• Bulletin of the Korean Chemical Society
• /
• v.31 no.11
• /
• pp.3233-3237
• /
• 2010

A $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_2$ cathode was modified by coating with Li-La-Ti-O, and the effect of the coating thickness on their electrochemical properties was studied. The thickness of the coating on the surface of $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_2$ was increased by increasing the wt % of the coating material. The rate capability of the Li-La-Ti-O-coated electrode was superior to that of the pristine sample. 1- and 2-wt %-coated samples showed considerable improvement in capacity retention at high C rates. However, the rate capability of a 5-wt %-coated sample decreased. All the coated samples showed a high discharge capacity and slightly improved cyclic performance under a high cut-off voltage (4.8 V) condition. Results of a storage test confirmed that the Li-La-Ti-O coating layer was effective in suppressing the dissolution of the transition metals as it offered protection from the attack of the acidic electrolyte. In particular, the 2- and 5-wt %-coated samples showed a better protection effect than the 1-wt %-coated sample.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05c
• /
• pp.75-78
• /
• 2002

The dielectric properties for Ni electrode multilayer ceramic chip capacitor for Y5V has been studied with $(Ba_{0.93}Ca_{0.07})_m(Ti_{0.82}Zr_{0.18})O_2+MnO_2$ 0.2wt%, $Y_2O_3$ 0.18wt%, $SiO_2$ 0.15wt%, glass frit 1 wt% composition. The m ratio in the range of 1.006 ~ 1.012 have dielectric constant 9,500 ~ 14,500 and insulation resistance 390 ~ 460 $G{\Omega}$. Using the dielectrics, nikel electrode multilayer chip capacitor with Y5V, 104Z in EIA 0603 size specific capacitance were developed.

• Proceedings of the KIEE Conference
• /
• 1987.11a
• /
• pp.234-238
• /
• 1987

In this paper, the used specimen composition was added basic additives ($Bi_2O_3\;lmol%$, $Sb_2O_3\;lmol%$, CoO 0.5 mol%, MnO 0.5mol%) to ZnO powder, and $TiO_2$ (1,2,3,4 mol%) to the above basic composition. It appears that there are four regions of conduction current depended upon the strength of the applied electric field ; Ohimic region, Poole-Frenkel region, Schottky region and Tunneling region. Increasing of $TiO_2mol%$, the breakdown voltages of ZnO ceramic varistors are decreased. The decrease of breakdown voltages was explained with the decrease of potential barrier height. Moreover, V-I characteristics with temperature dependence are decreased with increasing of $TiO_2mol%$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.1
• /
• pp.1-5
• /
• 2006

The effect of A/B moi ratios and sintering temperatures on dielectric properties and microstructure of $(Ba_{0.93}Ca_{0.07})_m(Ti_{0.82}Zr_{0.18})O_3$ ceramics were investigated. The dielectric constant decreased with increasing the A/B mol ratio. However, the dielectric loss is improved. As the dielectric properties of A/B mol ratio with m = 1.009 at sintered temperature $1260^{\circ}C$, we obtained dielectric constant 12,800, dielectric loss $3.5\%$ and Y5V temperature characteristics. Highly reliable Ni-MLCCs, 1.6mm$(length){\time}0.8mm(width){\time}0.8mm$(height) with capacitance of 1.23 ${\mu}F$ and 야ssipation loss of $5.2\%$ were obtained employing dielectric material composed of $(Ba_{0.93}Ca_{0.07})_{1.009}(Ti_{0.82}Zr_{0.18})O_3$ - $MnO_2\;0.2wt\%-Y_2O_3\;0.18wt\%,\;-\;SO_2\;0.15wt\%-(Ba_{0.4}Ca_{0.6})SiO_3\;1wt\%$.

