• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.4
• /
• pp.673-682
• /
• 2001

The use of resin composites has continued to increase over the last several years. In spite of their growing popularity, composites continue to exhibit a number of undesirable characteristics. One of the major deficiencies of composite restorative resins is their inadequate resistance to wear. Of the multitude of factors that have been associated with wear, subsurface degradation within the restoration is considered to be one. The aim of this study was to evaluate the resistance to degradation of four commercial composite resins in an alkaline solution. This solution with a high concentration of hydroxyl ions is a convenient medium for accelerated degradation of silane coupling and filler particles. The brands studies were Definite($Degussa-H\ddot{u}ls$ AG, Germany), Prodigy(Kerr, USA), Pyramid(Bisco, USA) and Synergy(Coltene, Swiss). Preweighed discs of each brand were exposed to 0.1N NaOH solution at $60^{\circ}C$. After 14 days they were removed, neutralized with HCl, washed with water and dried. Resistance to degradation was evaluated on the basis of following parameters : (a) mass loss(%)-determined from pre-and post-exposed specimen weights : (b) Si loss(ppm)-obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation $depth({\mu}m)$-measured microscopically (SEM) from polished circular sections of exposed specimens. The results were follows: 1. Mass loss of Synergy was $1.24{\pm}0.002%$, it was the highest, there was no significant difference among the materials. 2. The degree of degradation layer depth of Synergy was $107.83{\pm}2.52{\mu}m$, it was the highest, there was no significant difference among any other materials than Synergy. 3. There was no difference among the four materials in Si loss. 4. The correlation coefficient between mass loss and degradation depth was relatively high(r=0.06, p<0.05). 5. There was no coefficient correlation between Si loss and mass loss, the degree of degradation layer depth and Si loss. 6. When observed with SEM, destruction of bonding is observed between resin matrix and filler.

• The Journal of the Korean dental association
• /
• v.58 no.7
• /
• pp.435-442
• /
• 2020

Porcelain is the first ceramic material to be introduced into dentistry. Porcelain jacket crown was introduced by Dr. Charles H Land in 1886, which was an excellent aesthetic dental restoration but has not been widely used due to high firing shrinkage and low tensile strength. Then metal-ceramic system, which combines the esthetic properties of ceramics and the mechanical properties of metals, was introduced and nowadays it is still used in dental clinical field. However, the metal-ceramic system has shown some problems, such as increased lightness by reflection of light at opaque layer, shadow beneath the gingival line due to the block-out of light by metal coping, exposure of metal in margin part, bond failure between metal and porcelain, oxidation of metal coping during firing the porcelain, etc. Recently, along with the advance of fabrication methods of dental ceramics, the all-ceramic restorations with high esthetic and mechanical properties has increased and gradually replaced metal-ceramic restorations. Especially, CAD/CAM technology has opened a new era in fabricating the dental ceramic restorations. This overview will take a look at the past, present and future possibility of the dental ceramic materials.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.114-114
• /
• 1999

