시멘트 및 건설산업은 그 제조과정에서 다량의 이산화탄소를 배출하기 때문에 지구온난화 문제를 가속화시키고 있는 것으로 알려져 있다. 따라서 이러한 시멘트를 대체할 수 있는 재료 개발에 많은 연구가 이루어지고 있으며, 철강산업 부산물인 고로슬래그 미분말은 그 중 하나의 재료라 할 수 있다. 고로슬래그 미분말은 물과 직접 반응하지 않으나 알칼리 환경하에서는 물과 반응하여 CSH 수화물을 생성하게 된다. 본 연구에서는 알칼리 자극제를 첨가한 경우의 무시멘트 경화체에 대한 강도 및 수화 특성에 대하여 분석하고자 하였다.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.3
• /
• pp.273-280
• /
• 2015

In this study, tests were carried out to find out a method to ensure the fire resistance performance of high-performance non-refractory coating CFT columns. For the high performance concrete fabrication with 100MPa, blast furnace slag(BS) and steel and nylon fibers were used. It was found that the partial replacement with BS improved the fire resistance performance of the concrete. Based on the results of lab tests, the large fire test was conducted. For this test, the CFTs with the size of ${\phi}500{\times}4,200mm$ and the reinforcement of SS 400 steel were prepared and they were subjected to a loading condition. It was found that as the level of load increased, the level of fire resistance decreased. For example, In with the loading condition of 2000kN the CFT could resist the fire for over 240 minutes, whereas, with the loading condition of 3,000kN and 4000kN applying to equivalent CFTs, the resisting time against fire were 184 minutes, and 120 minutes, respectively.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.114-121
• /
• 2010

Portland cement production is under critical review due to high amount of CO2 gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. However, most study deal only with alkali-activated ground granulated blast furnace slag or fly ash, as for the combined use of the both, little information is reported. In this study, we investigated the influence of mixture ratio of fly ash/ blast furnace slag tand curing condition on the flowability and compressive strength of mortar in oder to develop cementless alkali-activated concrete. In view of the results, we found out that the mixture ratio of fly ash/blast furnace slag always results to be significant factors. But the influence of curing temperature in the strength development of mortar is lower than the contribution due to other factors. At the age of 28days, the mixture 50% fly ash and 50% ground granulated blast furnace slag activated with 1:1 the mass ratio of 9M NaOH and sodium silicate, develop compressive strength of about 65 MPa under $20^{\circ}C$ curing.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.605-608
• /
• 2008

We have studied statistically about quality difference of Blast furnace slag Type Ⅲ that affects carbonation of concrete. According to KS F 2563 blast furnace slag was classified 3 types. Type Ⅲ blast furnace slag(specific surface area is $4000cm^2/g$) from different providers with Type A, the B and the C. The statistical technique was applied to exclude error of engineering judgement. T test and F test were used among 3 groups to investigate statistical meaning. The effect which on the quality of blast furnace slag type Ⅲ that affects carbonation of concrete is significant.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.2
• /
• pp.82-89
• /
• 2014

This study evaluates the shear performance of precast beams with ground granulated blast furnace slag. A total of four specimens according to replacement ratio of ground granulated blast furnace slag. The specimens under three loading points had a shear span-to-depth ratio of 2.5, and a rectangular section with a width of 200mm and a effect depth of 300 mm. In this study, existing equations were used for predicting the shear strength of the specimens. The shear strength by existing equations was compared with those of 89 reinforced concrete beams without shear reinforcement. It can be shown from experimental results that all specimens with ground granulated blast furnace slag showed a similar shear strength as compared with the specimen with portland cements alone.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.6
• /
• pp.1-10
• /
• 2014

In this study, thirteen reinforced concrete beams, ground granulated blast furnace slag, replacing recycled coarse aggregate with PVA fiber (BSPG series) and recycled coarse aggregate with hybrid fiber ($BSPGR_1$, $BSPGR_2$ series), and standard specimen (BSS) were constructed and tested under monotonic loading. Experimental programs were carried out to improve and evaluate the Structural performance of such test specimens, such as the load-displacement, the failure mode, and the maximum load carrying capacity. All the specimens were modeled in 1/2 scale-down size. Test results showed that test specimens ($BSPGR_1$, $BSPGR_2$ series) was increased the compressive strength by 13%, the maximum load carrying capacity by 4~21% and the ductility capacity by 4~28% in comparison with the standard specimen (BSS). And the specimens ($BSPGR_1$, $BSPGR_2$ series) showed enough ductile behavior and stable flexural failure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.669-672
• /
• 2008

To analyze possibility for high performance concrete that massively displaces blast furnace slag, this study analyzed the characteristics of concrete by blast furnace slag displacement rate changes, and the results are summarized as follows. Firstly, as for fresh concrete characteristics, flow tended to increase and air amount decreased with increase in blast furnace slag displacement rate, and settling time was shown delayed. As for hardened concrete characteristics, in conditions where blast furnace slag displacement rate increased up to 50%, the compressive strength decreased below OPC at early age, however at age 28 days, its level was no less than that of OPC, and as for temperature rise by simple insulation, it decreased as displacement rate increased at early stage of hydration, but in the latter stage, hydration progress slowed down and hydration heat increased.

• Journal of the Korea Institute of Building Construction
• /
• v.24 no.1
• /
• pp.11-21
• /
• 2024

This research elucidates the fundamental properties of carbon dioxide (CO₂)-cured mortar as influenced by varying substitution rates of blast furnace slag fine powder. The findings indicate that CO₂ curing enhances the formation of calcium carbonate (CaCO₃), contributing to pore reduction and the early development of strength. While calcium hydroxide (Ca(OH)₂) plays a more pivotal role in the primary development of strength compared to CaCO₃, an increase in the substitution rate of blast furnace slag fine powder results in reduced production of Ca(OH)₂. Nonetheless, the maintenance of strength through CaCO₃ formation is observed even after the depletion of Ca(OH)₂, suggesting that the required performance can be sustained post-exposure to the atmosphere following CO₂ curing. It is noted that substitution rates exceeding 50% lead to performance deterioration due to CO₂, highlighting the necessity for careful adjustment of the substitution ratio.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.164-170
• /
• 2002

Effect of the polymer-binder ratio and slag content on the properties of combined wet/dry-cured polymer-modified mortars using granulated blast-furnace slag are examined. Results shows that the flexural and compressive strengths of polymer-modified mortar using the slag tend to increase with increasing slag content, and reaches a maximum at a slag content of 40 ％, and is inclined to increase with increasing polymer-binder ratio. Water absorption, carbonation depth and chloride ion penetration depth tend to decrease with increasing polymer-binder ratio and slag content. Accordingly, the incorporation of slag into polymer-modified mortars at a slag content of 40％ is recommended for a combined wet/dry curing regardless of the types of polymer.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.197-198
• /
• 2018

As part of the effort to shorten the construction period, this study examined the strength expression characteristics at the early age of concrete using high fineness cement and blast furnace slag. accordingly to provide a basic data on how to solve the problem that the initial strength is lowered.