• Korean Journal of Materials Research
• /
• v.16 no.7
• /
• pp.445-448
• /
• 2006

Highly c-axis oriented ZnO thin films were grown on Si(100)substrates with Zn buffer layers. Effects of the Zn buffer layer thickness on the structural and optical qualities of ZnO thin films were investigated using X-ray diffraction (XRD), photoluminescence (PL) and Atomic force microscopy (AFM) analysis techniques. It was confirmed that the quality of a ZnO thin film deposited by rf magnetron sputtering was substantially improved by using a Zn buffer layer. The highest ZnO film quality was obtained with a Zn buffer layer 110 nm thick. The surface roughness of the ZnO thin film increases as the Zn buffer layer thickness increases.

• Transactions on Electrical and Electronic Materials
• /
• v.1 no.1
• /
• pp.22-25
• /
• 2000

Polycrystalline SBTN layered ferroelectric thin film with various Nb mole ratios were prepared by sol-gel method Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperature and characterized in terms of phase and microstructure. The films were crystallized with a high (105) diffraction intensity and had rodike structure, SBTN films fired at 800$^{circ}C$ revealed standard hysteresis loops with no fatigue for up to 10$^{10}$ cycles. At an applied voltage of 5V the dielectric constant($varepsilon$) , dissipation factor (tan $delta$), remanent polarization(ZPr) and coercive field(Ec) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$) $O_{9+}$$alpha$/ thin film(x=0.1) prepared on Pt/ $SiO_2$/Si (100) were about 277.7, 0.042, 3.74$mu$C/$textrm{cm}^2$, and 24.8kv/cm respectively.ly.y. respectively.ly.y.y..

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.3
• /
• pp.102-105
• /
• 2011

This work describes the characteristics of zinc oxide (ZnO) thin films formed on a polycrystalline (poly) 3C-SiC buffer layer using a sol-gel process. The deposited ZnO films were characterized using X-ray diffraction, scanning electron microscopy, and photoluminescence (PL) spectra. ZnO thin films grown on the poly 3C-SiC buffer layer had a nanoparticle structure and porous film. The effects of post-annealing on ZnO film were also studied. The PL spectra at room temperature confirmed the crystal quality and optical properties of ZnO thin films formed on the 3C-SiC buffer layer were improved due to close lattice mismatch in the ZnO/3C-SiC interface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.45-49
• /
• 2001

We have investigated physical and electrical properties of the Hf $O_2$/HfS $i_{x}$/ $O_{y}$ thin film for alternative gate dielectrics in the metal-oxide-semiconductor device. The oxidation of Hf deposited directly on the Si substrate results in the H $f_{x}$/ $O_{y}$ interfacial layer and the high-k Hf $O_2$film simultaneously. Interestingly, the post-oxidation N2 annealing of the H102/H1Si70y thin films reduces(increases) the thickness of an amorphous HfS $i_{x}$/ $O_{y}$ layer(Hf $O_2$ layer). This phenomenon causes the increase of the effective dielectric constant, while maintaining the excellent interfacial properties. The hysteresis window in C-V curves and the midgap interface state density( $D_{itm}$) of Hf $O_2$/HfS $i_{x}$/ $O_{y}$ thin films less than 10 mV and ~3$\times$10$^{11}$ c $m^{-2}$ -eV without post-metallization annealing, respectively. The leakage current was also low (1$\times$10-s A/c $m^2$ at $V_{g}$ = +2 V). It is believed that these excellent results were obtained due to existence of the amorphous HfS $i_{x}$/ $O_{y}$ buffer layer. We also investigated the charge trapping characteristics using Fowler-Nordheim electron injection: We found that the degradation of Hf $O_2$/HfS $i_{x}$/ $O_{y}$ gate oxides is more severe when electrons were injected from the gate electrode.e electrode.e.e electrode.e.

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.650-656
• /
• 1995

High frequency SAW filters for cellular communications were fabricated by metallizing 36$^{\circ}$Y-X LiTaO$_3$piezoelectric substrate with IIDT type electrodes. It was found that the center frequency of the filter was lowered than as designed. In order to overcome such a drawback and enable a fine tuning of its center frequency, dielectric SiN$_{x}$ thin films were deposited on LiTaO$_3$substrate by PECVD as passivation layer and then frequency responses were also characterized. As a result, the center frequency of the filter could be shifted to a higher frequency with increasing the thickness of SiN$_{x}$ film, because SAW velocity increased with increasing the ratio of the thickness of dielectric thin film to wavelength. The insertion loss of the filter, however, became larger with increasing the thickness of SiN$_{x}$ film.

• Proceedings of the KIEE Conference
• /
• 1999.11a
• /
• pp.31-34
• /
• 1999

In the present study, we fabricated stoichiometric $(Ba_{1-x}Sr_x)TiO_3$ thin films at various substrate temperature and contents using of magnetron sputtering method on optimized Pt-based electrodes (Pt/TiN/$SiO_2$/Si). The substate temperature deposited at 200[ $^{\circ}C$], 400[$^{\circ}C$] and 600[$^{\circ}C$] and crystalline BST thin films show above 400[$^{\circ}C$]. Also, the composition of $(Ba_{1-x}Sr_x)TiO_3$ thin films deposited on Si wafer substrate at 400[$^{\circ}C$] were closed to stoichiometry($1.015{\sim}1.093$ in A/B ratio), but compositional deviation from a stoichiometry is larger as $SrCO_3$ is added. The drastic decrease of dielectric constant and increase of dielectric loss in $(Ba_{1-x}Sr_x)TiO_3$thin films is observed above 100[kHz]. V-I characteristics of $(Ba_{1-x}Sr_x)TiO_3$ thin films show the decrease of leakage current with the increase of $SrCO_3$ contents.

