이 첨가됨에 따라 높은 경도등의 기계적성질의 향상이 얻어지지만 Al 기지에 Si의 함량이 증가할 수록 편석이 심해져 조대한 Si-rich상이 미세조직에 존재하여 합금이 취약해지는 단점을 갖고 있다. 따라서 본 연구에서는 Al 기지에 Pb의 중력편석을 최소화하고 Al 기지에 조대한 Si-rich상이 생성되는 것을 막기 위하여 Al과 Pb가 공존하는 온도구역에서 높은 교반속도로 용탕을 강제교반하여 액상에서 Pb와 Si을 미세하게 분산시킨 후 수냉되는 동주형에서 급속응고시켜 Pb와 Si-rich 상이 균일하게 분포된 Al계 베어링합금을 제조하였다. 본 연구에서는 Pb의 양을 0%에서 35%까지 변화시켰으며, Si의 양을 0%에서 20%까지 변화시켜서 베어링합금을 제조하였으며, 강제교반속도는 500rpm에서 2500rpm 까지 변화시켜 베어링합금을 제조하였다.

• Journal of Korean Society of Steel Construction
• /
• v.16 no.5 s.72
• /
• pp.621-628
• /
• 2004

This paper introduces a new theory, that in a stiffened plate, a steel stiffener could be substituted a composite material in order to prevent from buckling. Changing a steel stiffener into a composite material would not only preclude welding, but could also prevent damage to the material due to fatigue and corrosion.A composite material is assumed to adhere to a steel plate, and is never separated from the plate until the steel plate reaches buckling.Such plate has variable shapes, with different lengths and widths, and also shows an anisotropic material property. LUSAS, a commercial finite element analysis package, was used in the buckling analysis.This paper investigated buckling behavior in anisotropic composite plates with variable parameters.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2018.05a
• /
• pp.132-132
• /
• 2018

홍수피해 발생 시 각 지역의 특성에 따라 피해의 정도가 다르게 나타나고 있다. 도시지역의 경우 포장도로로 인하여 불투수 면적이 넓어 배제 시설의 허용 용량을 초과하는 강우 발생 시 지표면 위로 유량이 누적된다. 특히 농촌지역에 비해 도시지역에서 국지적으로 기습적인 강우에 빈번히 침수피해가 발생한다. 우리나라 도시지역은 인구와 건물이 밀집되어 재산과 인명피해 및 교통체증 등으로 인한 간접피해 등 농촌지역에 비해 더 큰 피해가 발생할 수 있다. 도시 지역의 침수 피해 저감을 위해 우수 유출 저감시설과 내수배제 시설을 설치하여 우수의 유출을 지연시키거나 인위적으로 방류부 하천으로 방류시키는 방법이 있지만 이러한 시설의 설치에는 막대한 비용이 필요하며, 내수배제시설이 설치된 장소에 따라 침수현상이 다르게 나타나 저감시설 설치 전 공간적, 효율적으로 설치 가능한 장소와 침수 저감 효율에 대한 분석이 필요하다. 본 연구는 도림1 배수분구를 대상으로 XP-SWMM모델을 이용하였으며, 2010년 09월 21일 침수 발생 당시의 강우를 적용하여, 연구대상지역의 도시유출해석을 진행하였다. 또한, 어린이 공원과 학교운동장에 가상지하저류조를 설치하였을 시 침수저감 효과에 대하여 연구를 진행하였으며, 다양한 지하저류조 설치 시나리오에 따른 침수저감효과를 수심별 침수면적으로 나타내어 분석을 실시하였다. 본 연구를 통해, 도심지 지하 저류시설 도입의 기초자료로 활용될 수 있을 것으로 판단된다.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.42-42
• /
• 2009

마찰교반접합 (Friction Stir Welding)은 1991년 영국 TWI에서 개발된 접합 법으로서 회전하는 툴이 재료내부에 삽입되면 툴과 재료사이에서 발생하는 마찰열에 의하여 온도가 상승하게 되어 재료는 연화되고, 이러한 재료 내부에서 회전하는 툴이 이동하게 되면 재료 내부는 기계적 교반에 의해 소성변형이 일어남과 동시에 접합이 이루어진다. 마찰교반접합은 동적 재결정에 의한 접합부의 미세한 결정립 형성으로 인하여 기계적 특성이 향상되며 보호 가스가 필요 없어 친환경적임과 동시에 용융 용접 법에 비해 접합 시 에너지 소모가 적으며 또한 접합 후 접합부에서의 변형이 상대적으로 적다는 장점이 있다. 이러한 장점을 가진 마찰교반접합은 알루미늄 합금, 마그네슘 합금 그리고 동 합금과 같은 저 융점 비철재료에 많은 연구와 적용 사례들이 있어왔다. 하지만 최근에는 일반 탄소강, 연강, 오스테나이트계 스테인리스강, 니켈 합금, 티타늄 합금과 같은 고융점 재료에도 연구 및 적용이 진행되고 있는 추세이다. 페라이트계 스테인리스강은 가격이 비싼 Ni을 함유하지 않아 오스테나이트계 스테인리스강에 비하여 강재의 가격은 낮으면서도 고온특성 및 내식성이 우수하여 건축용, 자동차 배기계용으로 널리 사용되고 있다. 하지만 이런 장점을 가진 페라이트계 스테인리스강을 기존의 용융 용접 법으로 접합 시 용접부 및 열영향부에서의 결정립의 조대화로 인한 인성 및 연성이 저하되며, 특히 예민화된 열영향부 입계 내에 Cr 탄화물이 석출되어 입계주변에 Cr 결핍 층을 형성되어 입계부식이 발생되는 문제점이 발생된다. 본 연구에서는 마찰교반접합을 이용하여 두께 3mm의 409 스테인리스강에 대해 맞대기 접합을 실시하였다. 접합 변수를 툴의 재료 (WC-12wt%Co, $Si_3N_4$)로 하여 접합을 실시하였고 접합 후 외관상태 점검, 광학 현미경과 주사 전자 현미경을 통하여 미세조직을 관찰하였으며 황산-황산동 부식 시험을 실시하여 접합부의 부식 특성을 평가하였다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.693-696
• /
• 1999

