• Journal of the Korean Applied Science and Technology
• /
• v.36 no.4
• /
• pp.1281-1289
• /
• 2019

This study was conducted to evaluate the optimal operating condition of ultra-fine bubble washing machine for removing calcium chloride from road concrete structure. The diameter of the ultra-fine bubble was measured to 196.6 ± 100.6 nm and the ultra-fine bubble concentration was measured to 1.36 × 108 cell/ml. As a result of the performance on the spray device of the washing machine, it was confirmed that the washing efficiency of 93% and 91% appeared at 100cm and 150cm of injection distance at 100bar injection pressure. By increasing the ultra-fine bubble generation cycles from 2 to 6, the chloride removal rate increased from 1% to 7%. As the ultra-fine bubble generation air flow was lowered from 4 ml/min to 0.5 ml/min, it was confirmed that the washing efficiency increased up to 30%. The washing efficiency of ultra-fine bubble water was 25% higher than normal water.

• Journal of the Korea Concrete Institute
• /
• v.14 no.5
• /
• pp.742-749
• /
• 2002

This study was performed to clarify the formation procedure of continuous voids in cellular concrete, and to examine the effect of a foaming agent on the manufacture of cellular concrete with continuous voids. By the experiments, it was determined that cellular concrete to be formed with continuous voids is influenced by temperature, viscosity and flowability of cement paste, and stability of air voids, and is formed in accordance with cohesion of air voids. It was also found that separate voids are formed at an added amount of air voids corresponding to 2 ％ or less of the amount of cement, whereas an antifoaming phenomenon occurs when the added amount of air voids exceeds 9 ％ of the amount of cement. In products with respective cement fineness of 3,000, 6,000, and 8,000㎠/g, a higher compressive strength was exhibited at a higher cement fineness. The continuous void ratio depending on a variation in fineness was 38 ％, 52 ％, and 22 ％ in those products, respectively. That is, a highest continuous void ratio was exhibited at a cement fineness of 6,000㎠/g. When the water-cement ratio was reduced from 45％ to 25％, the compressive strength of the cellular concrete was increased from 15 kgf/㎠ to 20 kgf/㎠ Thus, the reduction in water-cement ratio was effective in achieving an increase in strength without any variation in the specific gravity of the cellular concrete.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.43 no.1
• /
• pp.1-7
• /
• 2023

A set of foamed concrete specimens with different densities were prepared, and several microscopic techniques, such as scanning electron microscope (SEM) and X-ray micro-computed tomography (micro-CT) were used to characterize the foamed specimens. The pore and solid characteristics of the specimens at different ages were examined to investigate the effect of aging on the materials. The compressive strength and the thermal conductivity of the foamed specimens were also evaluated, and the relationship between the material characteristics and properties was integrated to identify the effect of density and aging on the material properties.

• Polymer(Korea)
• /
• v.26 no.2
• /
• pp.218-226
• /
• 2002

For the preparation of high resilience polyurethane (PU) foams with polyether type cell openers which have different ethylene oxide (EO) content, molecular weight and chain structure, the influences of tell opener structure on the kinetics, rheology, structural stability, open cell content and mechanical properties of the obtained foam were investigated. It was observed that urea formation reaction was delayed with the increase of EO content and incorporation of ester linkage in cell opener molecule and was relatively independent on the molecular weight. With the rheological studies, the decreases of viscosity and storage modulus were confirmed for the increase of EO content and molecular weight, so that the resulted foam had low structural stability and high open cell content. The cell opener having ester linkage in molecule exhibited the lowest values of viscosity and storage modulus and the obtained foam has high open cell content. However, the structural stability increased due to the larger intermolecular interaction of ester linkage. The hardness, tensile strength, tear strength and elongation of foam were deteriorated with increase of EO content and molecular weight of tell opener. On the other hand, the cell opener having ester linkage in molecule improved the values of tensile strength, tear strength and elongation.

• Journal of the Korea Institute of Building Construction
• /
• v.9 no.4
• /
• pp.63-73
• /
• 2009

Recently, the use of lightweight panels in building structures has been increasing. Of the various lightweight panel types, styrofoam sandwich panels are inexpensive and are excellent in terms of their insulation capacity and their constructability. However, sandwich panels that include organic material are quite vulnerable to fire, and thus can numerous casualties in the event of a fire due to the lack of time to vacate and their emission of poisonous gas. On the other hand, lightweight foamed concrete is excellent, both in terms of its insulation ability and its fire resistance, due to its Inner pores. The properties of lightweight concrete is influenced by foaming agent type. Accordingly, this study investigates the insulation properties by foaming agent type, to evaluate the possibility of using light-weight foamed concrete instead of styrene foam. Our research found thatnon-heating zone temperature of lightweight foamed concrete using AP (Aluminum Powder) and FP (animal protein foaming agent) are lower than that of light-weight foamed concrete using AES (alkyl ether lactic acid ester). Lightweight foamed concrete using AES and FP satisfied fire performance requirements of two hours at a foam ratio 50, 100. Lightweight foamed concrete using AP satisfied fire performance requirements of two hours at AP ratio 0.1, 0.15. The insulation properties were better in closed pore foamed concrete by made AP, FP than with open pore foamed concrete made using AES.