• Journal of the Korean earth science society
• /
• v.27 no.1
• /
• pp.49-60
• /
• 2006

The purpose of this study is to investigate geochemical characteristics for stream sediments in the Naju area. We collected 139 stream sediments samples from primary channels. Samples were dried slowly in the laboratory and chemical analysis was carried out using XRF. ICP-AES and NAA. In order to investigate geochemical characteristics, the geological groups categorized into granitic gneiss area, schist area, granite area, arenaceous rock area, tuff area, andesite area, and rhyolite area. Average contents of major elements for geological groups are $SiO_2\;58.37{\sim}66.06wt.%,\;Al_2O_3\;13.98{\sim}18.41wt.%,\;Fe_2O_3\;4.09{\sim}6.10wt.%,\;CaO\;0.54{\sim}1.33wt.%,\;MgO\;0.86{\sim}1.34wt.%,\;K_2O\;2.38{\sim}4.01wt.%,\;Na_2O\;0.90{\sim}1.32wt.%,\;TiO_2\;0.82{\sim}1.03wt.%,\;MnO\;0.09{\sim}0.15wt.%,\;P_2O_5\;0.11{\sim}0.18wt.%$. According to the comparison of average contents of major elements, $Al_2O_3\;and\;K_2O$ are higher in granitic gneiss area, $Fe_2O_3,\;CaO,\;P_2O_5$ are higher in tuff area, MgO and $TiO_2$ are higher in andesite area, $Na_2O_$ is higher in rhyolite area, $SiO_2$, and MnO are higher in arenaceous rock area. Average contents of minor and rare earth elements for geological groups are $Ba\;1278{\sim}1469ppm,\;Be\;1.1{\sim}1.5ppm,\;Cu\;18{\sim}25ppm,\;Nb\;25{\sim}37ppm,\;Ni\;16{\sim}25ppm,\;Pb\;21{\sim}28ppm,\;Sr\;83{\sim}155ppm,\;V\;64{\sim}98ppm,\;Zr\;83{\sim}146ppm,\;Li\;32{\sim}45ppm,\;Co\;7.2{\sim}12.7ppm,\;Cr\;37{\sim}76ppm,\;Cs\;4.8{\sim}9.1ppm,\;Hf\;7.5{\sim}25ppm,\;Rb\;88{\sim}178ppm,\;Sc\;7.7{\sim}12.6ppm,\;Zn\;83{\sim}143ppm,\;Pa\;11.3{\sim}37ppm,\;Ce\;69{\sim}206ppm,\;Eu\;1.1{\sim}1.5ppm,\;Yb\;1.8{\sim}4.4ppm$. According to the comparison of average contents of minor and rare earth elements for geological groups, Pb, Li, Cs, Hf, Rb, Sb, Pa, Ce, Eu, and Yb are higher in granitic gneiss area; Ba, Co, and Cr in schist area; Nb, Ni, and Zr in arenaceous rock area; Sr in tuff area: and Be, Cu, V, Sc, and Zn are such in andesite area.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.2 no.2
• /
• pp.170-176
• /
• 1998

The team mixed PbO, $ZrO_2$, $TiO_2$, $Nb_2O_5$ and $MnCO_3$, to make $Pb[(Zr_{0.54}\;Ti_{0.46})\;Nb_{0.005}]O_3+4%MnCO_3$. The electroded PZT ceramics were poled by 3 kV/mm at $110^{\circ}C$ for 600 s. We assembled the 0.4mm thick PZT slices into ultrasonic transducers. Central frequency of the probe is 5 MHz, which is proper to the thickness gauge for steel pipes and for flaw detector. The probe can detect a disk shape defect of 1mm diameter at 15cm deep in steel block. The new probe's Fresnel zone that the ultrasonic beam do not broaden is 13mm. Over the Fresnel zone, the ultrasonic beam spreads. Half of the beam spread angle of the probe is $4.3^{\circ}-4.6^{\circ}$. This probe can be used for the ultrasonic transducers for non-destructive testing of steel bridges.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.589-598
• /
• 1997

