• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.321-324
• /
• 1991

In this study, $(Sr{\cdot}Pb)TiO_3$ series ceramics which is used in high voltage were fabricated by the mixed oxide method, and the electrical conduction mechanism and D.C. breakdown voltage characteristics of the specimens in accordance with the contents of $Bi_2O_3{\cdot}3TiO_2$ were investigated. As a result, the leakage current was increased with the contents of $Bi_2O_3{\cdot}3TiO_2$ and the measuring temperature. At room temperature, the leakeage current was showed a tendency of saturating when D.C. electrical field of $l5{\sim}30$[kV/cm] was applied to the specimen. As a result of breakdown voltage characteristics. breakdown strength was decreased when the contents of $Bi_2O_3{\cdot}3TiO_2$ were increased. On the other hand, in the temperature region below $60[^{\circ}C]$, the electronic breakdown was occured, and in the temperature region from 60 to $200[^{\circ}C]$, the thermal breakdown was occured by the Joule heat and the dissipation factor.

• Electrical & Electronic Materials
• /
• v.8 no.5
• /
• pp.611-618
• /
• 1995

The (Sr$_{1-x}$ .Ca$_{x}$)TiO$_{3}$+0.6[mol%]Nb$_{2}$O$_{5}$ (0.05.leq.x.leq.0.2) ceramics were fabricated to form semiconducting ceramics by sintering at about 1350[.deg. C] in a reducing atmosphere(N$_{2}$ gas). Metal oxides, CuO, was painted on the both surface of the specimens to diffuse to the grain boundary. They were annealed at 1100 [.deg. C] for 2 hours. The 2nd phase formed by thermal diffusing from the surface lead to a very high apparent dielectric constant. According to increase of the frequency as a functional of temperature, all specimens used in this study showed the dielectric relaxation, and the relaxation frequency was above 106 [Hz], it move to low frequency with increasing resistivity of grain. The specimens showed three kinds of conduction mechanisms in the temperature range 25-125 [.deg. C] as the current increased: the region I below 200 [V/cm] shows the ohmic conduction. The region rt between 200 [V/cm] and 2000 [V/cm] can be explained by the Poole-Frenkel emission theory, and the region III above 2000 [V/cm] is dominated by the tunneling effect.fect.

• Journal of the Korean Ceramic Society
• /
• v.40 no.5
• /
• pp.455-459
• /
• 2003

Tunneling spectra of B $i_2$S $r_2$Ca(C $u_{1-x}$ N $i_{x}$ )$_2$ $O_{8+}$$\delta$/ film by LPE method have been measured using break junctions. The energy gap 2$\Delta$ and 2$\Delta$/ $k_{B}$ $T_{c}$ $^{zero}$ increased with increase of ft. We obtained the energy gap Parameter 2$\Delta$(4.2 K) = 54.4~64 meV, and corresponding1y $\Delta$/ $k_{B}$ $T_{c}$ $^{zero}$=7.36~10.14, larger than the BCS value. The lattice constant c and critical temperature $T_{c}$ $^{zero}$ decrease with increase of $\chi$$_{L}$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.5
• /
• pp.393-399
• /
• 2020

A series of phosphors, SrWO₄:5 mol% Dy³⁺, SrWO₄:5 mol% Sm³⁺, and SrWO₄:5 mol% Dy³⁺:x Sm³⁺ (x＝1~15 mol%), were prepared using a facile co-precipitation. The crystal structure, morphology, photoluminescence properties, and application in anti-counterfeiting fields were investigated. The crystalline structures of the prepared phosphors were found to be tetragonal systems with the dominant peak occurring at the (112) plane. The excitation spectra of the Dy³⁺ singly-doped SrWO₄ phosphors were composed of an intense charge-transfer band centered at 246 nm in the range of 210~270 nm and two weak peaks at 351 nm and 387 nm due to the ⁶H_15/2→⁶P_7/2 and ⁶H_15/2→⁴I_13/2 transitions of Dy³⁺ ions, respectively. The wavelength of 246 nm was optimum for exciting the luminescence of Dy³⁺ and Sm³⁺ co-doped SrWO₄ phosphors. The emission spectra consisted of two intense blue and yellow emission bands at 480 nm and 573 nm corresponding to the ⁴F_9/2→⁶H_15/2 and ⁴F_9/2→⁶H_13/2 transitions of Dy³⁺, and two strong emission peaks at 599 nm and 643 nm originating from the ⁴G_5/2→⁶H_7/2 and ⁴G_5/2→⁶H_9/2 transitions of Sm³⁺, respectively. As the concentration of Sm³⁺ ions increased, the emission intensities of Dy³⁺ rapidly decreased, while the emission intensities of Sm³⁺ gradually increased. These results suggest that the color of the emission light can be tuned from yellow to white by changing the concentration of Sm³⁺ ions at a fixed 5 mol% Dy³⁺. Furthermore, the fluorescent security inks were synthesized for use in anti-counterfeiting applications.

