• Journal of the Korean Wood Science and Technology
• /
• v.49 no.6
• /
• pp.574-590
• /
• 2021

International efforts to prevent illegally logged wood are expanding around the world. The "Legal Wood Trade Promotion System" was enacted in Korea in 2019 to strengthen the legal import and distribution of commercial wood in Korea. Since then, this system has promoted and ensured that the imported wood and wood products are legal with respect to the country of origin, wood species, and harvested area. As verification methods, DNA analysis technology and anatomical analysis using a microscope are mainly used in conjunction. Therefore, in this study, wood species of plywood were identified by analyzing the anatomical characteristics of various wood products for the first time. Douglas fir (Pseudotsuga menziesii (Mirb.) Franco.) and larch (Larix kaempferi (Lamb.) Carriere) plywoods (7, 9 ply) were obtained from four companies that supply plywood in Korea. After cutting each company's plywood to a size of about 1 cm³, the layers from top to bottom were separated into single layers, and three sections were observed using an optical microscope. The results revealed that the plywood was composed of a mixture of softwood and hardwood wood species, pine wood species, poplar wood species, or a mixture of larch and pine wood species. Identification of wood species using microscopy is important and can enable the scientific analysis and verification of various wood products, including plywood, imported from countries where the likelihood of indiscriminate distribution of illegal wood and illegal logging is high.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.1
• /
• pp.73-84
• /
• 2018

Recently, the importance of flame retardation treatment technology has been emphasized due to the increase in urban fire accidents and fire damage incidents caused by building exterior materials. Particularly, in the utilization of wood-based building materials, the flame retarding treatment technology is more importantly evaluated. An Intumescent system is one of the non-halogen flame retardant treatment technologies and is a system that realizes flame retardancy through foaming and carbonization layer formation. To apply the Intumescent system, composite material was prepared by using Ethylene vinyl acetate (EVA) as a matrix. To enhance the flame retardant properties of the Intumescent system, a nano-clay was applied together. Composite materials with Intumescent system and nano - clay technology were processed into sheet - like test specimens, and then a new structure of cross laminated timber with improved flame retardant properties was fabricated. In the evaluation of combustion characteristics of composite materials using Intumescent system, it was confirmed that the maximum heat emission was reduced efficiently. Depending on the structure attached to the surface, the CLT had two stages of combustion. Also, it was confirmed that the maximum calorific value decreased significantly during the deep burning process. These characteristics are expected to have a delayed combustion diffusion effect in the combustion process of CLT. In order to improve the performance, the flame retardation treatment technique for the surface veneer and the optimization technique of the application of the composite material are required. It is expected that it will be possible to develop a CLT structure with improved fire characteristics.

• The Journal of the Korean bone and joint tumor society
• /
• v.16 no.1
• /
• pp.1-7
• /
• 2010

Purpose: With advances in various treatment modalities, limb salvage surgery has been commonly used in osteosarcoma of extremities. An alternative method for skeletal reconstruction is reimplantation of the tumor bearing bone following extracorporeal irradiation (ECI). We report the long-term results of ECI autograft in aspect of the oncological and functional outcomes, and complications. Materials and Methods: We retrospectively reviewed 31 osteosarcoma patients who underwent reconstruction with ECI between July 1995 and January 2006. There were 24 males and 7 females with a mean age of 24 (7-74 years) and a mean follow-up of 117 months (17-177 months). Twenty-five cases were reconstructed with ECI autograft, 6 cases with ECI autograft-prosthesis composite. The pathologic subtypes were conventional in 29 cases, periosteal in 1 case, and parosteal in 1 case. The most common location of tumor was distal femur (15 cases) followed by humerus (3), proximal fibula (3) and proximal tibia (3). Musculoskeletal Tumor Society (MSTS) score was used for functional evaluation. The overall survival rate, local recurrence, complications were analyzed. Results: The overall survival rate was 80.6% and the disease-free survival rate was 64.5%. Five patients died of distant metastasis. One patient required above-knee amputation due to local recurrence. All of them, twenty-three complications occurred, which included nonunion in 7 cases, deep infection in 5 cases, joint instability in 4 cases, metal failure in 2 cases, Limb-length discrepancy (LLD) in 2 cases, periprosthetic fracture in 1 case, epiphyseal collapse in 1, local recurrence in 1 case. The mean MSTS functional score was 62.5%. Conclusion: Extracorporeal irradiated autograft can be achieved relatively good result in aspect of oncological and functional aspect, but is needed to be additional research about occurring many complications. The reconstruction with ECI after intercalary or fragmentary resection is effective reconstruction in aspect of oncological and functional result, complications.

