• 소성∙가공
• /
• 제32권5호
• /
• pp.247-254
• /
• 2023

This study conducted the wear tests on bending punches coated with PVD CrN and examined the surface quality of the product formed by each punch in the forming of uncoated TRIP1180 sheets. The study quantitatively estimated the surface quality of the product by measuring the roughness and imaging the product surface. The correlation between the punch wear depth and the product surface roughness was quantitatively analyzed. The results showed that before failure occurs, the product roughness was comparable with that of the as-received, and the product surface was smooth without scratches and defects. However, after failure, the punch wear is caused by fretting wear mechanism, and a punch whose coating is not completely peeled plows the product surface, resulting in severe scratches with grooves and ridges on the product surface. Severe wear on the punch surface caused by fretting wear can rapidly degrade the product surface quality as it is directly affected by the punch surface condition, and the product surface quality accurately reflects the punch wear condition.

• 한국산학기술학회논문지
• /
• 제2권1호
• /
• pp.1-6
• /
• 2001

회전성형법은 프레스 축 중심에 대하여 일정한 각도로 경사진 요동축과 원추형상의 상부 금형을 축 중심에 대하여 회전시키고 소재를 상승 가압하면 상부금형과 소재가 점진적으로 접촉하면서 제품을 성형하는 공정이다. 본 연구팀에서 개발된 회전 분말단조 프레스(500kN)를 이용해서 산업용 고밀도 베벨기어의 성형성 실험을 수행하였다. 실험결과로 회전 분말단조 공정과 회전 분말성형 공정에서의 성형하중, 성형밀도, 경도, 미세조직 등의 변화를 조사하여 제품의 기계적 성질을 규명하고 실제로 산업 전반에 적용할 수 있는 가능성을 제시한다.

• 산업경영시스템학회지
• /
• 제30권4호
• /
• pp.85-95
• /
• 2007

Single PPM Quality Innovation activity made a great contribution to strengthening the quality competitiveness and the international competitiveness for the domestic small and medium enterprises. But it doesn't work to companies that deal with the particular products for the difficulties during the promotion and the business management. Then, SQ-Mark, which is currently adopted to domestic automobile companies, was benchmarked and studied for its accessibility and solutions. Quality Innovation activity in the particular industry is requested to conduct the confirmation and the inspection in deeper level caused by the specialty of product itself, product engineering manufacturing processes. This study improved 6 steps of the Single PPM activity so that the Single PPM Quality Innovation activity is progressed well for the Mold industry especially among the particular industries. It shows the improvement to the management of the delivery schedule, which has been problematic, if adopted to the relating industries based on this study, it is anticipated to help the corporate operation much.

• Design & Manufacturing
• /
• 제15권3호
• /
• pp.32-38
• /
• 2021

Plate-shaped works are one of the materials that can be applied to the entire industry due to their various shapes and sizes. Plate-shaped parts workpieces are thin and wide, and when processing is completed, they are often bent or deformed in various directions, making it difficult to produce normal products. In particular, this study intends to study the processing deformation and distortion of plate-shaped parts fastened to the jig during milling processing. In this study, a method for preventing deformation occurring in plate-shaped parts was derived through jig element change and CAE analysis, and this was applied to actual processing to produce products with stable dimensions. Through a finite element analysis experiment, it was found that installing two supports on the back of the plate-shaped part results in minimal deformation and the optimal distance between the two supports is 150 mm. Through this experiment, when processing a thin plate product, a support was installed in a direction opposite to the cutting force applied to the thin plate to prevent deformation of the product, thereby improving defects.

