• Analytical Science and Technology
• /
• v.6 no.3
• /
• pp.275-282
• /
• 1993

A direct and simultaneous method to determine the $SiO_2$ and $ZrO_2$ in zircon sand of raw mineral and its treated one were studied by optical emission spectrometer using DC arc source. The synthetic standard was prepared by mixing with pure metal oxide, and it was diluted with buffer(graphite) and flux($Li_2B_4O_7$). The mixing ratio of buffer and flux and its dilution ratio to sample was investigated in order to choose the best excitation conditions. The optimum mixing and dilution ratios were 0.22:1 and 40, and the standard deviations of analytical results were 1.9% for $SiO_2$ and 4.7% for $ZrO_2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.3
• /
• pp.227-231
• /
• 2008

In this study, in order to improve the electrical properties of low temperature sintering piezoelectric ceramics, $[0.05Pb(Zn_{1/2}W_{1/2})-0.07Pb(Mn_{1/3}Nb_{2/3})-0.088Pb(Zr_{0.48}Ti_{0.52})]O_3$(abbreviated as PZW-PMN-PZT) ceramic systems were fabricated using $Bi_2O_3$, CuO and $Li_2CO_3$ as sintering aids and then their piezoelectric and dielectric properties were investigated according to the amount of $Li_2CO_3$ and post-annealing process. Post-annealing process enhanced all physical properties except for mechanical quality factor (Qm). 0.2 wt% $Li_2CO_3$ added and post-annealed specimen showed the excellent values suitable for low loss piezoelectric actuator application as follow: the density = 7.86 $g/cm^3$ electromechanical coupling factor (kp) = 0.575, piezoelectric constant $d_{33}$ = 370 pC/N, dielectric constant ($\varepsilon_r$) = 1546, and mechanical quality factor (Qm) = 1161, respectively.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.5
• /
• pp.995-999
• /
• 2007

The lead zirconate titanate (PZT) powders were synthesized to make the piezoelectric ceramics in low temperature as low as $900^{\circ}C$. To investigate the influence of additives on sintering of PZT, two kinds of sintering aids were made as follows; $wB_2O_3-xBi_2O_3-zCuO$and LiBiO2-CuO. The sintering aid, $1{\sim}3$ wt.% $LiBiO_2-CuO$, was added into these PZT powders and the specimens were fired at temperature in the range of $800{\sim}1200^{\circ}C$. The highest density was shown in the specimen with 1 wt.% $LiBiO_2-CuO$ as additive at temperature of $900^{\circ}C$. The sintered specimen were analyzed by X-ray diffraction(XRD) and scanning electron microscopy (SEM) was utilized to observe the microstructure, especially the densified morphology of specimens. In the XRD pattern, the well-crystallized PZT phase could be obtained in consequence of firing at $900^{\circ}C$. The scanning electron microscopy(SEM) was utilized to observe the structure of specimens after firing at $900^{\circ}C$. The densified perovskite structure of $PbZrTiO_3$ could be obtained by sintering at temperature as low as $900^{\circ}C$. The high sinterability of PZT ceramics was attributed to the low formation temperature of the liquid phase of additives.

• Korean Journal of Materials Research
• /
• v.29 no.3
• /
• pp.150-154
• /
• 2019

This study investigates the effect of MnO2 and CuO as acceptor additives on the microstructure and piezoelectric properties of $0.96(K_{0.5}Na_{0.5})_{0.95}Li_{0.05}Nb_{0.93}Sb_{0.07}O_3-0.04BaZrO_3$, which has a rhombohedral-tetragonal phase boundary composition. $MnO_2$ and CuO-added $0.96(K_{0.5}Na_{0.5})_{0.95}Li_{0.05}Nb_{0.93}Sb_{0.07}O_3-0.04BaZrO_3$ ceramics sintered at a relatively low temperature of $1020^{\circ}C$ show a pure perovskite phase with no secondary phase. As the addition of $MnO_2$ and CuO increases, the sintered density and grain size of the resulting ceramics increases. Due to the difference in the amount of oxygen vacancies produced by B-site substitution, Cu ion doping is more effective for uniform grain growth than Mn ion doping. The formation of oxygen vacancies due to B-site substitution of Cu or Mn ions results in a hardening effect via ferroelectric domain pinning, leading to a reduction in the piezoelectric charge coefficient and improvement of the mechanical quality factor. For the same amount of additive, the addition of CuO is more advantageous for obtaining a high mechanical quality factor than the addition of $MnO_2$.

• Korean Journal of Materials Research
• /
• v.31 no.11
• /
• pp.614-618
• /
• 2021

As the size of market for electric vehicles and energy storage systems grows, the demand for lithium-ion batteries (LIBs) is increasing. Currently, commercial LIBs are fabricated with liquid electrolytes, which have some safety issues such as low chemical stability, which can cause ignition of fire. As a substitute for liquid electrolytes, solid electrolytes are now being extensively studied. However, solid electrolytes have disadvantages of low ionic conductivity and high resistance at interface between electrode and electrolyte. In this study, Li₇La₃Zr₂O₁₂ (LLZO), one of the best ion conducting materials among oxide based solid electrolytes, is fabricated through RF-sputtering and various electrochemical properties are analyzed. Moreover, the electrochemical properties of LLZO are found to significantly improve with co-sputtered Li₂O. An all-solid thin film battery is fabricated by introducing a thin film solid electrolyte and an Li₄Ti₅O₁₂ (LTO) cathode; resulting electrochemical properties are also analyzed. The LLZO/Li₂O (60W) sample shows a very good performance in ionic conductivity of 7.3×10^-8 S/cm, with improvement in c-rate and stable cycle performance.