• Journal of Korean Society of Forest Science
• /
• v.60 no.1
• /
• pp.51-57
• /
• 1983

Properties and glue shear strength of each water soluble rues-phenol copolymer adhesive and phenolic resin adhesive were examined as a high temperature curing binder through the manufacture of plywood made of Kapur veneer. The former has different molar ratio and the latter was made from different catalyst method. The results are summarized as follows: 1) Specific gravities of air dried plywood manufactured from each adhesive ranged from 0.67 to 0.82 and their moisture contents met the K.S. standard 2) In dry and wet shear strength, adhesives with 60 percent of non volatile content showed higher values than those with 50 percent except phenolic resin. Urea-phenol copolymer resin with 20 percent of phenol content exhibited the highest, and that with 70 percent the lowest. Filling effect of wood flour on the bonding strength is great in urea-phenol copolymer resin with more than 50 percent of phenol content, especially significant in 50 percent of non volatile content including alkali catalyst phenolic resin. Alkali and acid catalyst methods were the highest among the adhesive manufacture methods. In wet strength, urea resin belongs to the lowest group. 3) In glue shear strength after boiling and drying test, no method for manufacturing phenolic formaldehyde resin adhesive was stronger than alkali and acid catalyst methods. Phenolic resin made from alkali catalyst method needs a wood flour filler to improve the bonding quality. Urea-phenol copolymer resin with 10 percent of phenol content showed the reasonable water resistance.

• Journal of the Korean Wood Science and Technology
• /
• v.24 no.1
• /
• pp.34-47
• /
• 1996

Veneers of two nominal thicknesses, 1.5 and 2.5mm, were rotary peeled from Japanese larch (Larix leptolepis). Dahurian larch (Larix gmelinei) and Radiata pine (Pinus radiata) bolts unheated and heated in the water vat temperature of $66^{\circ}C$ by rising a final temperature at 10cm core of $60^{\circ}C$ to remain core diameter of 11.4cm. 1.5 and 2.5mm thick veneer cut from the heated Japanese larch were significantly thinner than those of the unheated bolt and 2.5mm thick veneer cut from the heated Dahurian larch were significantly thicker than that of the unheated bolt. 1.5mm thick Dahurian larch veneer and 1.5 and 2.5mm thick Radiata pine veneers showed insignificant difference between the unheated and heated bolts, respectively. Check distance on the loose side of 1.5mm thick veneer cut from the heated Radiata pine was significantly wider than that of the unheated bolt. However check distances on the loose side of 1.5 and 2.5mm thick Japanese larch and Dahurian larch veneers and 2.5mm thick Radiata pine veneers showed insignificant difference between the unheated and heated bolts. Also the depth of check on the loose side of three species showed insignificantly difference between the unheated and heated bolts. Arithmatic mean deviation($R_a$) and maximum height($R_{max}$) of the profile on the loose side of dried veneer by preheating the bolt compared with unheated bolts were different among apecies and between veneer thickness. The preheating treatment slightly affected qualities of these thin veneers such as 1.5 and 2.5mm. The yield of 2.5mm thick veneer from the heated radiata pine was significantly higher than that of the unheated bolt. However the yield of 2.5mm thick veneer for other two species and 1.5mm thick veneer for three species showed insignificant difference between the unheated and heated bolts. The yield of 2.5mm thick veneer for three species were higher than those of 1.5mm thick veneer. The average yields of green veneer of Japanese larch. Dahurian larch and Radiata pine were 57.1, 55.1 and 54.0 percent, respectively. Variables such as initial MC. drying time and veneer thickness had strong effect for Japanese larch veneer, less effect for Radiata pine veneer and nuch less effect on final MC for Dahurian larch veneer in jet drying. Correlation between the current MC and the drying time of Dahurian larch with low variation of initial MC was higher than those of Japanese larch and Radiata pine veneer with high variation of initial MC in high temperature drying. Thickness shrinkages of 2.5mm thick veneer for Japanese larch and Radiata pine were higher than those of 1.5mm thick veneers, but shrinkages of Dahurian larch veneer were similar between two nominal veneer thicknesses.