• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.4 no.5
• /
• pp.1151-1156
• /
• 2000

In this paper, we report a fabrication of InP-based microstructurs for III-V compound semiconductor micromachining. Vertical liquid phase epitaxy(LPE) system was used in order to grow the InP/lnGaAsP/InP layers. The thicknesses of InP top-layer and InGaAsP were $1\mum \;and \;0.4\mum$, respectively. The fabrication of InGaAsP microstructures involves front-side bulk micromachining. The experimental result showed the beams must be carefully aligned in the <100> direction since the etching of the beam in the <100> direction is more faster than that of the beam in the <110> and <110> direction.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2000.05a
• /
• pp.447-450
• /
• 2000

In this paper, we report a fabrication of InP-based microstructurs for III-V compound semiconductor micromachining. Vertical liquid phase epitaxy(LPE) system was used in order to grow the Inp/InGaAsP/InP layers. The thicknesses of InP top-layer and InGaAsP were 1$\mu\textrm{m}$ and 0.4$\mu\textrm{m}$ respectively. The fabrication of InGaAsP microstructures involves front side bulk micromachining. The experimental result showed the beams must be carefully aligned in the <110> direction since the lateral etching of the beam in the <110> direction is more faster than that of the beam in the <100> direction.

• Korean Journal of Materials Research
• /
• v.7 no.6
• /
• pp.453-459
• /
• 1997

용탕단조법에 의해 제조된 Mg-9AI-2Zn 합금을 미세조직관찰, 미소경도측정, 인장시험 등을 행하여 시효거동과 기계적 성질을 조사하였다. 용탕에 가압을 한 결과 주조결함이 제거된 미세한 주조조직을 얻었으며 미세조직은 초정 $\alpha$(Mg 고용체), 과포화고용체 $\alpha$상 및 $\beta$(Mg$_{17}$AI$_{12}$)화합물의 3가지 상으로 구성되어 있었다. 16$0^{\circ}C$및 20$0^{\circ}C$에서 시효열처리한 결과 $\beta$석출물에 의한 피크 경도값이 나타났으며 피크경도에서의 석출물의 형태는 lamella 형태의 불연속 석출물이 대부분이었고 과시효에 따라 불연속석출물의 조대화와 함께 연속석출물의 분율이 증가하였다. 용탕단조방법에 의해 제조된 Mg-9AI-2Zn 합금의 인장특성은 인장강도 261.4MPa, 연산율 7.6%로서 상용 AZ 92 합금보다 인장강도 및 연신율에서 우수한 기계적 성질을 가졌는데 이는 Zn의 고용강화 및 용탕의 가압에 의한 효과였다.다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.466-473
• /
• 2001

Ni-YSZ 음극의 미세구조와 임피던스특성에 미치는 YSZ 입자크기 및 소결온도의 영향을 고찰하였다. 0.3~0.6$\mu\textrm{m}$의 미세한 NiO 분말을 사용할 경우에는 NiO 분말과 크기가 비슷한 미세한 YSZ 분말(TZ8Y, 0.3$\mu\textrm{m}$)을 첨가했을 때 NiO의 입성장을 억제하는 효과가 가장 크고 환원후 Ni의 입자크기를 미세하게 유지할 수 있는 미세구조를 형성하였다. 또한 미세한 YSZ 분말 (TZ8Y, 0.3$\mu\textrm{m}$)과 조대한 YSZ 분말(FYT13.0, 2$\mu\textrm{m}$)의 혼합비를 달리하여 후막을 제조하였을 때에 TZ8Y 분말만 첨가한 조성이 가장 낮은 분극 저항을 나타내었다. 한편 소결온도는 삼상계면의 양과 분극저항에 영향을 주었으며, 140$0^{\circ}C$에서 소결한 시편의 분극저항이 가장 낮은 값을 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.1
• /
• pp.36-42
• /
• 2010

This study has been carried out to investigate the characteristics of pellets manufactured from sawdust, and a mixture of liquid wood-tar and sawdust. Pellets were prepared at room temperature under 2000 kgf/$cm^2$ using an universal testing machine. The pellets prepared from Q. variabilis wood had slightly higher density than those prepared from P. densiflora wood. The amount of fine particles from Q. variabilis wood pellets was smaller than those from P. densiflora wood. The pellets from P. densiflora wood had higher heating values than those from Q. variabilis wood. The wood pellets manufactured with wood tar showed higher moisture content, density and heating value, but lower fine particles. From the experimental results, it is suggested that wood tar can be used to obtain the higher quality wood pellets.