• Journal of the Korean Ceramic Society
• /
• v.37 no.12
• /
• pp.1212-1220
• /
• 2000

Bi-2223 초전도체계에서 석출물을 flux-pinning center로 이용할 수 있는지 가능성을 타진하기 위하여 $Bi_{1.8}$P $b_{0.4}$S $r_{2}$C $a_{2.2}$C $u_3$ $O_{8}$ 조성을 가진 Bi-2223/Ag 선재를 반응온도, 산소분압, 시간 등을 변화시키면서 열처리를 행하였다. 열처리 후 석출물들은 XRD, SEM, TEM, EDS로 분석하였다. Bi-2223 모상내의 (Ca, Sr)$_2$(Pb,Bi) $O_4$, B $i_{0.5}$ P $b_3$S $r_2$C $a_2$Cu $O_{12+}$$\delta$/ (3221)와 같은 2차상들의 크기와 분포는 2223 입자들의 연결성을 파괴하지 않고 열처리 조건에 의해서 조절할 수 있었다. 서냉 열처리가 된 시편은 임계전류밀도( $J_{c}$)값이 증가하였는데, 이는 2223 입자내 나노미터 크기로 형성된 석출물들이 flux-pinning sites로 작용한 것으로 추정된다.다.

• Asian-Australasian Journal of Animal Sciences
• /
• v.10 no.2
• /
• pp.201-205
• /
• 1997

An experiment has been conducted to compare the sweating rate between male and female Bali cattle under tropical conditions in Bali, Indonesia with dry bulb (DB) temperatures varying from 25 to $34.5^{\circ}C$ and relative humidity (RH) 70 to 98%. Rectal temperature (Tr) was significantly different (p < 0.05) between males and females (39.7 vs $39.4^{\circ}C$ compared to 39.2 vs $38.8^{\circ}C$ on weeks 1 and 8 respectively). There were significant effects on RR associated with both $week{\times}sex$ (p < 0.01) and $sex{\times}time$ (p < 0.01) interactions, with values for males higher than females. Skin temperature (Ts) differed significantly between sexes (p <0.05), weeks (p < 0.05) and times (p < 0.01); being lower in females (36 vs $36.4^{\circ}C$). With prolonged working, there were marked increase in RR were recorded after 30 minutes (the overall increase was $12.4^{\circ}C$). Sweating rate (SR) differed significantly between sexes (p < 0.05), weeks (p < 0.01) and times (p < 0.01) during exercise. Females had a lower mean SR ($225.3g/m^2/h$) than males ($238.8g/m^2/h$). With increasing time, the highest SR was achieved after 30 minutes of exercise of $313.3g/m^2/h$.

• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.165-168
• /
• 2000

We fabricated ramp-edge Josephson junctions with barriers formed by interface treatments instead of epitaxially grown barrier layers. A low-dielectric Sr$_2$AlTaO$_6$(SAT) layer was used as an ion-milling mask as well as an insulating layer for the ramp-edge junctions. An ion-milled YBa$_2$Cu$_3$O$_{7-x}$ (YBCO)-edge surface was not exposed to solvent through all fabrication procedures. The barriers were produced by structural modification at the edge of the YBCO base electrode using high energy ion-beam treatment prior to deposition of the YBCO counter electrode. We investigated the effects of high energy ion-beam treatment, annealing, and counter electrode deposition temperature on the characteristics of the interface-controlled Josephson junctions. The junction parameters such as T$_c$, I$_c$c, R$_n$ were measured and discussed in relation to the barrier layer depending on the process parameters.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.12
• /
• pp.1610-1616
• /
• 1995

