• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.506-508
• /
• 2000

Oxide of the form $Mn_{3}O_{4}-NiO-Fe_{2}O_{3}$ present properties that make them useful as multilayer chip NTC thermistor for mobile phone NTC thermistor electric properties of $Mn_{3}O_{4}-NiO-Fe_{2}O_{3}$ system has been measured as a function of temperature and composition. In $Mn_{3}O_{4}-NiO-Fe_{2}O_{3}$ composition, it can be seen that resistivity and B-constant were increased as the ratio of $Mn_{3}O_{4}/F_{2}O_{3}$ and $Mn_{3}O_{4}$/NiO was increased. In particular, resistance change ratio (${\Delta}R$), the important factor for reliability varied within ${\pm}1%$, indicating the compositions of these products could be available for mobile phone.

• Resources Recycling
• /
• v.9 no.4
• /
• pp.44-49
• /
• 2000

Among dusts which were generated in AOD process producing a medium-low carbon ferromanganese, the dust collected in bag filter contained manganese about 63% and its phase was $Mn_3$$O_4$. the maximum extraction of Mn by nitric acid is about 67% because of remaining amorphous $MnO_2$. Therefore this research investigated reducibility of the activated charcoal in Mn extraction from the dust. Addition of charcoal over 10% of pulp density made possible Mn extraction of 90% at $70^{\circ}C$, 0.5N $HNO_3$. To convert $Mn_3$$O_4$ to MnO by reducing roasting, the minimum mixture ratio of activated charcoal was 5% in $750^{\circ}C$, 1 hour. Extraction of Mn from the reduced dust was over 99% with nitric acid at $25^{\circ}C$, 6N $HNO_3$, pulp density 150 g/l§.

• Journal of the Korean Ceramic Society
• /
• v.39 no.9
• /
• pp.829-834
• /
• 2002

Ferroelectric properties of $ErMnO_3$ thin films deposited on Si(100) substrate using Sol-gel process with metal salts were investigated. $ErMnO_3$ thin films with a (001) preferred orientation were crystallized at 800$^{\circ}C$. The $ErMnO_3$ thin film post-annealed at 800$^{\circ}C$ for 1 h showed the dielectric constant(k) of 26 and the dielectric loss(tan ${\delta}$) of 0.032 at the frequency range from 1 to 100 KHz. The grain size of $ErMnO_3$ thin film post-annealed at 800 for 1 h was 10∼30 nm. The remanent polarization($P_r$) of the $ErMnO_3$ thin films increased with increasing (001) preferred orientation. The $ErMnO_3$ thin films post-annealed at 800$^{\circ}C$ for 1 h showed the remanent polarization($P_r$) of 400 nC/$cm^2$, with the increase of post-annealing time at 800$^{\circ}C$, the coercive field($E_c$) of thin films was lowered because the dense and homogeneous thin films were obtained.

• Transactions of Materials Processing
• /
• v.31 no.6
• /
• pp.365-375
• /
• 2022

The microstructure and high-temperature plastic deformation behavior of the modified Al-0.7Mn alloy were investigated and compared with the conventional Al-0.3Mn (Al3102) alloy. α-Al (matrix) and Al₆(Mn, Fe) phases were identified in both alloys. As a result of microstructure observation, both alloys showed equiaxed grains, and Al-0.7Mn alloy showed larger grain size and higher Al₆(Mn, Fe) fraction than Al-0.3Mn alloy. High temperature compressive tests, the deformation temperatures of 410℃, 450℃, 490℃, 530℃ and strain rats of 10^-2/s, 10^-1/s, 1/s, 10/s, were conducted using Gleeble equipment. The flow stress values of Al-0.7Mn alloy were higher than that of Al-0.3Mn alloy at all strain rates and temperature conditions. Constitutive equations were presented using the flow stresses obtained from experimental results and the Zener-Hollomon parameter. In the true stress-true strain curves of the two alloys, the experimental and predicted values were in good agreement with each other. Based on the dynamic material model, eutectic deformation maps of Al-0.7Mn and Al-0.3Mn alloys were suggested, and the plastic instability region was presented. The modified Al-0.7Mn alloy showed a wider plastic instability region than that Al-0.3Mn alloy. Based on the process deformation maps, the MPE tube parts could be manufactured through the actual extrusion process using the suggested conditions.

