[ $SiO_2$ ] nanowires were synthesized using the catalyst evaporation method. Grown nanowires had different shapes by kind of used metal catalyst. Mean diameters of grown $SiO_2$ nanowire were about 30 nm. The kind of catalysts affected microstructure of grown $SiO_2$ nanowire because of its typical growth reactions through the liquid state metal catalysts. Optical property were measured by photoluminescence spectroscopy. Relatively broad peak was obtained and mean peak positioned at 450 nm.

• 한국재료학회지
• /
• 제22권1호
• /
• pp.1-7
• /
• 2012

Thin film electrode consisting purely of porous anodic tin oxide with well-defined nano-channeled structure was fabricated for the first time and its electrochemical properties were investigated for application to an anode in a rechargeable lithium battery. To prepare the thin film electrode, first, a bi-layer of porous anodic tin oxides with well-defined nano-channels and discrete nano-channels with lots of lateral micro-cracks was prepared by pulsed and continuous anodization processes, respectively. Subsequent to the Cu coating on the layer, well-defined nano-channeled tin oxide was mechanically separated from the specimen, leading to an electrode comprised of porous tin oxide and a Cu current collector. The porous tin oxide nearly maintained its initial nano-structured character in spite of there being a series of fabrication steps. The resulting tin oxide film electrode reacted reversibly with lithium as an anode in a rechargeable lithium battery. Moreover, the tin oxide showed far more enhanced cycling stability than that of powders obtained from anodic tin oxides, strongly indicating that this thin film electrode is mechanically more stable against cycling-induced internal stress. In spite of the enhanced cycling stability, however, the reduction in the initial irreversible capacity and additional improvement of cycling stability are still needed to allow for practical use.

• 한국재료학회지
• /
• 제21권4호
• /
• pp.232-235
• /
• 2011

ZnO nanorods for gas sensors were prepared by a hydrothermal method. The ZnO gas sensors were fabricated on alumina substrates by a screen printing method. The gas-sensing properties of the ZnO nanorods were investigated for $CH_4$ gas. The effects of growth time on the structural and morphological properties of the ZnO nanorods were investigated by X-ray diffraction and scanning electron microscope. The XRD patterns of the nanocrystallized ZnO nanorods showed a wurtzite structure with the (002) predominant orientation. The diameter and length of the ZnO nanorods increased in proportion to the growth time. The sensitivity of the ZnO sensors to 5 ppm $CH_4$ gas was investigated for various growth times. The ZnO sensors exhibited good sensitivity and rapid response-recovery characteristics to $CH_4$ gas, and both traits were dependent on the growth time. The highest sensitivity of the ZnO sensors to $CH_4$ gas was observed with the growth time of 7 h. The response and recovery times were 13 s and 6 s, respectively.

• 한국재료학회지
• /
• 제17권6호
• /
• pp.323-330
• /
• 2007

We fabricated thermaly evaporated 10 nmNi/(poly)Si films to investigate the energy saving property of silicides formed by rapid thermal annealing (RTA) at the temperature of $300{\sim}1200^{\circ}C$ for 40 seconds. Moreover, we fabricated $10{\sim}50$ nm-thick ITO/Si films with a rf-sputter as reference films. A four-point tester was used to investigate the sheet resistance. A transmission electron microscope (TEM) and an X-ray diffractometer were used for the determination of cross sectional microstructure and phase changes. A UV-VISNIR and FT-IR (Fourier transform infrared rays spectroscopy) were employed for near-IR and middle-IR absorbance. Through TEM analysis, we confirmed $20{\sim}70nm-thick$ silicide layers formed on the single and polycrystalline silicon substrates. Nickel silicides and ITO films on the single silicon substrates showed almost similar absorbance in near-IR region, while nickel silicides on polycrystalline silicon substrate showed superior absorbance above 850 nm near-IR region to ITO films. Nickel silicide on polycrystalline substrate also showed better absorbance in middle IR region than ITO. Our result implies that nano-thick nickel silicides may have exellent absorbing capacity in near-IR and middle-IR region.

• 한국재료학회지
• /
• 제18권7호
• /
• pp.367-372
• /
• 2008

ZnO nanorod gas sensors were prepared by an ultrasound radiation method and their gas sensing properties were investigated for NO gas. For this procedure, 0.01, 0.005 and 0.001M of zinc nitrate hydrate [$Zn(NO_3)_2\;{\cdot}\;6H_2O$] and hexamethyleneteramine [$C_6H_{12}N_4$] aqueous solutions were prepared and then the solution was irradiated with high intensity ultrasound for 1 h. The lengths of ZnO nanorods ranged from 200 nm to 500 nm with diameters ranging from 40 nm to 80 nm. The size of the ZnO nanorods could be controlled by the concentration of solution. The sensing characteristics of these nanostructures were investigated for three kinds of sensor. The properties of the sensors were influenced by the morphology of the nanorods.

