• Journal of the Korean Wood Science and Technology
• /
• v.31 no.4
• /
• pp.38-43
• /
• 2003

This is the second in a series of reports on the evaluation of weathering durability of waterborne preservative treated wood by accelerated weathering. The leaching of copper from ACQ-, CCA-, and CuAz-treated samples during weathering was increased by UV irradiation, when compared between full weathering and water-only weathering. The FTIR spectra of the weathered ACQ-, CCA, CuAz-treated samples at 1731 cm^-1, 1625 cm^-1, 1510 cm^-1, which are related to the fixation of copper, were different from those of unweathered controls. This result means that UV irradiation can weaken the chemical bond between lignin and copper and/or extraction of lignin-copper complex can be occured when lignin erode away by weathering.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.716-725
• /
• 2016

In this study, MCQ (Micronized copper Quat) which was copper-based wood preservative, was investigated on decay properties by difference of the its infiltration volume. After pressure-treatment with different MCQ concentration, test specimens (Japanese Red Pine) were exposed by a brown-rot fungus (Fomitopsis palustris). At the end of the 12 weeks exposure to the fungus, untreated specimen was showed the mass loss of more than 35%, and the value of preservative effectiveness of MCQ by indoor decay was $3.99{\pm}0.42kg/m^3$. Therefore, MCQ should be pressure-injected at least $3.99kg/m^3$. The three dimensional of the specimens were observed by using the light microscope and scanning electron microscope, Untreated and treatment specimens with low concentration generally had underwent serious decays and had a lot of fungal hyphae. Howere, the formation of bore hole by hyphae were not observed. Mass loss and decay properties of specimens were affected by amount of MCQ injection. Therefore, it is necessary to the review of the adequacy of the MCQ injection amount in domestic environments.

• Korean Journal of Environmental Agriculture
• /
• v.28 no.4
• /
• pp.378-385
• /
• 2009

Arsenic (As) is known to be very toxic and carcinogenic to human beings. Arsenic contaminated soil was collected from a timber mill site at Busan Metropolitan City, Korea, where chromated copper arsenate (CCA) had been used to protect wood from rotting caused by insects and microbial agents. The soil was stabilized using both natural oyster shells (NOS) and calcinated oyster shells (POS). The calcination of natural oyster shells was accomplished at a high temperature in order to activate quicklime from calcite. Two different oyster shell particle sizes (-#10 mesh and -#20 mesh) and curing periods of up to 28 days were investigated. The stabilization effectiveness was evaluated based on the Korean Standard Test (KST) method (1N HCl extraction). The stabilization results showed that the POS treatment was more effective than the NOS treatment at immobilizing the As in the contaminated soils. A significant As reduction (96%) was attained upon a POS treatment at 20 wt% and passed the Korean warning standard of 20 mg/kg ('Na' area). However, an As reduction of only 47% (169 mg/kg) was achieved upon a NOS treatment at 20 wt%. The -#20 mesh oyster shells seem to perform better than the -#10 materials. The scanning electron microscopy (SEM)-energy dispersive X-ray spectroscopy (EDX) results showed that As immobilization was strongly associated with Ca and O in the presence of Al and Si.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.1
• /
• pp.15-22
• /
• 1997

The effectiveness of presteaming for improving CCA treatability on refractory Japanese larch heartwood was investigated in this study. Presteaming was effective on improving treatability, and the extent of improvement was dependent on moisture contents of wood specimen and steaming conditions. Green wood showed higher average value in both preservative retention and penetration than dry wood, and steaming under pressure conditions also had higher treatability than steaming at atmospheric conditions. The degree of improvement for treatability was increased with the extension of steaming period. Treatability of dry wood pres teamed under pressure conditions more than 6 hours and green wood for 3 hours was similar to that enhanced by conventional incising. Presteaming green wood under pressure conditions more than 6 hours was more effective than conventional incising in improvement of CCA treatability, and resultant treatability satisfied a minimum value required for CCA-treated wood for being used at the regions of hazard class H3 and H4. In addition, an improvement of treatability by presteaming was due to an increase in permeability resulted from the degradation of hemicelluloses within aspirated pit membrane and cell wall, not the removal of extractives from pit membrane. The reduction in strength, measured as longitudinal compressive strength, due to pres teaming was related with the degradation of hemicelluloses, and was increased as steaming conditions were severe. The degree of strength reduction associated with presteaming treatment to obtain required treatability could be quantified from the relatively good relation between the increase in treatability and the decrease in strength.

