• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.901-904
• /
• 2001

For the c-axis oriented epitaxial YBa$_2$Cu$_3$O$_{7-{\delta}}$ thin film on r-cut sapphire substrate it is necessary to deposit buffer layers. The CeO$_2$buffer layer was deposited on sapphire substrate using RF magnetron sputtering system. We investigated XRD pattern of CeO$_2$thin films at various sputtering conditions such as sputtering gas ratio, sputtering power, target to substrate distance, sputtering pressure and substrate temperature. The optimum condition was 15 mTorr with deposition pressure, 1:1.2 with $O_2$and Ar ratio and 9cm with target to substrate distance. The CeO$_2$(200) peak was notable for a deposition temperature above 75$0^{\circ}C$. The YBa$_2$Cu$_3$O$_{7-{\delta}}$ was deposited on CeO$_2$buffered r-cut sapphire substrate using pulsed laser ablation. The YBa$_2$Cu$_3$O$_{7-{\delta}}$CeO$_2$(200)/A1$_2$O$_3$thin film was exhibited a critical temperature of 89K.xhibited a critical temperature of 89K.

• 한국초전도ㆍ저온공학회논문지
• /
• 제10권1호
• /
• pp.1-5
• /
• 2008

The effect of $BaCeO_3$ doping on the critical current density of YBCO film by TFA-MOD method was studied. $BaCeO_3$ doping was made by two method; one is direct addition of $BaCeO_3$ nano-sized powder prepared by citrate process followed by grinding with planetary ball mill for 10 hours. Another is addition of Ba-Ce precursor solution prepared with Ba-acetate and Ce acetate dissolved in TFA to the YBCO-TFA precursor solution. The film was made by standard dip coating and heat treatment process with conversion temperature of $790^{\circ}C$ in 1000 ppm oxygen containing moisturized Ar gas atmosphere. The direct addition of $BaCeO_3$ powder resulted in YBCO film with good epitaxial growth and no evidence of second phase formation. The addition through precursor solution resulted in the increase of critical current density upto 30 at% doping and uniform dispersion of $BaCeO_3$ fine inclusion was confirmed by SEM-EDX.

• 한국결정학회지
• /
• 제14권2호
• /
• pp.51-55
• /
• 2003

YBa₂CU₃O/sub 7-8/(YBCO) coated conductor의 완충층 구조를 개선하기 위하여 2축배향된 Ni-3 wt%W 합금 기판위에 단일 완충층으로 SrTiO₃(STO) 박막을 증착하였다. YBCO와 STO 박막은 펄스레이저 증착법으로 성장시켰다. STO 박막의 표면은 증착온도에 따라 다른 미세조직을 보여 주었고, XRD 분석에서는 STO와 YBCO 박막이 금속기판의 배향성을 가지면서 성장되었음을 알 수 있었다. 액체질소 온도에서 1.2 MA/㎠의 임계전류밀도와 86 K의 임계온도를 가지는 짧은 길이의 coated conductor를 STO 단일완충층을 이용하여 제조하였다.

• 센서학회지
• /
• 제8권2호
• /
• pp.195-201
• /
• 1999

$Al_2O_3$ (알루미나 및 R-면 사파이어)기판 위에 c-축 $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) 박막을 펄스레이저 증착법을 이용하여 성장하였다. 완충층으로 사용하기 위해 $Al_2O_3$ 기판 위에 증착한 $CeO_2$ 박막의 결정성은 기판온도에 많은 영향을 받았다. $CeO_2$ 박막은 $800^{\circ}C$의 기판온도에서 $\alpha$-축방향으로 잘 성장하였으며, $CeO_2$ 완충층의 두께에 따라 YBCO/$CeO_2/Al_2O_3$ 박막의 초전도 특성은 큰 변화를 나타내었다. 알루미나 기판 위에서 $CeO_2$ 완충층의 두께는 약 $1200\;{\AA}$이하, 사파이어 기판의 경우 $100{\sim}1000\;{\AA}$ 범위에서 YBCO 박막은 양호한 초전도 특성을 나타내었으나, 그 보다 두껍게 성장시킬 경우 초전도 특성이 급격하게 나빠졌다. 알루미나 기판 위에 성장된 YBCO 박막의 임계온도는 83 K였으며, R-면 사파이어 기판 위에 성장된 YBCO 박막의 임계온도는 ${\geq}89.5\;K$였고, 임계전류밀도는 77K에서 $3{\times}10^6\;A/cm^2$로 나타났다.