The effects of PT/PZ ratio variations in a modified PZT system on crystal structure and electrical properties were studied. $0.05Pb(Sn_{0.5}Sb_{0.5})O_3＋xPbTiO_3＋yPbZrO_3$＋0.4Wt% $MnO_2$(＝0.55PSS＋0.11PT＋0.84PZ＋0.4wt%$MnO_2$ ; x＋y=0.95) systems with variations of PT/PZ from 0.50/0.45 to 0.l1/0.84 were sintered at $1250^{\circ}C$ for 2 hr, and then sintering density, crystal structure, dielctric, piezoelectric, pyroelectic and voltage responsity to infrared were investigated. Sintering density was increased from 7.52g/$\textrm {cm}^3$ to 7.82g/$\textrm {cm}^3$ with increasing PZ content. Dielectric constants at 1 KHz were decreased from 1147 to 193 with variation of PT/PZ from 0.50/0.45 to 0.l1/0.84 after poling of $4 KV_{DC}$/mm at $140^{\circ}C$ for 20 minutes. All Dielectric losses at 1 KHz were less than 1 % in all specimens. $K_{p}$ was increased near to 1 of PT/PZ, and maximun value of 48.2 % was .at 0.45/0.50. Pyroelectric coefficient of PT/PZ with 0.l1/0.84 was maximun value, 0.0541 C/$\m^2$K, and voltage responsity to infrared was 1.5 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.3
• /
• pp.228-232
• /
• 2006

In this paper, in order to develop low temperature sintering $PbTiO_3$-system piezoelectric ceramics for thickness-vibration-mode piezoelectric transformer, $Pb_{0.76}Ca_{0.24}[(Mn_{1/3}Sb_{2/3})_{0.04}Ti_{0.96}]O_3$ ceramics using $0.25\;wt\%\;CaCO_3$ and $0.2\;wt\%\;Li_{2}CO_3$ as sintering aids were manufactured according to the variation of poling field. The specimens could be sintered at $930\;^{\circ}C$. The piezoelectric properties were investigated according to the poling field. The maximum properties showed at the field of 6.5 kV/mm, which had kt of 0.49, Qmt of 1816, and $d_{33}$ of 81.4 pC/N.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.176-177
• /
• 2005

In this paper, in order to develop low temperature sintering $PbTiO_3$-system piezoelectric ceramics for thickness-vibration-mode piezoelectric transformer, $Pb_{0.76}Ca_{0.24}[(Mn_{1/3}Sb_{2/3})_{0.04}Ti_{0.96}]O_3$ ceramics using $0.25wt%CaCO_3$ and 0.2wt%$Li_2CO_3$ as sintering aids were manufactured according to the variation of poling field. Specimens could be sintered at the sintering temperature of $930^{\circ}C$. The piezoelectric properties increased according to the increase of poling field and showed the maximum values (kt=0.49, Qmt=1816, and $d_{33}$=81.4pC/N) under 6.5kV/mm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.746-748
• /
• 2002

The effect of $MnO_2$ addition in $0.05Pb(Sn_{0.5}Sb_{0.5})O_3-0.8PbZrO_3-0.15PbTiO_3$(0.05PSS-0.8PZ-0.15PT) ceramics on crystal structure and electrical properties were studied. The sintering temperature and time were $1230^{\circ}C{\sim}1270^{\circ}C$ and 2hr, respectively. Then crystal structure, dielectric and pyroelectric properties were investigated. All the poled specimens showed the lower dielectric constant and $tan{\delta}$ than the unpoled specimens. Dielectric constant at 1kHz of the 0.05PSS-0.8PZ-0.15PT(MnO2 0.3wt%) system specimen sintered at $1250^{\circ}C$ for 2hr were 270 and showed the lowest $tan{\delta}$ of 0.2% after poling of $2kV_{DC}/mm$ at $150^{\circ}C$ for 30 minutes. Pyroelectric coefficient was maximum value of $50nC/cm^2K$ and Curie temperature was $224^{\circ}C$.