• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.2
• /
• pp.106-110
• /
• 1998

The $LiNbO_3$ thin films were prepared directly on Si(100) substrates by conventional RF magnetron spurttering system for nonvolatile memory applications. RTA(Rapid Thermal Annealing) treatment was performed for as-deposited films in an oxygen atmosphere at 600 $^{\circ}C$ for 60 s. The rapid thermal annealed films were changed to poly-crystalline ferroelectric nature from amorphous of as-deposition. The resistivity of the ferroelectric $LiNbO_3$ film was increased from a typical value of $1{\sim}2{\times}10^8{\Omega}{\cdot}cm$ before the annealing to about $1{\times}10^{13}{\Omega}{\cdot}cm$ at 500 kV/cm and reduced the interface state density of the $LiNbO_3/Si$ (100) interface to about $1{\times}10^{11}/cm^2{\cdot}eV$. Ferroelectric hysteresis measurements using a Sawyer-Tower circuit yielded remanent polarization ($P_r$) and coercive field ($E_c$) values of about 1.2 ${\mu}C/cm^2$ and 120 kV/cm, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.12
• /
• pp.1283-1288
• /
• 2004

Metal-ferroelectric-insulator-semiconductor(WFIS) capacitors using rapid thermal annealed LiNbO$_3$/AlN/Si(100) structure were fabricated and demonstrated nonvolatile memory operations. The capacitors on highly doped Si wafer showed hysteresis behavior like a butterfly shape due to the ferroelectric nature of the LiNbO$_3$ films. The typical dielectric constant value of LiNbO$_3$ film in the MFIS device was about 27, The gate leakage current density of the MFIS capacitor was 10$^{-9}$ A/cm$^2$ order at the electric field of 500 kV/cm. The typical measured remnant polarization(2P$_{r}$) and coercive filed(Ec) values were about 1.2 $\mu$C/cm$^2$ and 120 kV/cm, respectively The ferroelectric capacitors showed no polarization degradation up to 10$^{11}$ switching cycles when subjected to symmetric bipolar voltage pulses of 1 MHz. The switching charges degraded only by 10 % of their initial values after 4 days at room temperature.e.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.37 no.6
• /
• pp.64-71
• /
• 2000

An optical switch composed of identical, equally-spaced $Ti:LiNbO_3$ three-waveguides was designed and fabricated. Patterned Ti was diffused into z-cut $LiNbO_3$ substrates. $SiO_2$ buffer layer was evaporated to reduce the propagation loss of TM mode, and Al electrodes of CPW structure were built on the layer for switching of the guided beam. The optical switching phenomenon was confirmed when a beam of ${\lambda}=1.3{\mu}m$ was launched into the center waveguide and an electric field was applied to detune the three waveguides symmetrically.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.3
• /
• pp.85-91
• /
• 1999

$H:LiNbO_3$ optical modulator with Cu/parylene electrode layer, which has a merits in the bandwidth, power consumption and fabrication conditions as compared with conventional Au/Cr/$SiO_2$, is proposed and fabricated. Analysis and design of optical modulator is performed by finite element calculation. Various unit processes for fabricating the proposed modulator, 1550nm $H:LiNbO_3$ optical waveguide, parylene buffer layer, and CPW Cu electrode, were developed, After dicing and end-face polishing of fabricated modulator chip, optical modulation responses as sawtooth electrical driving voltage has been measured at low frequencies. Properties of optical waveguide had not been changed before and after Cu/parylene electrode processes, which make confirm the reproducible fabrication of optical modulator.

• