• 한국세라믹학회지
• /
• 제30권6호
• /
• pp.510-516
• /
• 1993

$PbTiO_3$ thin films have been formed by rapid thermal annealing(RTA) of $TiO_2$/Pb/$TiO_2$ multilayer films deposited on Si wafers by RF sputtering. Based on the optimal depositon conditions of TiO2 and Pb, $TiO_2$/Pb/$TiO_2$ three layers were deposited for 900$\AA$ each. These films were subjected to RTA process at the temperatures ranging from $400^{\circ}C$ to $900^{\circ}C$ for 30 seconds in air, and were analyzed by X-ray diffraction and transmission electron microscopy to investigate the phases and the microstructures. As a result, perovskite $PbTiO_3$ phases was obtained above $500^{\circ}C$ with the trace of unreacted $TiO_2$. RBS analysis revealed the anisotropic behavior of diffusion that the diffusivity of Pb to the bottom $TiO_2$ layer was faster than that of Pb to the top $TiO_2$ layer. The amorphous Pb-silicate was formed between film and Si substrate due to the diffusion of Pb, but Pb-silicate existed locally at the interface and the amount of that phase was very small. Therefore the effect of bottom $TiO_2$ layer as a diffusion barrier was confirmed. $PbTiO_3$ films formed by current technique showed a relative dielectric constant of 60, and the maximum breakdown field reached 170kV/cm.

• 한국세라믹학회지
• /
• 제35권11호
• /
• pp.1130-1140
• /
• 1998

Thin films of $Bi_4Ti_3O_{12}\;nBaTiO_3(n=1&2)$ were prepared using sols erived Ba-Bi-Ti complex alkoxides. The sols were spin-cast onto $Pt/Ti/SiO_2/Si$ substrates and followed by pyrolysis for 1 hr at $620^{\circ}C,\;700^{\circ}C\;and\;750^{\circ}C$ In the thin films a pyrochlore phase seemed to be formed at a lower temperature and then tran-formed to the layered perovskite phase as the heating temperature increased. In the thin films pyrolyzed at formed to the layered perovskte phase as the heating temperature increased. In the films pyrolyzed at $750^{\circ}C$ the amount of $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ reached to 94% while $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ was 77% in composition. This result shows that the formation of the layered pervoskite phase becomes difficult as the amount of complexing $BaTiO_3$ increases. The microstructures and the electrical properties of the thin films were gen-erally improved with the incease of the heating temperature. However the presence of the pyrochlore phase could not be removed effectively. Our study showed that the electrical properties of $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ were pronouncedly improved with complexing with BaTiO3 when compared to those of $Bi_4Ti_3O_{12}$ while the presence of the pyrochlore phase was detrimental to the those of $Bi_4Ti_3O_{12}{\cdot}2BaTiO_3$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.79-81
• /
• 2004

$TiO_2-SnO_2$ thin films are fabricated using sol-gel method. The thickness of thin films increase about $0.03{\sim}0.04{\mu}m$ every a dipping. The permittivity and dissipation factor of $TiO_2-SnO_2$ thin films decrease with increasing frequency. Thin films show semiconductive characteristics above $400^{\circ}C$.

• 한국재료학회지
• /
• 제24권4호
• /
• pp.207-213
• /
• 2014

Flexible $BaTiO_3$ films as dielectric materials for high energy density capacitors were deposited on polyethylene terephthalate (PET) substrates by r.f. magnetron sputtering. The growth behavior, microstructure and electrical properties of the flexible $BaTiO_3$ films were dependent on the sputtering pressure during sputtering. The RMS roughness and crystallite size of the $BaTiO_3$ increased with increasing sputtering pressure. All $BaTiO_3$ films had an amorphous structure, regardless of the sputtering pressures, due to the low PET substrate temperature. The composition of films showed an atomic ratio (Ba:Ti:O) of 0.9:1.1:3. The electrical properties of the $BaTiO_3$ films were affected by the microstructure and roughness. The $BaTiO_3$ films prepared at 100 mTorr exhibited a dielectric constant of ~80 at 1 kHz and a leakage current of $10^{-8}A$ at 400 kV/cm. Also, films showed polarization of $8{\mu}C/cm^2$ at 100 kV/cm and remnant polarization ($P_r$) of $2{\mu}C/cm^2$. This suggests that sputter deposited flexible $BaTiO_3$ films are a promising dielectric that can be used in high energy density capacitors owing to their high dielectric constant, low leakage current and stable preparation by sputtering.

• 한국광학회지
• /
• 제5권1호
• /
• pp.9-17
• /
• 1994

Ar 이온빔 보조 증착법(IBAD)으로 제작한 $TiO_2$ 박막의 광학적 특성을 연구하였다. 포락선 방법으로 측정한 단층 IBAD TiO2 박막의 굴절률은 이온빔을 사용하지 않은 보통 $TiO_2$ 박막보다 증가하여 bulk의 값에 보다 가까웠으며, 진공과 공기 중에서 투과 파장 영역의 이동을 측정하여 조사한 단층 IBAD 박막의 조밀도는 보통 박막보다 현격히 증가하였다. 이온빔 보조 증착법으로 $(TiO_2/SiO_2)$ 다층 박막 간섭필터를 제작하였고, 진공과 공기 중에서 각각 간섭 필터의 최고 투과 파장의 이동을 측정하였다. IBAD 간섭 필터의 파장 이동량은 보통 간섭필터에 비해 무시할 수 있을 정도로 작아 IBAD 박막의 조밀도가 증가하고 광학적으로 안정된 것을 알 수 있었다. 또한 IBAD $TiO_2$ 박막과 보통 $TiO_2$ 박막 모두 원소 조성비는 정상이었으며 결정 구조는 비정질이었다.