• 한국재료학회지
• /
• 제27권11호
• /
• pp.617-623
• /
• 2017

Mesoporous carbon nanofibers as electrode material for electrical double-layer capacitors(EDLCs) are fabricated using the electrospinning method and carbonization. Their morphologies, structures, chemical bonding states, porous structure, and electrochemical performance are investigated. The optimized mesoporous carbon nanofiber has a high sepecific surface area of $667m^2\;g^{-1}$, high average pore size of 6.3 nm, and high mesopore volume fraction of 80 %, as well as a unifom network structure consiting of a 1-D nanofiber stucture. The optimized mesoporous carbon nanofiber shows outstanding electrochemical performance with high specific capacitance of $87F\;g^{-1}$ at a current density of $0.1A\;g^{-1}$, high-rate performance ($72F\;g^{-1}$ at a current density of $20.0A\;g^{-1}$), and good cycling stability ($92F\;g^{-1}$ after 100 cycles). The improvement of the electrochemical performance via the combined effects of high specific surface area are due to the high mesopore volume fraction of the carbon nanofibers.

• 한국재료학회지
• /
• 제27권11호
• /
• pp.609-616
• /
• 2017

We investigated a Leidenfrost effect in the growth of ZnO nanostructures on silicon substrates by ultrasonic-assisted spray pyrolysis deposition(SPD). Structural and optical properties of the ZnO nanostructures grown by varying the growth parameters, such as substrate temperature, source concentration, and suction rate of the mist in the chambers, were investigated using field-emission scanning electron microscopy, X-ray diffraction, and photoluminescence spectrum analysis. Structural investigations of the ZnO nanostructures showed abnormal evolution of the morphologies with variation of the substrate temperatures. The shape of the ZnO nanostructures transformed from nanoplate, nanorod, nanopencil, and nanoprism shapes with increasing of the substrate temperature from 250 to $450^{\circ}C$; these shapes were significantly different from those seen for the conventional growth mechanisms in SPD. The observed growth behavior showed that a Leidenfrost effect dominantly affected the growth mechanism of the ZnO nanostructures.

• 한국재료학회지
• /
• 제14권11호
• /
• pp.795-801
• /
• 2004

The injection molded Fe sintered bodies were fabricated using two kinds of Fe powders haying 50 nm and $3\sim5{\mu}m$ in diameter. In the using of Fe powder having 50 nm in diameter, the comparatively dense bodies ($94\sim97\%$) were obtained even at low sintering temperature ($600\sim700^{\circ}C$), while in the sintered bodies ($1000^{\circ}C$) using $3\sim5{\mu}m$ Fe powder, their relative densities showed low values about $93\%$, although they were strongly depend on the sintering temperature and volume ratio of Fe powder and binder. In the sintered bodies using of 50 nm Fe powders, the volume shrinkage and grain size increased as the sintering temperature increased, but the values of hardness decreased. In the sample sintered at $650^{\circ}C$, the values of relative density, volume shrinkage and grain size were $96\%,\;37\%\;and\;0.97{\mu}n$, respectively and the minimum value of wear depth was obtained due to combination of fine grain and comparatively high density.

• 한국재료학회지
• /
• 제15권2호
• /
• pp.112-114
• /
• 2005

Dispersion stability of the $Sm_xCe_{1-x}O_{2-2/x}$ nanoparticles, which was produced by hydrothermal process, was studied in aqueous suspension using ESA (Eletrokinetic Sonic Amplitude). The average particle size of the synthesized $Sm_xCe_{1-x}O_{2-2/x}$ at nanoparticles was about $5{\pm}2nm$. The dispersion and rheological behavior of the $Sm_xCe_{1-x}O_{2-2/x}$ nanoparticles aqueous suspension was investigated using $NH_4OH\;and\;HNO_3$ as a disperse agent. The colloidal stability of aqueous suspensions with $Sm_xCe_{1-x}O_{2-2/x}$ nanoparticles at different pH values has been investigated by means of zeta potential, average particle size, and the distribution of synthesized $Sm_xCe_{1-x}O_{2-2/x}$ nanoparticles. The isoelectric point of the $Sm_xCe_{1-x}O_{2-2/x}$ nanoparticles was at pH around 11 and the value of zeta potential was at its maximum near pH 6.5.

• 한국재료학회지
• /
• 제12권6호
• /
• pp.499-507
• /
• 2002

The carbon nanotube emitters for field emission displays were fabricated by using screen printing techniques. The pastes for screen printing are composed of organic binders, carbon nanotubes (multiwalled or singlewalled), and some additive materials. The pastes were printed on Cr-coated/Ag-printed soda-lime glass substrates. From the I-V characteristics, the turn-on field of SWNT was lower than that of MWNT. The decrease in the mesh size of screen masks (i.e. increase in the opening size of the screen mesh) resulted in decreasing the turn-on field and increasing the electron emission current. When the carbon nanotubes were mixed with silver pastes, silver powders appeared to contribute to the vertically aligning of carbon nanotubes on a glass.