• Composites Research
• /
• v.28 no.5
• /
• pp.254-259
• /
• 2015

Carbon fiber/aluminum (CF/Al) composites were successfully fabricated without pressure casting using wettability modification of carbon fiber. The wettability of liquid aluminum on carbon fibers was enhanced through electroless plating of copper on carbon fibers. Liquid aluminum was well infiltrated into carbon fiber bundles with Cu coating layer due to low wetting angle, and a lot of pores that existed in CF/Al composite without Cu coating on CF were greatly removed. However, a few tiny pores existed in carbon fiber bundles, which is due to not bad wettability between CF and Al but shrinkage cavity that was generated during cooling of CF/Al composite. The tiny pores could be effectively removed by a subsequent rolling.

• Polymer(Korea)
• /
• v.39 no.2
• /
• pp.293-299
• /
• 2015

Conductive microcellular foams consisted of polystrene (PS) and polydopamine-coated carbon nanotube (PDA-CNT) were prepared via high internal phase emulsion (HIPE) polymerization and their morphology and electrical conductivity were investigated. CNT as a conductive nanofiller was modified to PDA-CNT by coating with hydrophilic PDA on the surface of CNT to increase aqueous phase dispersion and emulsion stability. It was possible to prepare the HIPEs having higher PDA-CNT content and the resultant foams having improved conductivity due to its good dispersion. The foams showed the morphology of interconnected cell structure. As PDA-CNT content increased, yield stress and storage modulus increased and cell size reduced. The PDA-CNT content showing electrical percolation threshold was ca. 0.58 wt% and the conductivity at PDA-CNT content of 5 wt% was increased to $10^{-3}S/m$.

• Journal of the Mineralogical Society of Korea
• /
• v.23 no.3
• /
• pp.191-197
• /
• 2010

Fine nickel metal powder of uniform morphology, narrow size distribution, and high purity was prepared from high purity metal solution. Slurry reduction method for the synthesis of metal powder was applied with a special interest in their fine and spherical shape. The products were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Well dispersed ultrafine nickel powder with the particle size range of 100~200 nm was produced from Ni-hydrazine precursor using hydrazine as a reductant for 90 min reaction in 4.5 M NaOH solution.

• Journal of the Korean Vacuum Society
• /
• v.3 no.1
• /
• pp.45-50
• /
• 1994

CoCr 박막에 있어서 C축 결정배향성과 미세구조 변화에 대한 Co73Cr27 씨앗층의 영향이 조사되 었다. 기록밀도가 높고 재생전압도 높은 CoCr 수직기록매체를 개발하기 위해서는 CoCr층의 두께가 엷 으면서 결정배향성이 우수하고 결정립 크기가 적고 균일한 자성기록막 제조가 필요하다. CoCr 단층막 또는 CoCr/퍼말로이 이중막 제조에서 500$\AA$정도의 Co73Cr27 층을 씨앗층으로 만들어 줌으러써 기록층인 CoCr 박막이 $0.2mu$m의 두께에서도 천이층이 거의 없고 결정배향성이 우수한 자성막을 제조할 수 있었 다. 또한 Co73Cr27 씨앗층은 비록 결정립 크기는 증가시켰지만 기록층의 에피택시 성장에 보다 바람직 한 것으로 조사되었다.

• Transactions of the Korean hydrogen and new energy society
• /
• v.14 no.4
• /
• pp.313-320
• /
• 2003

볼밀링법을 이용하여 타이타늄 스펀지와 칩 또는 스크랩으로부터 상온애서 직접 타이타늄 수소와 분말을 재조하는 실험을 행하였다. 실험결과 진공중에서 볼링을 행한 타이타늄 스펀지와 칩의 경우 24시간외 후 합금분말의 크기는 약 20 um 정도의 크기를 갖는 것을 확인하였다. 그러나 수소화 분위기에서 볼밀링을 행한 경우에 12시간 후 수소화분말의 입도는 0.1-0.2 um로 극히 미세한 합금 분말이 제조되었다. 수소분위기에서의 볼밀링에 의한 타이타늄 분말제조는 기존의 방법에 비해 열을 가하지 않고 타이타늄 수소화분말을 얻을 수 있다는 장점과 나노크기의 미세한 수소화 분말을 얻을 수 있음을 알 수 있었다.