• Progress in Superconductivity
• /
• 제2권2호
• /
• pp.86-91
• /
• 2001

Temperature dependences of the unloaded Ｑ(Ｑ$_{0}$) and the resonant frequency ( $f_{0}$) of YB $a_2$C $u_3$ $O_{7-{\delta}}$ (YBCO) microstrip ring resonators and rutile-loaded cylindrical cavity resonators were measured at low temperatures. Dc magnetron-sputtered YBCO films grown on Ce $O_2$-buffered r-cut sapphire (CbS) substrates were used fur this purpose. The surface resistances ( $R_{s}$) of YBCO films measured by both a microstrip ring resonator and a TE $01\delta$/ mode rutile-loaded cylindrical cavity resonator are compared with each other. It turned out that the values of $R_{s}$ measured by the microstrip resonator technique are comparable to those by the rutile-loaded resonator technique at temperatures lower than ~50 K. However, above 50 K, the $R_{s}$ measured by the microstrip resonator technique appeared higher according to the temperature. Our results show that the current crowding effects near the edge of a microstrip resonator become more significant at temperatures near the critical temperature.emperature.e.e.e.e.e.e.

• 한국초전도ㆍ저온공학회논문지
• /
• 제12권3호
• /
• pp.7-11
• /
• 2010

For many large-scale applications of high-temperature superconducting materials, large critical current density($J_c$) in high applied magnetic fields are required. A number of methods have been reported to introduce artificial pinning centers(APCs) in $YBa_2Cu_3O_{7-\delta}$(YBCO) films for enhancement of their $J_c$. In this work, we investigated electric characteristic of YBCO films on $SrTiO_3$ (100) substrates whose surfaces were modified by the introduction of Au nanoparticles (AuNPs). Au nanoparticles were uniformly dispersed on STO substrates with one of typical solution techniques, self assembled monolayer. After heating the STO substrates with Au nanoparticles, the size of Au nanoparticles was around 29~32 nm in height and 41~49 nm in diameter. XRD diffraction patterns taken on the YBCO film with Au nanoparticles show the c-axis orientation. The measured $T_c$ of YBCO /AuNPs films was around 89K and the $J_c$ was 0.75 MA/$cm^2$ at 65 K and 1 T.

• 한국초전도ㆍ저온공학회논문지
• /
• 제6권1호
• /
• pp.12-17
• /
• 2004

High critical current density. $J_c$ over $1MA/cm^2$ at 77 K in a self field was successfully achieved from the YBCO film prepared on (100) $SrTiO_3$ single-crystal substrates by the TFA-MOD process. Unlike a normal TFA-MOD process, we prepared the TFA precursor solution by dissolving YBCO powder into the trifluoroacetic acid. A significant amount of the second phases, including $BaF_2$, was observed in the films fired at $700-725^{\circ}C$ for 2 h under $P(O_2)=10^{-3}$ atm and $P(H_2O)=4.2%$, most probably due to an insufficient reaction time, and hence $T_c$ was greatly degraded. However the films fired at $750-800^{\circ}C$ for 2 h were composed of strongly c-axis oriented YBCO grams without any second phases. and exhibited the $T_c$ values of 89.5 ~ 91 K with a sharp transition. With increasing the firing temperature from 750 to $800^{\circ}C$ average grain size of YBCO was increased and grain connectivity was enhanced. The highest $J_c$ value of $1.1MA/cm^2$ was obtained from the YBCO film fired at $800^{\circ}C$.

• 한국초전도ㆍ저온공학회논문지
• /
• 제15권4호
• /
• pp.15-20
• /
• 2013

We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) films with the same thickness of ~350 nm for a comparative purpose. The films were prepared on the $SrTiO_3$ (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density ($J_c$) and pinning force density ($F_p$). The anisotropic $J_{c,min}/J_{c,max}$ ratio in the field-angle dependence of $J_c$ at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic $J_c$ values of 9.0 and $2.9MA/cm^2$ with the maximum $F_p$ ($F_{p,max}$) values of 19 and $5GN/m^3$ at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller $BaZrO_3$ (BZO) nanoparticles (the average size ${\approx}28.4$ nm) than $YBa_2SnO_{5.5}$ (YBSO) nanoparticles (the average size ${\approx}45.0$ nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

• 한국산학기술학회논문지
• /
• 제7권5호
• /
• pp.801-804
• /
• 2006

[ $YBa_2Cu_3O_{7-{\delta}}(YBCO)$ ]계 초전도 선재용 $GdAlO_3(GAO)$ 버퍼층을 졸-겔(sol-gel) 공정에 의해 제조하였다. 전구체 용액은 Gd 질산염과 Al 질산염을 1:1 화학양론비로 하여 메탄올에 용해하여 준비하였다. 전구체 용액을 $SrTiO_3(STO)$ (100) 단결정 기판위에 스핀 코팅하고, 수분이 포함된 $N_2-5%\; H_2$ 분위기에서 $1000^{\circ}C$에서 2시간 열처리 하였다. 열처리 후 GAO 층의 표면에 대한 주사전자현미경 관찰에 의해 GAO 층이 에피택셜의 특징인 각면 형상을 갖는 것을 알 수 있었다. X-선 회절분석에 의하면 GAO 버퍼층은 c-축으로 우선 배향된 에피택셜 박막으로써 반가폭이 각각 (002)면에서 $0.29^{\circ}(out-of-plane)$, {112}지면에서 $1.10^{\circ}(in-plane)$의 우수한 배향성을 나타내었다.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2006년도 High Temperature Superconductivity Vol.XVI
• /
• pp.57-57
• /
• 2006