Reinforced concrete is, in general, known as high durability construction material under normal environments due to strong alkalinity of cement. It is , however, well known that moderate or minor cracks in reinforced concrete should be most serious causes to deteriorate the durability of RC structures. Furthermore, chloride contents penetrating through unexpected cracks in reinforced concrete bridges get to weaken corrosion resistance of reinforcement steel in concrete and than to accelerate the deterioration of concrete durability. The objective of this experimental research is 1) to evaluate the effect of various corrosion protection system for reinforced concrete specimens with moderate or minor cracks which are exposed to cyclic wet and dry seawater, and then 2) to develop effective corrosion protection system for reinforced concrete bridges under the exposure of various detrimental environments such as seawater, deicing and etc.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2005.05b
• /
• pp.60-64
• /
• 2005

강우-유출 모형을 수행하기 위해서는 지표면의 성질을 나타내는 보조 자료로서 식생피복자료, 토양분포, DEM 등이 주어지는데, 이러한 인자들이 흐름을 지배하게 되므로 중요하다. 그러므로 강우-유출 모형에서는 지표에서의 식생을 적절하게 나타내 줄 필요가 있는데, 최근의 원격 탐사 기술이 하나의 대안으로 제시되어 왔으며 식생 정보는 2차원 디지털 지도로 작성되어 수치모형에서는 이 디지털지도로부터 조도계수의 값을 전환하는 다단계 방법을 이용하여 오고 있다. 그러나 강우-유출 모형의 격자 간격이 식생 피복을 나타내기 위한 디지털 지도의 격자 간격과 항상 일치하는 것이 아니고 디지털 지도의 격자 간격이 일반적으로 더 세밀하므로 강우-유출 모형에서 디지털 지도를 이용하기 위해서는 적당한 방법의 스케일 확장 (up-scaling)이 필요하며, 이 연구에서는 질량 보존의 법칙을 사용하여 이론적 기반에 근거한 하나의 전략적인 방법이 제시된다. 이 연구의 목적은 강우-유출 모형의 수행 시 이질성을 보이는 지표면에서 식생과 관련된 매개변수를 통합/확장 처리하는 하나의 기법을 대기모형에서 이미 제시된 방법을 모사하여 제시함으로써 이질성을 보이는 지표면의 처리할 때 방향을 설정해 주고자함이다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10c
• /
• pp.223-228
• /
• 1998

This study is to investigate on the remaining life of reinforced concrete apartment by using the probability of a reinforcing-steel corrosion and the carbonation tendency of domestic reinforced concrete apartments by using the statistic method. The results are as follow. ·To compare with the carbonation velocity of Kishitani's formula (x=3.727{{{{ SQRT { t} }}) when water-cement ratio is w=0.6, R=1, it is founded out that the carbonation velocity is slow a little in all area investigated and inland area, and fast a bit in coastal area. ·In the influencing factors in regard to the probability of reinforcing-steel corrosion, It seems that the influence of elapsed time is more effective than that of region. Therefore, it is necessary that it makes sure of the cover depth under apartment construction in recent so far as the durability is considered.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2017.11a
• /
• pp.222-223
• /
• 2017

해외 선진국에서 부식에 강한 플라스틱 등부표를 설치 운영하고 있으며 국내 도입을 위하여 플라스틱 부표에 대한 장 단점을 분석하는 연구가 필요하다. 본 연구에서는 특수소재 부표류의 실제 해상 설치를 통하여 등부표의 안정성 분석, 표체 상부의 색도 변화 및 조패류 부착 상태를 비교 분석하였다. 안정성 분석을 위하여 2축 디지털 경사계를 표체 상부 철탑에 설치하였으며, 플라스틱(JET-7000, PB-26) 등부표와 철재 표준형(LL-26(M)) 등부표에 대하여 일일 최대 경사각을 확인하여 각 등부표의 최대 경사각을 분석하였다. 플라스틱 부표의 해상 환경에 따른 특성 분석을 위하여 자외선에 의한 색도 변화, 해양생물의 부착정도 등을 관찰하였다.

• Journal of Environmental Science International
• /
• v.18 no.2
• /
• pp.187-195
• /
• 2009

This study was investigated to control the corrosion and scale at the cooling water system in steel works. Laboratory and field tests were performed for the indirect cooling water system of plate mill. Throughout the experiment, various factors such as leakage of pipes, heating rate and capacity, and the reaction between existing and substitute inhibitors were carefully monitored. The results showed that the harmful effect of high temperature could be minimized, and satisfactory corrosion/scale controls were effectively achieved using inhibitor, even at the increased temperature of $80^{\circ}C$. The batch and field tests in the gas scrubbing cooling water system of blast furnace and cooling water system of corex plant indicated that the new inhibitor was more effective for the prevention of corrosion and scale than the existing one.