• Journal of Korean Society of Forest Science
• /
• v.29 no.1
• /
• pp.1-19
• /
• 1976

This study has been made to make an observation regarding present status of the coal mine props which is desperately needed for coal production, despite of great shortage of the timber resources in this country, and investigate the effects of diffusion process on the decay resistances of the mine props as applied preservatives of Malenit and chromated zinc chloride. The results are as follows. 1. Present status of the coal mine props Total demand of coal mine props in the year of 1975 was approximately 456 thousand cubic meters. The main species used for mine props are conifer (mainly Pinus densiflora) and hardwood (mainly Quercus). Portions between them are half and half. With non fixed specification, wide varieties of timber in size and form are used. And volume of wood used per ton-of coal production shows also wide range from 0.017 cubic meter to 0.03 cubic meter. 2. Decay resistance test a) The oven dry weight decreased between untreated specimen and treated specimen has not shown any significantly, although it has shown some differences in average values between them. It may be caused by the shorter length of the test. b) The strength of compression test between untreated specimen and treated specimen has also shown the same results as shown in case of weight decrease. Reasons assumed are the same. c) The amounts of the extractives in one percent of sodium hydroxide (NaOH) between untreated and treated specimen have shown the large value in case of untreated specimen than that of treated. 3. The economical benifit between untreated and treated wood when applied in field has seen better in long term base in case of treated wood, although the primary cost of treated wood add a little bit more cost than that of the untreated wood.

• Journal of the Korean Wood Science and Technology
• /
• v.2 no.2
• /
• pp.25-31
• /
• 1974

1. Various gluing qualities applying Resorcinol Plyophen #6000 were studied on aiming the strength relationships of laminated woods resulted by single species [poplar (Populus deltoides), larch(Larix leptolepis)], mixed species of (poplar and larch), preservatives, treated poplar the scarf joint with mixed species of poplar and larch and the scarf joint treated with preservatives. 1. 1 On the block shear and on the DVL tension test, the mean wood failure ratio showed an excellent value i.e., above 65% and the tangential strength for larch was higher than that of radial, but it was reversed for poplar as shown in Tables 1 and 2. 1. 2 The lamina treated with Na-PCP reduced slightly the strength but the limited strength allowed for manufacturing laminated wood was not influenced by treating Na-PCP as shown in Tables 3 and 4. 1. 3 The safe scarf ratio in the plane scarf joint was above 1/12 for larch and 1/6 for poplar regard less of the chemical treatment or untreatment as shown in Tables. 5, 6, 7 and 8. 2. In the normal and boiled state, the gluing quality of the laminated wood composed of single[poplar (Populus deltoides), larch (Larix leptolepis)] and double species (poplar and larch) glued with Resorcinol Plyophen #6000 were measured as follow, and also represented the delamination of the same laminated wood. 2.1 The normal block shear strength of the straight and curved laminated wood (in life size) were more than three times of the standards adhesion strength. And, the value of the boiled stock was decreased to one half of the standard shear adhesion strength, but it was more than twice the standard strength for the boiled stock. Thus, it was recognized that the water resistance of the Resorcinol Plyophen #6000 was very high as shown in Tables 9 and 10. 2. 2 The delamination ratio of the straight and curved laminated woods in respect of their composition were decraesed, in turn, in the following order i. e., larch, mixed stock (larch+poplar) and poplar. The maximum value represented by the larch was 3.5% but it was below the limited value as shown in Table 11. 3. The various strengthes i.e., compressive, bending and adhesion obtainted by the straight laminaced wood which were constructed by five plies of single and double species of lamina i. e., larch (Larix leptolepis) and poplar (Populus euramericana), glued with urea resin were shown as follows: 3. 1 If desired a higher strength of architectural laminated wood composed of poplar (P) and larch (L), the combination of the laminas should be arranged as follows, L+P+L+P+L as shown in Table 12. 3.2 The strength of laminated wood composed of laminas which included pith and knots was conside rably decreased than that of clear lamina as shown Table 13. 3.3 The shear strength of the FPL block of the straight laminated wood constructed by the same species which were glued with urea adhesives was more than twice the limited adhesion strength, thus it makes possible to use it for interior constructional stock.