• Journal of the Korean Vacuum Society
• /
• v.13 no.2
• /
• pp.72-78
• /
• 2004

Cu seed layers deposited by magnetron sputtering onto tantalum nitride barrier films were treated with ECR plasma and then the copper films were electroplated and rapid thermal annealed in an argon or nitrogen atmosphere at various temperatures ranging from 200 to $500^{\circ}C$. Changes in the microstructure and physical properties of the copper films electroplated on the hydrogen ECR plasma cleaned copper seed layers were investigated using X-ray diffraction (XRD), electron back-scattered diffraction (EBSD), and atomic force microscopy (AFM) analyses. It was found that the copper film undergoes complete recrystallization during annealing at a temperature higher than $400^{\circ}C$. The resistivity of the Cu film tends to decrease and the degree of (111) preferred orientation tends to increase as the annealing temperature increases. Theoptimum annealing condition for obtaining the film with the lowest resistivity, the smoothest surface and the highest degree of the (111) preferred orientation is rapid thermal annealing in a nitrogen atmosphere at $400^{\circ}C$ for 120 s. The resistivity and the surface roughness of the electroplated copper film annealed under this condition are 1.98 $\mu$O-cm and 17.77 nm, respectively.

• Korean Chemical Engineering Research
• /
• v.54 no.3
• /
• pp.293-298
• /
• 2016

A hydrogel electrolyte consisting of 6 M KOH aqueous solution, potassium polyacrylate (PAAK, 3 wt.%), and a hydrophilic silica OX50 (1 wt.%) was prepared to use as an electrolyte medium coated on a Scimat separator of activated carbon supercapacitor. The silica particle distributed homogeneously on surface pores of the separator to increase ionic conductivity and electrochemical stability of the hydrogel electrolyte. The silica addition also involved superior specific capacitance even at higher scan rates due to decrease in interfacial resistance between hydrogel electrolyte and activated carbon electrode.

• Resources Recycling
• /
• v.15 no.2 s.70
• /
• pp.32-36
• /
• 2006

Magnesium has been used as light and functional material, and its demand is increasing as a material for automobile engine and for mobile phone or notebook PC case. Fused salt electrolysis and thermal reduction are regarded as main methods for the extraction of magnesium, and choice for the method is firstly according to raw material. In this study, magnesium metal is obtained by an electrolysis of magnesium chloride. Two types of fused salt mixtures were used as electrolyte and electrolyzed at 7V with a graphite anode having the same depth, and their results were compared with each other. A mixed salt of $KCl/NaCl/MgCl_2$ was the more effective than $KCl/NaCl/CaCl_2/CaF_2/MgCl_2$ in current efficiency through the experiments at $760^{\circ}C$. Purity of the prepared magnesium metal was above 98%. Some basic data for scale-up of the magnesium electrolysis equipment, which would be necessary for a commercialization, could be obtained.

• Membrane Journal
• /
• v.18 no.4
• /
• pp.345-353
• /
• 2008

Organic/inorganic composite electrolyte membranes were prepared for dye sensitized solar cell (DSSC). Polyethylene Glycol (PEG)s with various molecular weight (400, 600, 1,500 and 3,400) was ethoxysilated to fabricate organic/inorganic composite materials through sol-gel processes. The electrolyte membranes were produced by doping the composite materials with NaI and $I_2$, and their ionic conducting behavior was investigated. The ionic conductivity of the composite electrolyte was highly affected by the PEG molecular weight, and the highest conductivity was shown by the composite membrane prepared with PEG with the molecular weight of 1,500. The composite electrolyte membranes showed considerable improvement of ionic conductivity. Compared to PEO electrolyte membranes, the composite electrolyte membrane prepared by PEG, MW 1,500, showed much higher ionic conductivity.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.16 no.4
• /
• pp.46-54
• /
• 2002

A dielectric pellets bedded parallel plates with a membrane centered have been proposed as an ion separation and collection system in water. and effects of the relative dielectric constant and the applied square wave pulse voltage on the characteristics of ion separation and collection in tap water and NaCl dissolved tap water have been investigated. As a result, electrolyzed water of pH 3.1 and 10.6 were obtained with only tap water at the pulse current of 1.0[A] and flow rate of 0.5[LPM]. And the higher ionized water of pH 2.8 and pH 11.7 ware obtained in 0.1[%wt] NaCl dissolved water. When the dielectric pellets of BaTiO$_3$ having the highest dielectric constant were bedded in the ion separation and collection cell, the ionized water of pH 2.7 and pH 11.7 were obtained with only tap water. And the ionized water of pH 2.4 and pH 12.0 were obtained in 0.1[wt%] NaCl dissolved tap water with the dielectrics pellets bedded ones.

• Polymer(Korea)
• /
• v.26 no.2
• /
• pp.179-184
• /
• 2002

Polymer electrolyte films consisting of poly (vinylidenefluoride-hexafluoro-propylene) (PVdF-HFP) $H_3PO_4$and a mixture of ethylene carbonate(EC), $\gamma$-butyrolactone(BL) and dimethylcarbonate (DMC) were examined in order to obtain the best compromise between high protonic conductivity, homogeniety and dimensional stability. Measurements of differential scanning calorimetry and ionic conductivity have been carried out for various compositions. The highest proton conductivity of 7.3 $\times$$10^{-3}Sm^{-1}$ at $30^{\circ}C$ were obtained for a film of 30(PVdF-HFP) + 50EC/DMC + 20H$_3$PO$_4$. From the thermal study, it has been found that the PVdF-HFP gels are stable up to $80^{\circ}C$, and the $H_3PO_4$ enhances the miscibility of the polymer and the solvent by interacting sensitively with polymer segments.