• Journal of Ceramic Processing Research
• /
• v.19 no.5
• /
• pp.372-377
• /
• 2018

MgO or gadolinium-doped ceria (GDC, $Ce_{0.9}Gd_{0.1}O_{2-{\delta}}$) was added as a promoter to improve the oxygen transfer kinetics of $MgMnO_3$ oxygen carrier material for chemical looping combustion. Neither MgO nor GDC reacted with $MgMnO_3$, even at the high temperature of $1100^{\circ}C$. The average oxygen transfer capacities of $MgMnO_3$, 5 wt% $MgO-MgMnO_3$, and 5 wt% $GDC-MgMnO_3$ were 8.74, 8.35, and 8.13 wt%, respectively. Although the addition of MgO or GDC decreased the oxygen transfer capacity, no further degradation was observed during their use in 5 redox cycles. The addition of GDC significantly improved the conversion rate for the reduction reaction of $MgMnO_3$ compared to the use of MgO due to an increase in the surface adsorption process of $CH_4$ via oxygen vacancies formed on the surface of GDC. On the other hand, the conversion rates for the oxidation reaction followed the order 5 wt% $GDC-MgMnO_3$ > 5 wt% $MgO-MgMnO_3$ >> $MgMnO_3$ due to morphological change. MgO or GDC particles suppressed the grain growth of the reduced $MgMnO_3$ (i.e., (Mg,Mn)O) and increased the specific surface area, thereby increasing the number of active reaction sites.

• Journal of the Korean Magnetics Society
• /
• v.19 no.3
• /
• pp.85-88
• /
• 2009

Magnetic phases of polycrystalline $Ge_{1-x}Mn_x$ thin films were studied. The $Ge_{1-x}Mn_x$ thin films were grown at $400^{\circ}C$ by using a molecular beam epitaxy. The $Ge_{1-x}Mn_x$thin films were p-type and electrical resistivities were $4.0{\times}10^{-2}{\sim}1.5{\times}10^{-4}ohm-cm$. Based on the analysis of magnetic characteristics and microstructures, it was concluded that the ferromagnetic phase formed on the $Ge_{1-x}Mn_x/SiO_2$/Si(100) thin films was $Ge_3Mn_5$ phase which has about 310 K of Curie temperature. Moreover, the $Ge_{1-x}Mn_x$ thin film which had $Ge_3Mn_5$ phase showed the negative magnetoresistance to be about 9% at 20 K when the magnetic field of 9 T was applied.

• Resources Recycling
• /
• v.21 no.2
• /
• pp.34-40
• /
• 2012

$Pt_{10}$/C, $Pt_9Mn_1$/C, $Pt_7Mn_3$/C electrocatalysts for Polymer Electrolyte Membrane Fuel Cells(PEMFCs) were synthesized by reduction with HCHO and their activity as a oxygen reduction reaction(ORR) was examined at half cell. The electrochemical oxygen reduction reaction(ORR) was studied by using a glaasy carbon electrode through cyclic voltammetric curves(CV) in a 1 M $H_2SO_4$ solution. The ORR activities of $Pt_9Mn_1$/C were higher than $Pt_{10}$/C, $Pt_7Mn_3$/C. Also potential-current curves of $Pt_9Mn_1$/C at 0.9, 0.8, 0.7, 0.6V for 5minutes respectively were higher than $Pt_{10}$/C, $Pt_7Mn_3$/C. Physical characterization was made by using x-ray diffraction(XRD) and transmission electron microscope(TEM). The TEM images of $Pt_9Mn_1$/C, $Pt_{10}$/C catalysts showed homogenous particle distribution with particle size of about 2.7 nm, 3 nm respectively and then the XRD results showed that the crystalline structure of the synthesized catalysts are seen FCC structure.