• Design & Manufacturing
• /
• 제15권4호
• /
• pp.8-13
• /
• 2021

A plastic roller for opening and closing the safety door of the injection molding machine was molded. The dimensional change of the measurement position of the roller was studied when the cooling time was applied differently among the molding conditions, and when the temperature of the coolant applied for mold cooling was also applied differently. Cooling times of 300 seconds and 400 seconds, hot and low-temperature coolant were applied. When the low-temperature coolant was applied, the measuring point of the roller shrank by 0.03 mm. However, when the high-temperature coolant was applied, the measuring point shrank by 0.3 mm. It was found that the application of low-temperature coolant among coolants was more suitable for the reference dimension of the molded article compared to the application of high-temperature coolant. Among the cooling water applied for the molding of plastic rollers, when high-temperature coolant is applied, the shrinkage rate measured immediately after ejection was smaller than when low-temperature coolant is applied. However, it was found that post shrinkage, which occurs over time, occurs much larger when high-temperature coolant is applied.

• 산업융합연구
• /
• 제17권4호
• /
• pp.9-14
• /
• 2019

본 논문은 1mm 이하의 극소형 LED 패키지 개발 과정에서 발생할 수 있는 여러 문제점들을 제시하고 이에 대한 해결 방안을 소개한다. 기존의 금형 구조는 상하 코어부가 일체형으로 이루어져 극소형 모델의 경우 EDM(Electric Discharge Machining)의 마찰계수로 인해 다양한 오류가 발생하였고 금형의 크기를 더 줄이는데 한계 요소가 되었다. 이의 개선 방안으로 선행 연구에서 조립식 모델을 제시하여 극소형 LED 패키지 개발의 방해 요소를 극복하려 하였다. 본 논문에서는 제시된 모델에 대한 결과물을 산출하기 위한 전초 작업으로 시제품을 제작하는 중에 여러 가지 문제점이 발견되었는데 이에 대한 유형을 제시하고 해결 방안을 논한다. 그리고 같은 크기의 Lead Frame(L/F) 안에 2열 구조를 3열 구조로 배치함으로써 효율적인 생산을 고려한다. 실험 과정을 통해 제시한 해결 방안을 검증하고 시제품을 양산하기 위한 테스트를 행하여 양질의 제품을 생산할 수 있는지를 확인한다.

• 광학세계
• /
• 제13권5호통권75호
• /
• pp.20-22
• /
• 2001

향후 초박형 렌즈에 있어서 플라스틱 DOE Lens가 주도적으로 사용될 전망이고, 광통신분야에서도 WDM(wavelenght Division Multiplexer)등에 응용 가능성이 높다. DOE Pattern의 회절광량 해석기술, DTM(Diamond Turning Machine)과 Laser가공기의 정밀도 향상 등으로 금형가공기술의 급속한 발전과 함께 DOE의 보편화는 조만간 이뤄질 것으로 보인다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 제3회 금형가공 심포지엄
• /
• pp.154-160
• /
• 2004

• 기계저널
• /
• 제30권S1호
• /
• pp.30-37
• /
• 1990

공정설계 및 금형설계의 자동화, 계측, 제어 등과 같은 일련의 작업들이 종래에는 대형의 컴퓨터 에 의하여 행하여졌지만 전자산업의 빠른 진보로 퍼스널컴퓨터에 의해서도 충분히 설계를 행할 수 있게 되었다. 특히 퍼스널컴퓨터의 이용은 대형컴퓨터에 비하여 적은 비용으로 설치가 가능 하며, 이용이 용이하고, 작은 공간을 차지하므로 많은 이점을 갖고 있다.

• 한국산업경영시스템학회:학술대회논문집
• /
• 한국산업경영시스템학회 2002년도 춘계학술대회
• /
• pp.85-90
• /
• 2002

분산된 조직들 간의 다양한 업무정보의 효율적 교환과 제품제조정보의 자유로운 유통은 생산성향상에 크게 기여한다. 이를 위해 인터넷기반 'Manufacturing Desk'를 개발하여 분산된 제조조직들 사이에서 제품생산과정 중 발생하는 문제를 효율적으로 해결하고 제조정보의 원활하고 신속한 공유 및 흐름을 유지하고 궁극적으로 제조조직의 생산성을 높일 수 있도록 하였다. 이를 위해 자동차의 프레스금형 생산을 대상으로 사례기반 추론과 검색을 구현하였다. 실시간으로 제조조직들을 연계하여 업무효율성을 높이기 위해 Net Meeting의 기능을 구축하였다.