The (Sr$_{1-x}$ .Ca$_{x}$)TiO$_{3}$(0.05.leq.x.leq.0.2) ceramics were fabricated to form semiconducting ceramics by sintering at about 1350[.deg. C] in a reducing atmosphere (N$_{2}$ gas). After being fired in a reducing atmosphere, metal oxides, CuO, was painted on the both surface of the specimens to diffuse to the grain boundary. They were annealed at 1100[.deg. C] for 2 hours. The 2nd phase formed by thermal diffusing from the surface lead to a very high apparent dielectric constant. The results of the capacitance-valtage measurements indicated that the grain boundary was composed of the continuous insulating layers. The capacitance is almost unchanged below about 20[V], but decreased slowly over 20[V]. The conduction mechanism of the specimens observed in the temperature range of 25~125[.deg. C], and is divided into three regions having different mechanism as the current increased: the region I below 200[V/cm] shows the ohmic conduction. The region II between 200[V/cm] and 2000[V/cm] can be explained by the Poole-Frenkel emission theory, and the region III above 2000[V/cm] is dominated by the tunneling effect.ct.

• Electrical & Electronic Materials
• /
• v.4 no.3
• /
• pp.201-210
• /
• 1991

본 논문에서는 (B $i_{1-x}$ P $b_{x}$)$_{2}$S $r_{2}$C $a_{2}$C $u_{3.6}$ $O_{y}$ (x=0~0.5)로 조성된 분말의 최적 하소온도를 결정하고 시편의 최적 소결온도를 규명하기 위하여 열분석을 하였다. 또 단일상의 고온 초전도체를 제작하기 위하여 열처리 온도, 시간 및 Pb 함량 변화에 따라 제작된 시편의 미세구조, 조성, 전기저항 및 전류밀도를 측정하여 상호 연관성을 종합적으로 분석, 검토하여 상변이에 관한 원인을 규명하고자 하였다. 또한 실용화 전 단계로서 임계특성 해석을 위하여 성형조건을 변화시켜 시편을 제작, 전류밀도값을 측정하였다.였다.다.

• Asian-Australasian Journal of Animal Sciences
• /
• v.29 no.5
• /
• pp.739-746
• /
• 2016

A total of 152 pig farms were randomly selected from the five provinces in South Korea. During the experiment, the average temperature and relative humidity was $24.7^{\circ}C$ and 74% in summer and $2.4^{\circ}C$ and 53% in winter, respectively. The correlation between floor space allowance (FSA) and productivity index was analyzed, including non-productive sow days (NPD), number of weaners (NOW), survival rate (SR), appearance rate of A-grade pork (ARA), and days at a slaughter weight of 110 kg (d-SW) at different growth stages. The objectives of the present study were i) to determine the effect of FSA on the pig productivity index and ii) to suggest the minimum FSA for pigs based on scientific baseline data. For the pregnant sow, NPD could be decreased if pregnant sows were raised with a medium level (M) of FSA (3.10 to $3.67m^2/head$) while also keeping the pig house clean which improves hygiene, and operating the ventilation system properly. For the farrowing sows, the NOW tended to decrease as the FSA increased. Similarly, a high level of FSA (H) is significantly negative with weaner SR of farrowing sows (p-value = 0.017), indicating this FSA tends to depress SR. Therefore, a FSA of 2.30 to $6.40m^2/head$ (very low) could be appropriate for weaners because a limited space can provide a sense of security and protection from external interruptions. The opposite trend was observed that an increase in floor space (> $1.12m^2/head$ leads to increase the SR of growing pigs. For the fattening pigs, H level of FSA was negatively correlated with SR, but M level of FSA was positively correlated with SR, indicating that SR tended to increase with the FSA of 1.10 to $1.27m^2/head$. In contrast, ARA of male fattening pigs showed opposite results. H level of FSA (1.27 to $1.47m^2/head$) was suggested to increase productivity because ARA was most affected by H level of space allowance with positive correlation ($R^2=0.523$). The relationship between the FSA and d-SW of fattening pigs was hard to identify because of the low $R^2$ value. However, the farms that provided a relatively large floor space (1.27 to $1.54m^2/head$) during the winter period showed d-SW was significantly and negatively affected by FSA.