• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.9
• /
• pp.725-728
• /
• 2000

Ferroelectric thin film capacitors with high dielectric constant are important for the application of memory devices. In this work, We have systematically investigated the variation of grain sizes depending on the process condition of two-step process. Both in-situ annealing and ex-annealing have been compared depending on the annealing time. C-V measurement, ferroelectric properties, leakage current, XRD and SEM were performed to investigate the electircal properties and microstructural properties of Pb(La, Ti)O$_3$ films.

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.560-565
• /
• 2008

$(Pb_{0.98}La_{0.08})(Zr_{0.65}Ti_{0.35})O_3$ (PLZT) thin films with $TiO_2$ buffer layers were deposited on Pt/Ti/$SiO_2$/Si substrates by an R.F. magnetron sputtering method in order to improve the ferroelectric characteristics of the films. And the ferroelectric properties and crystallinities of the PLZT thin films were investigated in terms of the effects of the post annealing temperatures of $TiO_2$ buffer layers between a platinum bottom electrode and PLZT thin film. The ferroelectric properties of the PLZT thin films improved as increasing of the post annealing temperatures of $TiO_2$ layers, thereby reaching their maximum at $600^{\circ}C$.

• Journal of the Korean Vacuum Society
• /
• v.18 no.2
• /
• pp.141-146
• /
• 2009

PLZT ferroelectric thin films were deposited on Pt/Ti/$SiO_2$/Si substrate with $TiO_2$ buffer layer in between by rf magnetron sputtering method. In order to investigate the effect of Ar/$O_2$ partial pressure ratio on the ferroelectric properties of PLZT thin films, PLZT thin films were deposited at various Ar/$O_2$ partial pressure ratio ; 27/1.5 seem, 23/5.5 seem, 21/7.5 seem and 19/9.5 seem. The crystallinities of PLZT thin films were analyzed by XRD. The surface morphology was observed using FE-SEM. The P-E hysteresis loops, the remanent polarization characteristics and the leakage current characteristics were obtained using a Precision LC. The crystallinity and elaborateness of PLZT thin films were decreased as increasing the oxygen partial pressure ratio. And preferred orientation of PLZT thin films changed from (110) plane to (111) plane. The oxygen partial pressure ratio affects the thin film surface morphology and the ferroelectric properties.

• Journal of Sensor Science and Technology
• /
• v.4 no.3
• /
• pp.37-42
• /
• 1995

The PLT thin films on MgO substrate have been fabricated by RF magnetron sputtering and the dependence of properties on fabrication conditions have been studied. The PbO-rich target was used and the optimum fabrication conditions of the PLT thin films were such that substrate temperature, working pressure, $Ar/O_{2}$ ratio, and rf power was $640^{\circ}C$, 10 mTorr, 10:1, and $1.7\;W/cm^{2}$, repectively. In these conditions, the PLT thin film showed the deposition rate of $62.5\;{\AA}/min$, the Pb/Ti ratio of 1/2, and the dielectric constant of 200. The PLT thin film showed good c-axis orientation and crystalinity according to XRD and SEM analysis.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.2
• /
• pp.87-95
• /
• 1996

We have studied the effects of La concentration on the optical and electrical properties of lead lanthanum titanate (PLT) thin films by using sol-gel method. Both the optical and electrical properties are greatly affected by the La concentration. The refreactiv eindices of the films varied from 2.23 to 1.93 with varying La concentration in the range from 15 to 33 mol%. The dielectric constants of the films vary form 340 to 870 with varying La concentration in the range form 15 to 33 mol%. Hysteresis loop becomes slimmer with the increase of La concentration form 15 to 28mol% and little fatter again with the increase of La concentration form 28 to 33 mol%. Among the films investigated in this research, PLT(28) thin film shows the best dielectric properties for the application to the dielectrics of ULSI DRAM's. At the frequency of 100Hz, the dielectric constant and the loss tangent of PLT(28) thin films are 940 and 0.08 respectively. Its leakage current density at 1.5${\times}10^{5}$V/cm is 1${\times}10^{-6}A/cm^{2}$. The comparision between the simulated and the experimental curves for the switching transient characteristics shows that PLT (28) thin films behaves like normal dielectrics.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.7
• /
• pp.473-478
• /
• 2001

Ferroelectric P $b_{0.99}$［(Z $r_{0}$ 6S $n_{0.4}$)/0.9/ $Ti_{0.1}$］0.98/N $b_{0.02}$ $O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on L $a_{0.5}$S $r_{0.5}$Co $O_3$(LSCO)/Pt/Ti/ $SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole%. The crystallinity and electrical properties of the thin films annealed at various temperature and time were investigated. The thin films deposited at the substrate temperature of 500 $^{\circ}C$ and the power of 80 W were crystallized to a perovskite phase after rapid thermal annealing(RTA). The thin films annealed at 650 $^{\circ}C$ for 10 seconds in air exhibited the good crystal structures. The remanent polarization and coercive field of the PNZST capacitor were about 20 $\mu$C/$\textrm{cm}^2$ and 50 kV/cm, respectively. The reduction of the polarization after 2.2$\times$10$^{9}$ switching cycles was less than 10 %..10 %......