Boron nitride (BN)는 매우 뛰어난 물리적, 화학적 성질을 가지고 있는 재료로 많은 연구가 진행되고 있다. hexagonal 형태의 hBN의 경우 큰 전기 저항과 열 전도도를 가지고 있고 열적 안정성을 가지고 있어 반도체 소자에서 절연층으로 쓰일 수 있다. 또한 X-ray와 가시광선을 투과시키기 때문에 X-ray와 가시광선을 투과시키기 때문에 X-ray lithography이 mask 기판으로 사용될 수 있다. Boron-carbon-nitrogen (BCN) 역시 뛰어난 기계적 성질과 투명성을 가지고 있어 보호 코팅이나 X-ray lithography에 이용될 수 있다. 또한 원자 조성이나 구성을 변화시켜 band gap을 조절할 수 있는 가능성을 가지고 있기 때문에 전기, 광소자의 재료로 이용될 수 있다. 본 연구에서는 여러 합성 조건 변화에 따른 hBN 막의 합성 거동을 관찰하고, 카본 농도변화에 따른 BCN 막의 기계적 성질과 구조의 변화, 그리고 실리콘 첨가에 의한 물성 변화를 관찰하였다. BN박막은 실리콘 (100) 기판 위에 r.f. plasma assisted CVD를 이용하여 합성하였다. 합성 압력 0.015 torr, 원료 가스로 BCl3 1.5 sccm, NH3 6sccm을 Ar 15 sccm을 사용하여 기판 bias (-300~-700V)와 합성온도 (상온~50$0^{\circ}C$)를 변화시켜 BN막을 합성하였다. BCN 박막은 상온에서 기판 bias를 -700V로 고정시킨 후 CH4 공급량과 Ar 가스의 첨가 유무를 변화시켜 합성하였다. 또한 SiH4 가스를 이용하여 실리콘을 함유하는 Si-BCN 막을 합성하였다. 합성된 BN 막의 경우, 기판 bias와 합성 온도가 증가할수록 증착속도는 감소하는 경향을 보여 주었다. 기판 bias와 합성온도에 따른 구조 변화를 SEM과 Xray로 분석하였다. 상온에서 합성한 경우는 표면형상이 비정질 형태를 나타내었고, X-ray peak이 거의 관찰되지 않았다. 합성온도가 증가하게 되면 hBN (100) peak이 나타나게 되고 이것은 합성된 막이 turbostratic BN (tBN) 형태를 가지고 있다는 것을 나타낸다. 50$0^{\circ}C$의 합성 온도에서 기판 bias가 -300V에서 hBN (002) peak이 관찰되었고, -500, -700 V에서는 hBN (100) peak만이 관찰되었다. 따라서 고온에서의 큰 ion bombardment는 합성되는 막의 결정성을 저해하는 요소로 작용한다는 것을 확인 할 수 있었다. 합성된 BN 막은 ball on disk type의 tribometer를 이용하여 마모 거동을 관찰한 결과 대부분 1이상의 매우 큰 friction coefficient를 나타내었고, nano-indenter로 측정한 BN막의 hardness는 매우 soft한 막에서부터 10 GPa 정도 까지의 값을 나타내었고, nano-indenter로 측정한 BN 막의 hardness는 매우 soft한 막에서부터 10GPa 정도 까지의 값을 가지며 변하였다. 합성된 BCN, Si-BCN 막은 FT-IR, Raman, S-ray, TEM 분석을 통하여 그 구조와 합성된 상에 관하여 분석하였다. FT-IR 분석을 통해 B-N 결합과 C-N 결합을 확인할 수 있었고, Raman 분석을 통하여 DLC의 특성을 분석하였다. 마모 거동에서는 BCN 막의 경우 0.6~0.8 정도의 friction coefficient를 나타내었고 Si-BCN 막은 0.3이하의 낮은 friction coefficient를 나타내었다. Hardness는 carbon의 함유량과 Ar 가스의 첨가 유무에 따라 각각을 측정하였고 이것은 BN 막 보다 향상된 값을 나타내었다.

• Journal of the Korean Geotechnical Society
• /
• v.38 no.5
• /
• pp.47-59
• /
• 2022

A series of experiments were performed to investigate the design and application of a rubble-ground modification method with grout injection. A small-sized injection machine was designed, and the grouts with various mix proportions were injected into 25 mm aggregate using the designed small-sized injection machine. With the compressive strength of the grout ranging from 20 to 80 MPa, the uniaxial compressive strength of the grout-filling bodies with clean gravels was higher than 1/6th of the strength of grouts themselves. However, this fraction may reduce depending on the interface conditions. The erosion resistance of the hardened grout was evaluated, and it was determined that the grout with a strength greater than 15 MPa did not require erosion consideration. Moreover, a full-scale injection test was performed for 25 cm-sized rubbles in cages with a diameter greater than 1 m and a height of 1.2 m to evaluate the filling characteristics of the grout. Results from this test indicated that the grout flowability sensitively influenced the filling characteristics.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.5
• /
• pp.500-510
• /
• 2008

Statement of problem: Recently researches about WC/C (Tungsten Carbide/Carbon) or TiN (Titanium Nitride) coating on abutment screws are going on. It decreases friction coefficient, resistance against corrosion and withdrawal of physical fragility when the coating is applied to the metal surfaces. It is reported that coated abutment screws improved abrasion, adaptability and detorque force. Purpose: This study is about the effects of coated abutment screws on loosening of screw and for the purpose of solving the loosening phenomenon of abutment screws which is clinical problem. Material and methods: Detorque force and surface changes are compared when 10 times of repeated closing and opening are applied to both uncoated titanium abutment screws (Group A) and coated abutment screws with WC/C (Group B) and TiN (Group C). Each group was made up of 10 abutment screws. Results: 1. Before repeated closing and opening, Somewhat rough surface with regular direction was observed in Group A. Coated granules were observed in group B and group C and overall coated layer appeared in regular and smooth form. 2. Before repeated closing and opening, The coated surface showed bigger and thicker size of coated granules in Group C than Group B. 3. After repeated closing and opening, abrasion and deformation of abutment screw surface was observed in Group A and Group B. Exfoliation phenomenon was observed in Group B. 4. Group A showed biggest range of decrease when the weight changes of abutment screws were measured before and after repeated closing and opening. Group C showed less weight changes than Group B but there was no statistical difference between two groups. 5. Group B and Group C showed higher average detorque force than Group A and there was statistical difference. 6. Group A showed more prominent decrease tendency of average detorque force than Group B and Group C. Conclusion: Coated abutment screws with WC/C or TiN did not show prominent surface changes than uncoated titanium abutment screws even though they were repeatedly used. And they showed excellent resistance against friction and high detorque force. Thus it is considered that adaptation of WC/C or TiN coating on abutment screws will improve the screw loosening problem.

