• Nano
• /
• 제13권10호
• /
• pp.1850117.1-1850117.11
• /
• 2018

Sulfated $TiO_2$ nanoparticles were successfully immobilized on zeolite through improving hydrolysis-deposition method. Microstructure, crystallization, surface state and surface area of composite catalysts were characterized by SEM, XRD, FTIR spectra, XPS and BET and the photocatalytic activity was evaluated by degradation of methyl orange under UV irradiation. We optimized these factors ($SO^{2-}_4$ ions, calcination temperature and loading amount of sulfated $TiO_2$) on photocatalytic activity and crystallization of composite photocatalysts. The results indicated that the $SO^{2-}_4$ ions are successfully immobilized on the surface of $TiO_2$, and sulfated $TiO_2$/zeolite show the highest photocatalytic activity for methyl orange at the $[SO^{2-}_4 ]/[Ti^{4+}]$ molar rate of 1:1, calcination temperature of $600^{\circ}C$ for 2 h, and sulfated $TiO_2$ loading amount of 40%, respectively.

• Korean Chemical Engineering Research
• /
• 제54권2호
• /
• pp.152-156
• /
• 2016

Brilliant blue FCF에 대한 분해 특성이 우수한 광촉매를 제조하는 연구를 수행하였다. 먼저 전구체인 titanium (IV) sulfate와 zinc acetate에 침전제로 각각 NaOH, $NH_4OH$를 첨가하여 비교적 낮은 온도와 상압에서 중간상 형성 없이 1단계의 수열합성법으로 $TiO_2$와 ZnO를 제조하였다. $TiO_2$의 경우 제조과정에 양이온성 계면활성제인 CTAB을 첨가하여 제조하기도 하였다. 제조된 $TiO_2$와 ZnO의 결정성, 입자크기, 흡광도 등과 같은 물리적 특성을 확인하기 위해 XRD, Zeta-potential meter, DRS 등을 사용하여 분석하였다. 광촉매적 특성을 확인하기 위해 회분식 반응장치를 이용하여 UV 조사 하에서 brilliant blue FCF의 광분해 특성을 조사하였다. CTAB을 첨가하지 않은 경우, $TiO_2$가 ZnO보다 입자가 작고 흡광도와 광촉매 반응의 초기속도가 큰 것을 확인할 수 있었다. 그리고 동일한 제조조건에서 CTAB을 전구체인 $Ti(SO_4)_2$ 농도의 1/10 첨가하여 제조한 $TiO_2$는 CTAB을 첨가하지 않은 것보다 brilliant blue FCF의 최종 제거율이 약 15% 정도 우수하였다.

• Bulletin of the Korean Chemical Society
• /
• 제34권11호
• /
• pp.3362-3366
• /
• 2013

A simple and quick separation technique for selenite in natural water was developed using $TiO_2$@$SiO_2/Fe_3O_4$ nanoparticles. For the synthesis of nanoparticles, a polymer-assisted sol-gel method using hydroxypropyl cellulose (HPC) was developed to control particle dispersion in the synthetic procedure. In addition, titanium butoxide (TBT) precursor, instead of the typical titanium tetra isopropoxide, was used for the formation of the $TiO_2$ shell. The synthesized nanoparticles were used to separate selenite ($Se^{4+}$) in the presence of $Se^{6+}$ or selenium anions for the photocatalytic reduction to $Se^0$ atom on the $TiO_2$ shell, followed by magnetic separation using $Fe_3O_4$ nanoparticles. The reduction efficiency of the photocatalytic reaction was 81.4% at a UV power of 6W for 3 h with a dark adsorption of 17.5% to the nanoparticles, as determined by inductively coupled plasma-mass spectrometry (ICP-MS). The developed separation method can be used for the speciation and preconcentration of selenium cations in environmental and biological analysis.

• 한국세라믹학회지
• /
• 제46권6호
• /
• pp.639-642
• /
• 2009

The research was performed to find out the optimum firing condition for the $SnO_2-TiO_2-V_2O_5$ system yellow pigment. The pigment based on $SnO_2-V_2O_5$ system showed very intense yellow color and it was used widely in ceramics industry. Synthesized pigment, with partial substitutions of $SnO_2\;by\;TiO_2$, was fired at $1300{^{\circ}C}$ soaking 1h and it showed bright yellow color. $SnO_2-TiO_2-V_2O_5$ system was very more intensive changes in yellow color by colorimetric value $b^*$ than $SnO_2-V_2O_5$ system. Synthesized yellow pigments were characterized by X-ray diffraction (XRD), FT-IR, and UV-vis spectroscopy. The best composition for yellow pigment was 93:7:0.5(mole%) for $SnO_2-V_2O_5-TiO_2$. The measurement of CIE $L^*a^*b^*$ of pigment was $L^*(78.82),\;a^*(-4.88)\;and\;b^*$(59.25).

• 한국분말재료학회지
• /
• 제12권4호
• /
• pp.266-272
• /
• 2005

Transition metal ions($Ni^{2+}$, $Cr^{3+}$ and $V^{5+}$) doped $TiO_2$ nanostructured powders were synthesized by mechanical alloying(MA) to shift the adsorption threshold into the visible light region. The synthesized powders were characterized by XRD, SEM, TEM and BET for structural analysis, UV-Vis and photoluminescence spectrum for the optical study. Also, photocatalytic abilities were evaluated by decomposition of 4-chlorophenol(4CP) under ultraviolet and visible light irradiations. Optical studies showed that the absorption wavelength of transition metal ions doped $TiO_2$ powders moved to visible light range, which was believed to be induced by the energy level change due to the doping. Among the prepared $TiO_2$ powders, $NiO^{2+}$ doped $TiO_2$ powders, showed excellent photooxidative ability in 4CP decomposition.