• Journal of the Korean Vacuum Society
• /
• v.16 no.6
• /
• pp.446-452
• /
• 2007

[ $(Pb_{1.1},La_{0.08})(Zr_{0.65}.Ti_{0.35})O_3$ ] thin films on the $Pt/Ti/SiO_2/Si$, $TiO_2(interlayer)/Pt/Ti/SiO_2/Si$ substrate were fabricated by the R.F. magnetron-sputtering method and considered their characteristics depending on $TiO_2$ interlayer. Changing the deposition conditions of $TiO_2$ interlayer, we obtained $TiO_2$ anatase single phase and rutile single phase. PLZT was deposited on these substrates and analyzed by x-ray diffraction(XRD) for there crystallinity and orientation. To investigate $PLZT-TiO_2$, $TiO_2-Pt$ interface, glow discharge spectrometer(GDS) analysis was carried out and we performed electrical measurements for dielectric properties of PLZT thin films. The PLZT thin film on $TiO_2$ anatase interlayer was found to have (110)-preferred orientation and 12.6 ${\mu}C/cm^2$ remaining polarization value.

• Proceedings of the IEEK Conference
• /
• 1999.11a
• /
• pp.199-202
• /
• 1999

반강유전 물질인 Pb[(Zr. Sn)Ti]NbO₃를 La/sub 0.5/Sr/sub 0.5/CoO₃/Pt/Ti/SiO₂/Si 기판상에 RF 마그네트론 스퍼터링 방법으로 박막화하여 그 결정성과 전기적 특성을 조사하였다. 80 W의 RF power, 400℃의 기판온도, Ar:O₂= 9:0.5의 분위기에서 증착되고, 650 ℃에서 10초동안 RTP(Rapid Thermal Process) 방법으로 열처리된 박막이 가장 우수한 페로브스카이트 구조를 보였으며, 10 ㎑ 에서 유전상수(ε')는 721, 유전손실(tan δ)은 0.06을 나타내었다. 잔류분극(Pr)은 15.5 μC/㎠ 였으며, 항전계(Ec)는 51 ㎸/㎝로 비교적 낮은 값을 나타내었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.187-191
• /
• 1995

Thin film of the (Pb$\_$1-x/La.sub x/)(Zr$\_$0.25/Ti/Sub 0.48/) O$_3$(x=0~13[at%]) were prepared by Sol - Gel method. Multi-layer PLZT thin films were fabricated by spin-coating on Pt/Ti/SiO$_2$/Si substrate. The crystallinity and microstructure of the films were investigated with the sintering condition. At the sintering temperature of of 600[$^{\circ}C$], the perovskite phase was dominat. PLZT(11/52/48)thin films sintered at 600[$^{\circ}C$], 1[hr] had good dielectric constant (1236), dielectric loss (2.2[%]), remanent polarization (1.38[${\mu}$C/$\textrm{cm}^2$] and coercive field(16.86[ kV/cm]) respectively.

• Journal of Sensor Science and Technology
• /
• v.7 no.2
• /
• pp.103-110
• /
• 1998

Pyroelectric infrared detectors based on La-modified $PbTiO_{3}$ (PLT) thin films have been fabricated by RF magnetron sputtering and rnicrornachining technology. The detectors form $Pb_{l-x}La_{x}Ti_{1-x/4}O_{3}$ (x=0.05) thin film ferroelectric capacitors epitaxially grown by RF magnetron sputtering on Pt/MgO (100) substrate. The sputtered PLT thin film exhibits highly c-axis oriented crystal structure that no poling treatment for sensing applications is required. This is an essential factor to increase the yield for realization of an infrared image sensor. Micromachining technology is used to lower the thermal mass of the detector by giving maximum sensor efficiency. Polymide is coated on top of the sensing elements to support the fragile structure and the backside of the MgO substrate is selectively etched to reduce the heat loss. The sensing element exhibited a very high detectivity D* of $8.5{\times}10^{8}cm{\cdot}\sqrt{Hz}/W$ at room temperature and it is about 100 times higher than the case of micromachining technology is not used. A sensing system that detects the position as well as the existence of a human body is realized using the array sensor.