• Applied Chemistry for Engineering
• /
• v.22 no.3
• /
• pp.308-311
• /
• 2011

The reaction mechanism of selective catalytic reduction of NOx over sewage sludge char impregnated with MnOx using $NH_3$ as the reducing agent was investigated. The active Mn phase was shown to be $Mn_3O_4$ from the XRD analysis. Adsorption was the dominant NOx removal mechanism at low temperatures below $150^{\circ}C$ although reduction reaction also contributed partly to the NOx removal at $100{\sim}150^{\circ}C$. The reaction rate constants of NOx removal over non-impregnated and MnOx-impregnated active chars were compared based on experimental results. The MnOx-impregnated char was shown to have a higher reaction rate constant and a higher NOx removal efficiency due to a higher collision coefficient and a lower activation energy. The activation energy for both chars was shown to be relatively low (10~12 kJ/mol) under the experimental conditions of this study.

• Journal of the Korean Ceramic Society
• /
• v.27 no.1
• /
• pp.7-12
• /
• 1990

The influence of MnO2 on the sintering property and PTCR behavior of(Ba0.8Sr0.2)TiO2 has been investigated. And the densities, grain sizes and electrical resitivities of specimens were measured as a function of doping with Mn ion of varying concentration. The density and grain size of the sintered specimens were almost the same regardless of MnO2 addition up to 0.2mol% MnO2. But in the case of 0.25mol% MnO2 addition, abnormal grain growth was appeared. So the grain size distribution was wide and density decreased greatly. The room-temperature resistivity increased as Mn content increased and the temperature coefficient of resistivity was highest in the case of 0.15mol% MnO2 addition.

• Development and Reproduction
• /
• v.16 no.4
• /
• pp.295-300
• /
• 2012

Manganese ($Mn^{2+}$) is a trace element that is essential for normal physiology, and is predominantly obtained from food. Several lines of evidence, however, demonstrated that overexposure to $MnCl_2$ exerts serious neurotoxicity, immunotoxicity and developmental toxicity, particularly in male. The present study aimed to evaluate the effect of 0, 1.0, 3.3, and 10 mg/kg/day doses of $MnCl_2$ on the reproductive organs in the immature female rats. Rats (PND 22; S.D. strain) were exposed to $MnCl_2$ ($MnCl_2{\cdot}4H_2O$) dissolved in drinking water for 2 weeks. The animals were sacrificed on PND 35, then the tissues were immediately removed and weighed. Histological studies were performed using the uteri tissue samples. Serum LH and FSH levels were measured with the specific ELISA kits. Body weights of the experimental group animals were not significantly different from those of control group animals. However, ovarian tissue weights in 1 mg and 3.3 mg $MnCl_2$ dose groups were significantly lower than those of control animals (p<0.05 and p<0.01, respectively). Uterine tissue weights of 3.3 mg dose $MnCl_2$ groups were significantly lower than those of control animals (p<0.01), while the 1 mg $MnCl_2$ dose and 10 mg $MnCl_2$ dose failed to induce any change in uterine weight. Similarly, only 3.3 mg $MnCl_2$ dose could induce the significant decrease in the oviduct weight compared to the control group (p<0.05). Non-reproductive tissues such as adrenal and kidney failed to respond to all doses of $MnCl_2$ exposure. The uterine histology revealed that the $MnCl_2$ exposure could affect the myometrial cell proliferation particularly in 3.3 mg dose and 10mg dose group. Serum FSH levels were significantly decreased in 1mg $MnCl_2$ dose and 10 $MnCl_2$ mg groups (p<0.05 and p<0.01, respectively). In contrast, treatment with 1 mg $MnCl_2$ dose induced a significant increment of serum LH level (p<0.05). The present study demonstrated that $MnCl_2$ exposure is capable of inducing abnormal development of reproductive tissues, at least to some extent, and altered gonadotropin secretions in immature female rats. Combined with the well-defined actions of this metal on GnRH and prolactin secretion, one can suggest the $Mn^{2+}$ might be a potential environmental mediator which is involved in the female pubertal process.