• 한국물환경학회지
• /
• 제29권2호
• /
• pp.204-211
• /
• 2013

In this study, the deriving optimum conditions for decolorization of Acid Orange II solution was carried using $TiO_2$ advanced oxidation process. After that, on base of the deriving results, the range of dye concentration was estimated. In addition, acute toxicity test was also carried to assess toxicity unit according to decolorization and TOC removal. In case of the blockage of light, 20 mg/L of dye solution, and 0.5 g $TiO_2$, the effect of decolorization at pH 3 was larger than at pH 6 and 10, so it was shown that decolorization is dependent on pH. The use of 5 g $TiO_2$ showed best performance of decolorization, but that of 3 g $TiO_2$ was chosen to optimum condition in considering of economical aspects. Four light sources, sun, fluorescent lamp, BLB lamp, and UV-B lamp, were used and decolorization was 99.4% and 100% at 50 mg/L, 98.6% and 99.7% at 100 mg/L for sun and UV-B lamp, respectively. In spite of the optimum condition of decolorization at pH 3, the evaluation of acute toxicity test showed highly toxic. In conclusion, although the optimum treatment of dye solution is performed, water ecology can be polluted in discharging it into water system. Therefore, it is needed to study of water ecological system with dye water treatment, and it takes all the circumstances into consideration.

• 한국결정성장학회지
• /
• 제10권3호
• /
• pp.271-277
• /
• 2000

투광성 $TiO_2$박막을 다량의 물을 사용한 티타늄알콕사이드 수용계로부터 sol-gel법으로 제조하였다. sol의 제조를 위해 각각 1 mole의 titanium(IV)iso-propoxide, acetylacetone과 8 mole의 isopropyl-alcohol로부터 킬레이트 화합물을 만들었다. 그리고 sol의 안정성을 위한 0.02~0.50 mole의 HCI과 코팅 접착성을 위한 0.3 mole의 polyethylene glycol을 함유한 50 mole의 수용액을 엄밀히 제어하여 킬레이트 화합물에 적하하였다. 제조된 sol로부터 dipping, 건조 및 $400^{\circ}C$에서 열처리하여 $TiO_2$박막을 제조하였으며, XRD, SEM, UV-visible spectrometer 등을 이용하여 특성을 검토하였다. TTIP : AcAc : IPA : $H_2$O : PEG : HCl의 몰비가 1 : 1 : 8 : 50 : 0.3 : 0.15인 조성을 갖는 중성 sol은 30일까지도 안정한 상태를 유지하였고 코팅성이 양호하였다. 30회까지 반복 침지하고 건조 및 열처리한 anatase상 $TiO_2$박막은 평활한 표면과 두께 약 2 $\mu\textrm{m}$의 치밀한 미세구조를 보였다. 제조한 $TiO_2$박막은 가시광선 영역에서 약 80%의 투과도를 나타내었다.

• Bulletin of the Korean Chemical Society
• /
• 제35권8호
• /
• pp.2295-2298
• /
• 2014

To effectively destruct 2-chlorophenol, a representative sterile preservative, nanometer-sized Mn (0.5, 1.0, 3.0 mol %)-incorporated $TiO_2$ powders were synthesized by a solvothermal method. XRD result demonstrated that the Mn ingredients were perfectly inserted into $TiO_2$ framework. The Mn-$TiO_2$ particles exhibited an anatase structure with a particle size of below 20 nm. The absorbance was shifted to the higher wavelength on Mn-$TiO_2$ compared to that of $TiO_2$. Otherwise, the PL intensities which has a close relationship for recombination between holes and electrons significantly decreased on Mn-$TiO_2$. The photodecomposition for 2-chlorophenol in a liquid system was enhanced over Mn-doped $TiO_2$ compared with pure $TiO_2$: 2-chlorophenol of 50 ppm was completely decomposed after 12 h when 1.0 mol % Mn-$TiO_2$ was used. Consequently, the core of this paper is as follows. introducing Mn into $TiO_2$ framework reduced the band-gap, moreover, it played as an electron capture resulted to lower recombination between electrons and holes during photocatalytic reaction for removal of 2-cholophenol.

• 한국대기환경학회지
• /
• 제16권4호
• /
• pp.373-380
• /
• 2000

A new type of photocatalyst plasma air purification filter for decomposition of some VOCs has been developed. The photocatalyst plasma air purification filter employs the pulsed discharge plasma as an energy source of TiO2. photocatalyst instead of UV light. In closed room(2m3) test removal efficiency of some VOCs was 80∼100% in 15∼24 hours. In the initial step of phptocatalyst plasma reaction. Acetone and Nitromethane etc were detected. But they were completely oxidized to CO2 and H2O.

• 한국환경보건학회지
• /
• 제31권5호
• /
• pp.415-422
• /
• 2005

The photocatalytic decolorization of Reactive Red 2B(RR2B) was studied using immobilized photocatalyst/UV System. Two pairs of 20 W UV-B and UV-C lamps were employed as the light source. Immobilization of $TiO_2$ was carried out using sponge (as the photocatalyst body) and silicone sealant(as the binder). The effects of parameters such as the thickness, pore size of sponge photocatalyst and attached material on the reactor bottom were investigated. The results showed that the optimum thickness of sponge photocatalyst was 1 cm. Decolorization of reactor which had the bottom coated $TiO_2$ was higher than that of reactor attached aluminum plate. Decolorization of photocatalyst with large pore size(mean pore size, 3.8 mm) was higher than that of the small(mean pore size, 1.75 mm). Initial decolorization of RR2B could be descrived using the Langmuir-Hinshelwood(L-H) model and gave constant values of $0.55mg/l{\cdot}min(k)\;and\;2.65{\times}10^{-2}l/mg(K)$, respectively.