• Journal of the Korean Physical Society
• /
• v.73 no.10
• /
• pp.1535-1540
• /
• 2018

In this study, we prepared and characterized Nb-doped $Li_7La_3Zr_{2-x}O_{12}$ (LLZNO) powder and pellets with a cubic garnet structure by using a modified sol-gel synthesis and hot pressing. LLZNO powder with a very small grain size and cubic structure without secondary phases could be obtained by using a synthesis method in which Li and La sources in a propanol solvent were mixed together with Zr and Nb sources in 2-methoxy ethanol. A pure cubic phase LLZNO pellet could be fabricated from the prepared LLZNO and an additional 6-wt% of $Li_2CO_3$ powder by hot pressing at $1050^{\circ}C$ and 15.8 MPa. The hot-pressed LLZNO pellet with a relative density of 99% exhibited a very dense surface morphology. The total Li ionic conductivity of the hot-pressed LLZNO was $7.4{\times}10^{-4}S/cm$ at room temperature, which is very high level compared to other reported values. The activation energy for ionic conduction was estimated to be 0.40 eV.

• Journal of Powder Materials
• /
• v.8 no.3
• /
• pp.163-167
• /
• 2001

A bulk porous $CaZrO_3/MgO$ composite with plantinum nano-dispersion was synthesized in air atmosphere through the combination of several in situ reactions, including the pyrolysis of $PtO_2$. A mixture of $CaMg(CO_3)_2$(dolomite), $ZrO_2$, $PtO_2$ and LiF (0.5 wt%, as an additive) was cold isostatically pressed at 200 MPa and sintered at $1100^{\circ}C$ for 2 h. The porous $CaZrO_3/MgO/Pt$ composite ($CaZrO_3/MgO$ : Pt=99 : 1 in volume) had a uniformly open-porous structure (porosity: 56%) with three-dimensional (3-D) network and a narrow pore-size distribution, similarly to the porous $CaZrO_3/MgO$ composites reported before. Catalytic Properties (viz., NO direct decomposition and NO reduction by $C_2H_4$) of the $CaZrO_3/MgO/Pt$ composite were investigated up to $900^{\circ}C$. In the absence of oxygen, the NO conversion rate reached ~52% for the direct decomposition and ~100% for the reduction by $C_2H_4$, respectively. The results suggest the possibility of the porous composite as a multifunctional filter, i.e., simultaneous hot gas-filtering and $de-NO_x$ in one component.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.3
• /
• pp.130-134
• /
• 2015

This research proposes the use of a composition modulated (ZrO₂)_x(Al₂O₃)_1-x film as a charge trapping layer for charge trap flash memory; this is possible when the Zr (Al) atomic percent is controlled to form a variable bandgap as identified by the valence band offsets and electron energy loss spectrum measurements. Compared to memory devices with uniform compositional (ZrO₂)_0.1(Al₂O₃)_0.9 or a (ZrO₂)_0.92(Al₂O₃)_0.08 trapping layer, the memory device using the composition modulated (ZrO₂)_x(Al₂O₃)_1-x as the charge trapping layer exhibits a larger memory window (6.0 V) at the gate sweeping voltage of ±8 V, improved data retention, and significantly faster program/erase speed. Improvements of the memory characteristics are attributed to the special energy band alignments resulting from non-uniform distribution of elemental composition. These results indicate that the composition modulated (ZrO₂)_x(Al₂O₃)_1-x film is a promising candidate for future nonvolatile memory device applications.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.3 no.2
• /
• pp.176-184
• /
• 1993

The glasses, which the $\beta$-spodumene as the principal crystalline phase could be precipitated, were melted by adding >, $P_2O_5, TiO_2, ZrO_2 in the Li_2O-Al_2O_3-SiO_2$ system. In order to achieve the glass-ceramic body of near-theoritical density by sintering method, the optimum condition of heat treatment, the effect of glass powder size and the properties were investigated by DTA, XRD, bulk density, thermal expansion and SEM. Addition of $P_20_5$ imProved the tendency of sintering and the sample with 9wt% $P_20_5$ content was the most dense OOdy by sintering method. The optimum condition of heat treatmemt was sintered for densitification at $740^{\circ}C$ and crystallized at $950^{\circ}C$. In the optimum condition, the relative density was above 90% and the thermal expansion was negative about $-1{\times}10^{-7}/^{\circ}C$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.2 no.2
• /
• pp.20-32
• /
• 1992

$Na_2O-CaO-MgO-Al_2O_3-SiO_2$ glass was taken as a basic glass and then $Li_2O$ O.5wt%, $K_2O$ 2.0wt% were substituted to $Na_2O$content, MgO 12.0wt %, ZnO 6.0wt % to CaO content. And also nucleation agent $ZrO_2 and $CaF_2$ were added to 1-2wt% respectively. The crystal according to the compositions appeared wollastonite, diopside and diopside.tremolite. The glasses substituted NazO by LizO was decreased thermal expansion coeffcient but substituted by ZnO was opposite direction and both of them increased bending strength. In the ratio of ZrOz to CaF, each 1: 1 and 1: 2 have shown considerable crystal growth at $1000^{circ}C~1050^{\circ}C$ and high bending strength, but the glass in the ratio 1: 2 have shown lowest thermal expansion coefficient. The activation energy was at the glass in the ratio of ZrO, to CaFz 1:2 evaluated 55.24kvsl/mol by Ozawa type and 53.05kal/mol by kissinger type.