• Polymer(Korea)
• /
• v.26 no.6
• /
• pp.785-791
• /
• 2002

The effect of the supercritical carbon dioxide (sc$CO_2$) on ion-conductive behaviors for polyether electrolytes based on, both poly (ethylene oxide) (PEO) and poly [oligo (oxyethylene glycol) methacrylate] (PMEO) with lithium triflate, LiCF$_3$SO$_3$, has been investigated. In particular, the present research is a new concept for improving the ionic conductivity of polyether electrolytes. The maximum ionic conductivity ($\sigma$$_{max}$) at room temperature of the PEO electrolyte was more than 100 times higher, and the $\sigma$$_{max}$ at 9$0^{\circ}C$ of the PMEO electrolyte was 30 times improved by the se$CO_2$ treatment, respectively. It was revealed that the penetration of $CO_2$ molecules into the polymer matrix causes the increase of carrier ions by ion-dispersion effect and the decrease of glass transition temperature (T$_{g}$) by plasticizing effect that results in the improvement of the ion transport behaviors.viors.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.144-144
• /
• 2016

플라즈마 전해 산화법(Plasma electrolytic oxidation)에 의해 형성된 코팅층은 특유의 기공구조로 인해 부식 환경에 노출 시 부식액의 침투가 급속히 이루어지는 단점이 있다. 이를 극복하기 위한 방법으로 유기코팅, sol-gel법, 폴리머 코팅 등에 의해 기공을 봉공(sealing)하는 방법이 제안되고 있다. 본 연구에서는 Al 합금의 플라즈마 전해 산화 처리 후 질산 세륨 수용액(Cerium nitrate solution)에 의한 봉공 효과를 확인하고자 하였다. PEO 코팅을 위한 전해액은 2g/L의 KOH와 $2g/L\;Na_2SiO_3$를 증류수에 용해시켜 준비하였다. PEO 코팅층은 Al 시편을 전해액 내에 위치시켜 양극으로 하고 STS를 음극으로 하여 $0.1A/cm^2$의 펄스 정전류밀도(주파수: 100Hz, 듀티비: 20%)를 15분 동안 인가하여 형성시켰다. 봉공을 위한 실링액은 증류수에 $0.3g/L\;H_2O_2$와 $1g/L\;H_3BO_3$를 첨가하고, $Ce(NO_3)_3$를 농도 변수로 첨가하여 준비하였으며, PEO 코팅 처리된 시편을 실링액에 침지하여 실링액의 농도와 침지시간을 달리하여 봉공을 실시하였다. 제작된 PEO 코팅층에 대해 SEM, EDS, XRD를 이용한 표면분석을 실시하였으며, 내식성을 확인하고자 동전위분극시험을 실시하였다. 연구 결과, 세륨 실링 처리된 PEO 코팅 층에서 미량의 세륨 성분이 검출되었으나, 세륨계 화합물 생성에 의한 마이크로 크기의 기공의 폐쇄는 관찰되지 않았다. 또한, 전기화학적 특성 평가 결과 실링 처리된 PEO 코팅층의 경우 Al 모재에 비해 2차수 정도 감소된 부식전류밀도를 나타내었다. 이 같은 내식성의 향상은 세륨 성분에 의한 부식 억제 효과 때문으로 판단된다.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.22 no.8
• /
• pp.82-88
• /
• 2008

This paper describes the influence of the bridge formed between electrodes by electrolyte for tracking process. Electrolytes is made by IEC(International Electrotechnical Commission) 60589, NaCl added to deionized water as each 1, 3, 5[wt%]. The used test equipment is made according to KS(Korean Industrial Standard) C IEC 00112. It is investigated voltage, current, value of resistance and thermal image when bridge formed between electrodes on tracking process. As a result, as conductivity of electrolyte gets bigger as Joule's heat on bridge also gets bigger. But It is not over electrolyte's boiling point due to evaporation heat of electrolyte. However as conductivity of electrolyte gets bigger as the necessary time of dry band gets shorter. So dry band is existed more long time between ahead of droplet to next droplet and discharge chance at dry band gets much. Therefore tracking process gets faster.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.13.2-13.2
• /
• 2009

전도성 고분자는 재료의 경제적 측면 이외에 반도체로서의 다양한 전기적 특성, 생물학적 적합성, 다양한 합성 가능성 등의 우수한 장점을 지니고있어 많은 분야에 응용되고 있다. 그러나 유기물질이라는 한계로 인하여 기존 nano/microfabrication에서 일반적으로 적용되는 패터닝 방법을 적용하는데 어려움이있다. 따라서 많은 연구자들이 독립적인 나노 크기 개체를 만든 후 이의 자가 조립, 혹은 이와 유사한 방법에 의해 소자를 형성하고자 하는 노력을 기울이고 있다.이러한 bottom-up방식에 의한 소자 구성은 나노크기의 전도성 고분자 물질을 소자화하는데에는 성공하고 있으나, 복잡한 패터닝과 다양한 크기의 나노구조체를 정확한 위치에 정렬시키는 문제에 있어서 명확한 해답을 제시하지 못하는 실정이다. 본 연구에서는 현재 보편적으로 이용되고 있는 금속의nano/microfabrication공정과 전도성 폴리머의 전해합성를 복합화하여 고정밀도 및 다양한 패턴의 나노 소자를 구현하고자하였다. 이를 위하여 전해합성 조건에 따른 polypyrrole의전기적 특성을 평가하였으며, 하부 금속전극관의 복합적층화를 통한 접촉저항의 최소화를 구현하고자 하였다. 또한 이와 같은 self-alignedelectropolymerization방법을 이용하여 구성된 nano/micro 소자의 gas sensor 및 bio sensor로서의 적용가능성에 대하여평가하였다.