• 한국표면공학회지
• /
• 제35권6호
• /
• pp.383-390
• /
• 2002

To investigate behaviors of Ti and O elements and microstructures of anodic titanium oxide films, the films were prepared by anodizing pure titanium in $H_2$S $O_4$, $H_3$P $O_4$, and $H_2O$$_2$ mixed solution at 180V. The microstructures and chemical states of the elements were analyzed using SEM, X-ray mapping, AFM, XRD, XPS (depth profile). The films formed on a titanium substrate showed porous layers which were composed of pore and wall, And with increasing anodizing time a hexagonal shape of cell structures were dominant and solace roughness increased. From the XRD result the structure of the Ti $O_2$ layer was anatase type of crystal on the whole. In the XPS spectra it was found that Ti and O were chemically binded in forms of Ti $O_2$, TiOH, $Ti_2$ $O_3$ at Ti 2p, and Ti $O_2$, $Ti_2$ $O_3$, $P_2$ $O_{5}$, S $O_4^{2-}$ at O ls respectively. Concentration of Ti $O_2$ decreased as the depth increased from the surface of the oxide film towards the substrate, but to the contrary concentrations of TiOH and $Ti_2$ $O_3$ increased.d.

• 한국광학회지
• /
• 제16권2호
• /
• pp.168-173
• /
• 2005

고주파 마그네트론 동시 스퍼터링법을 이용하여 $TiO_2$ 박막에 Ag를 도핑한 $Ag/TiO_2$ 박막을 제작하고, 열처리 온도에 따른 박막의 물리적, 화학적 특성을 조사하였다. XRD 측정 결과로부터 금속을 도핑한 박막이 순수 $TiO_2$ 박막보다 결정크기가 더 작은 것을 확인하였으며, SEM 측정 결과로부터 $Ag/TiO_2$ 박막은 순수 $TiO_2$ 박막보다 골자의 크기가 작고 균일하다는 것을 알 수 있었다. 제작된 박막은 가시광선 영역에서 높은 투과율을 나타내었다. $600^{\circ}C$에서 열처리한 박막은 아나타제 결정상이 나타났으며, $900^{\circ}C$에서 열처리한 박막은 아나타제와 루타일상이 혼합되어 나타났다 특히, $900^{\circ}C$에서 열처리한 경우 아나타제에서 루타일로의 상전이에 따른 밴드갭 에너지의 변화에 의해 박막의 흡수단이 장파장 영역으로 이동하였다. 또한 박막 내의 흡수와 산란효과에 의해 투과율이 감소하였다. $Ag/TiO_2$ 박막의 광활성은 순수 $TiO_2$ 박막보다 우수함을 알 수 있었다.

• 한국재료학회지
• /
• 제17권3호
• /
• pp.125-131
• /
• 2007

[ $TiO_{2}-solution$ ] was aaded in $SiO_{2}-solution$ by various composition. $SiO_{2}-TiO_{2}$ thin films were obtained by the dip-coating method on the $SiO_{2}$ glass substrates, and then heat-treated at various temperature. Nano-size $TiO_{2}$ particles dispersed $SiO_{2}-TiO_{2}$ films showed absorption peak by quantum size effect at short wavelength region $350{\sim}400nm$, which made them good candidates for non-linear optical materials and photo-catalytic materials. The thickness of $SiO_{2}-TiO_{2}$ films were $300{\sim}430nm$. The contact angle of $SiO_{2}-TiO_{2}$ films for water was $5.3{\sim}47.9^{\circ}$, and therefore it is clear that $SiO_{2}-TiO_{2}$ films have super hydrophilic properties and the self-cleaning effects.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 제36회 하계학술대회 논문집 C
• /
• pp.1850-1852
• /
• 2005

$SrTiO_3$ and $BaTiO_3$ sol-liquids and powders were prepared by the sol-gel method. $SrTiO_3/BaTiO_3$ heterolayered thin/thick films have been prepared on the $Al_2O_3$ substrates by screen printing and spin-coating method. The thin films were sintered at $750^{\circ}C$ in the air for 1 hour and the thick films sintered at $1325^{\circ}C$ in the air for 2 hours, respectively. The $SrTiO_3/BaTiO_3$ thin/thick films's structural and dielectric properties were investigated. Increasing the spin-coating times, (110), (200), (211) peaks of the $SrTiO_3$ were increased. The X-ray diffraction(XRD) patterns and SEM photographs indicated that the $SrTiO_3$ phase were formed in the surface of $BaTiO_3$ thick films. The average thickness of a $BaTiO_3$ thick films and $SrTiO_3$ thin films were $50{\mu}m$ and 400nm, respectively The dielectric constant and dielectric loss of the $SrTiO_3/BaTiO_3$ thin/thick films with $SrTiO_3$ coated 5 times were 1598 and 0.0436 at 10KHz.

• 한국전기전자재료학회논문지
• /
• 제29권5호
• /
• pp.294-297
• /
• 2016

Titanium oxide ($TiO_2$) thin films were fabricated by unbalanced magnetron (UBM) sputtering. The fabricated $TiO_2$ films were treated by oxygen plasma under various RF powers. We investigated the characteristics of oxygen plasma treatment on the surface, structural, and physical properties of $TiO_2$ films prepared at various plasma treatment RF powers. UBM sputtered $TiO_2$ films exhibited higher contact angle value, smooth surface, and amorphous structure. However, the rms surface roughness $TiO_2$ films were rough, and the contact angle value was decreased with the increase of the plasma treatment RF power Also, the hardness value of $TiO_2$ film as physical properties was slightly increased with the increase of the plasma treatment RF power. In the results, the performance of $TiO_2$ films for self cleaning critically depended on the with the plasma treatment RF power.