• Korean Journal of Poultry Science
• /
• v.47 no.4
• /
• pp.219-227
• /
• 2020

As the earth's average temperature rises, crop and livestock productions are at risk. Chickens are sensitive to heat stress, and increased temperatures may have adverse effects on their production performance and animal welfare. Reliable stress measurements are crucial for heat stress adaptation. Therefore, various measurement methods and biomarkers are used to evaluate poultry stress levels. Heat shock proteins (HSPs) are heat sensitive biological markers that are highly expressed under stress, thereby acting as a cellular thermometer. HSPs also have chaperone activity, which protects cells from heat stress. This review details the role of HSP70 as a molecular chaperone and biomarker for heat stress, which is important for breeding climate-adaptable, thermo-tolerant poultry.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.2
• /
• pp.273-284
• /
• 2007

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four esthetic restorative materials in an alkaline solution(0.1N NaOH). The composite resins studied were Composan LCM flow(Promedica, Germany). Clearfil ST(Kuraray medical, Japan), Durafi VS1(Heraeus Kulzer, U.S.A), Point 4(Kerr, U.S.A). The results were as follows : 1. The mass loss of each brand was $1.02{\sim}6.04%$ and highest value in Durafil VS$(6.04{\pm}0.29%)$. 2. The sequence of the degree of degradation layer depth was in descending order by Durafil VS, Clearfil ST, Point 4 and Composan LCM flow. There were significant differences between Point 4, Composan LCM flow and the others (p<0.001). 3. The sequence of the Si loss was in descending order by Clearfil ST, Durafil VS, Composan LCM flow and Point 4. There were significant differences among the materials (p<0.001). 4. On SEM, destruction of bonding between matrix and filler and on CLSM, the depth of degradation layer of specimen surface was observed. 5. The sequence of maximum wear depth was in descending order by Durafil VS, Composan LCM flow, Point 4 and Clearfil ST. There were no significant differences among the materials (p>0.001) 6. The correlation coefficient between Si loss and degradation layer depth (r=0.892, p<0.01) and Si loss and mass loss(r=0.736, p<0.01) were relatively high. These results indicate that hydrolytic degradation, wear and another factor may consider as evaluation factors of composite resins.

• The Journal of Korean Physical Therapy
• /
• v.16 no.2
• /
• pp.1-16
• /
• 2004

The purpose of this paper is to review changes in articular cartilage properties from the joint immobilization. Joint immobilization is accompanied not only by many disorders including rheumatologic disorders, degenerative disorders, trauma and fracture but treatment for disorders. Articular cartilage are sensitive to mechanical events. Immobilization is associated with cartilage degradation that may cause joint pain and reduced range of motion. An understanding of the effects of immobilization on the articular cartilage will help to plan of physical therapy program

• Magazine of the Korea Concrete Institute
• /
• v.8 no.6
• /
• pp.151-161
• /
• 1996

Recently, polypropylene fiber reinforced mortar and concrete as civil and architectural materials have been used in major countries in the world. Polypropylene fiber reinforced concrete has many advantages in terms of economical aspect, chemical stability and durability. It has been reported that polypropylene fiber can control restrained tensile stresses and cracks and increase toughness, resistance to impact, corrosion, fatigue and durability. The purpose of the present study is, therefore, to investigate the strength as well as many mechanical characteristics including toughness and shrinkage control properties. A specially devjsed shrinkage test has been applied to measure the crack control characteristics of polypropylene fiber reinforced concrete. The present study indicates that the polypropylene fiber reinforced concrete curbs greatly the crack occurrence due to shrinkage and enhances toughness resistance. The present study provides a firm base for the efficient use of polypropylene fiber reinforced concrete in actual construction such as pavements and slab structures.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.5
• /
• pp.407-415
• /
• 2008

The tubes in heat exchanger are typically made from copper alloy, stainless steel, carbon steel, titanium alloy material. type-439 ferritic stainless steel is ferromagnetic material, and furnish higher heat transfer rates than austenitic stainless steels and higher resistance to corrosion-induced flaws. Ferritic stainless steel can typically be found in low-pressure(LP) feedwater heaters and moisture separator reheaters(MSRs). LP feedwater heaters generally utilize thin wall type-439 stainless steel tubing, whereas MSRs typically employ a heavier wall tubing with integral fins. Service-induced damage can occur on the OD(outside diameter) surface of type-439 ferritic stainless steel tubing which is employed for MSRs tubing, and the most typical damage mechanism is vibration-induced tube-to-TSP(tube support plate) wear and fatigue cracking. The wear has been reported that occurs mainly on the OD surface. Accordingly, in this study, we have evaluated the flaw sizing capability of magnetic saturation eddy current technique using magnetic saturation probe and flawed specimen.