• Korean Journal of Materials Research
• /
• v.11 no.8
• /
• pp.671-678
• /
• 2001

All solid-state thin film micro supercapacitor, which consists of $RuO_2$/LiPON/$RuO_2$ multi layer structure, was fabricated on Pt/Ti/Si substrate using a $RuO_2$ electrode. Bottom $RuO_2$ electrode was grown by dc reactive sputtering system with increasing $O_2/[Ar+O_2]$ ratio at room temperature, and a LiPON electrolyte film was subsequently deposited on the bottom $RuO_2$ electrode at pure nitrogen ambient by rf reactive sputtering system. Room temperature charge-discharge measurements based on a symmetric $RuO_2$/LiPON/$RuO_2$ structure clearly demonstrates the cyclibility dependence on the microstructure of the $RuO_2$ electrode. Using both glancing angle x-ray diffraction (GXRD) and transmission electron microscopy (TEM) analysis, it was found that the microstructure of the $RuO_2$ electrode was dependent on the oxygen flow ratio. In addition, x- ray photoelectron spectroscopy(XPS) examination shows that the Ru-O binding energy is affected by increasing oxygen flow ratio. Furthermore, TEM and AES depth profile analysis after cycling demonstrates that the interface layer formed by interfacial reaction between LiPON and $RuO_2$ act as a main factor in the degradation of the cyclibility of the thin film micro-supercapacitor.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.5
• /
• pp.361-364
• /
• 2003

It was investigated that the structural and electrical Properties of Ce-doped Ba(Zr$_{x}$Ti$_{1-x}$ )O$_3$ (BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/SiO$_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/O$_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 nm (RMS at 500 $^{\circ}C$, Ar:6 sccm, $O_2$:6 sccm). It was found that annealing procedure after top electrode deposit can reduce the dissipation factor.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.1-8
• /
• 2012

The development of martensitic grades which can be processed in continuous galvanizing lines requires the reduction of the oxides formed on the steel during the hot dip process. This reduction mechanism was investigated in detail by means of High Resolution Transmission Electron Microscopy (HR-TEM) of cross-sectional samples. Annealing of a martensitic steel in a 10% $H_2+N_2$ atmosphere with the dew point of $-35^{\circ}C$ resulted in the formation of a thin $_{C-X}MnO.SiO_{2}$ (x>1) oxide film and amorphous $_{a-X}MnO.SiO_{2}$ oxide particles on the surface. During the hot dip galvanizing in Zn-0.13%Al, the thin $_{C-X}MnO.SiO_{2}$ (x>1) oxide film was reduced by the Al. The $_{a-X}MnO.SiO_{2}$ (x<0.9) and $a-SiO_{2}$ oxides however remained embedded in the Zn coating close to the steel/coating interface. No $Fe_{2}Al_{5-X}Zn_{X}$ inhibition layer formation was observed. During hot dip galvanizing in Zn-0.20%Al, the $_{C-X}MnO.SiO_{2}$ (x>1) oxide film was also reduced and the amorphous $_{a-X}MnO.SiO_{2}$ and $a-SiO_{2}$ particles were embedded in the $Fe_{2}Al_{5-X}Zn_{X}$ inhibition layer formed at the steel/coating interface during hot dipping. The results clearly show that Al in the liquid Zn bath can reduce the crystalline $_{C-X}MnO.SiO_{2}$ (x>1) oxides but not the amorphous $_{a-X}MnO.SiO_{2}$ (x<0.9) and $a-SiO_{2}$ oxides. These oxides remain embedded in the Zn layer or in the inhibition layer, making it possible to apply a Zn or Zn-alloy coating on martensitic steel by hot dipping. The hot dipping process was also found to deteriorate the mechanical properties, independently of the Zn bath composition.

• Journal of the Korean Magnetics Society
• /
• v.16 no.6
• /
• pp.283-286
• /
• 2006

We have studied the role of ${\alpha}-Al_{2}O_{3}$ buffer layer as a diffusion barrier in the Ba-ferrite/$SiO_{2}$ magnetic thin films for high-density recording media. In the interface of amorphous Ba-ferrite $(1900-{\AA}-thick)/SiO_{2}$ thin film during annealing, the interfacial diffusion started to occur at ${\sim}700^{\circ}C$. As the annealing temperature increased up to $800^{\circ}C$, the interfacial diffusion abruptly proceeded resulting in the high interface roughness and the deterioration of the magnetic properties. In order to control the interfacial diffusion at the high temperature, we introduced ${\alpha}-Al_{2}O_{3}$ buffer layer ($110-{\AA}-thick$) in the interface of Ba-ferrite/$SiO_{2}$ thin film. During the annealing of Ba-ferrite/${\alpha}-Al_{2}O_{3}/SiO_{2}$ thin film even at ${\sim}800^{\circ}C$, the interface was very smooth. The magnetic properties, such as saturation magnetization and intrinsic coercivity, were also enhanced, due to the inhibition of interfacial diffusion by the ${\alpha}-Al_{2}O_{3}$ buffer layer. Our study suggests that the ${\alpha}-Al_{2}O_{3}$ buffer layer act as a useful interfacial diffusion barrier in the Ba-ferrite/$SiO_{2}$ magnetic thin films.