• Journal of the Korea Convergence Society
• /
• v.8 no.12
• /
• pp.1-7
• /
• 2017

This study was conducted to investigate changes in ginsenoside by continuously treating fine bubble, which are mainly used for environmental purification, in 2-year-old ginseng. The ginsenoside content and composition of ginseng leaves and roots were analyzed for 4 months (120 days) after application of Fine bubble. As a result of treatment with common water in leaves, only Re of protopanaxatriol was significantly higher and As a result of treatment with fine buble, it was confirmed that protopanaxadiol Rb1, RC, Rb2 and Rd components were also increased. Especially, the increase of Re and Rb1 resulted in an increase of total ginsenoside. The ratio of PD / PT to ginseng was 0.811 in finebubble treated leaves and 1.28 in root. The fine bubble treatment induced the synthesis of ginsenoside from the roots and resulted in a PD / PT ratio of close to 1. Therefore, this study suggests a method of cultivating high quality ginseng using fine bubble water and suggests possibility of using it as a functional food material which can be used with leaves as well as roots.

• Journal of the Korean GEO-environmental Society
• /
• v.11 no.4
• /
• pp.33-42
• /
• 2010

The lightweight foamed concrete is used to reduce the weight of the backfill material. When it is applied, the volume is often contracted due to segregation, necessitating re-injection. In this study, it was manufactured a new lightweight foamed concrete by adding plasticizer and tested the engineering properties of the material. The tests included unconfined compressive strength test, unit weight test, flow test, pH test, and permeability test. The plasticizer is shown to have an important influence on the flow. It was shown that 2~2.4% of plasticizer was adequate. The new material was shown to have positive influence on the flow and reduction of weight when applied to the backfill of the structures.

• Journal of Korean Society of Environmental Engineers
• /
• v.34 no.1
• /
• pp.42-48
• /
• 2012

In this study, experiment on phosphorus removal was performed by using microbubble liquid film flotation tank with microbubble module. After dissolving gas and liquid in dissolving tank, microbubble liquid film system created microbubbles in equal size under fixed low pressure. After being passed through $A_2O$ and m-$O_3$ process, secondary treatment wastewater was used as influent in phosphorus removal process. When the T-P concentration of influent was 2.89 mg/L, alum(8%, 30 mg/L) was injected into a microbubble flotation tank, the treatment resulted 94% of T-P removal rate. Remaining T-P concentration was less than 0.2 mg/L, which is in accord with the effluent quality standard. Seasonal variations in water temperature showed no differences in T-P removal property. When the inflow concentration of SS was 1.0 mg/L or more, it served as coagulation nuclei in the coagulation process. In that condition, average T-P removal rate was higher than 97%. When 50% of floated scum was returned, coagulator Al included in scum assisted the injected coagulator and maximized the coagulation efficiency of pollutant. In such treatment, the T-P concentration was measured as 0.18 mg/L and satisfied the outflow water quality standard, which is 0.2 mg/L or less.

• Journal of the Korean GEO-environmental Society
• /
• v.23 no.3
• /
• pp.23-29
• /
• 2022

In this study, we investigated the ozone nanobubble process in which nanobubble and ultrasonic cavitation were applied simultaneously to improve the dissolution and self-decomposition of ozone. To confirm the organic decomposition efficiency of the process, a 200 mm × 200 mm × 300 mm scale reactor was designed and phenol decomposition experiments were conducted. The use of nanobubble was 2.07 times higher than the conventional ozone aeration in the 60 minutes reaction and effectively improved the dissolution efficiency of ozone. Ultrasonic irradiation increased phenol degradation by 36% with nanobubbles, and dissolved ozone concentration was lowered due to the promotion of ozone self-decomposition. The higher the ultrasonic power was, the higher the phenol degradation efficiency. The decomposition efficiency of phenol was the highest at 132 kHz. The ozone nanobubble process showed better decomposition efficiency at high pH like conventional ozone processes but achieved 100% decomposition of phenol after 60 minutes reaction even at neutral conditions. The effect by pH was less than that of the conventional ozone process because of self-decomposition promotion. To confirm the change in bubble properties by ultrasonic irradiation, a Zetasizer was used to measure the bubbles' size and zeta potential analysis. Ultrasonic irradiation reduced the average size of the bubbles by 11% and strengthened the negative charge of the bubble surface, positively affecting the gas transfer of the ozone nanobubble and the efficiency of the radical production.

• Korean Journal of Materials Research
• /
• v.4 no.1
• /
• pp.31-36
• /
• 1994

The bonding behavior of $SiO_{2}$ thin film and glass during VCR head fabrication was investigated, varying the surface roughness of substrate and the sputtering parameter. Insufficient fillings of grooves In the $SiO_{2}$ film with glass was postulated to give rise to the generation of bubble in the glass. The surface roughness of $SiO_{2}$ film was found to depend on that of substrate. The lower the deposition rate, the smoother the surface of film. The bubble free glass after bonding could be obtained using substrate polished with 0.05$\mu\textrm{m}$ $Al_2O_3$ powder under the sputtering condition of 10% oxygen pressure.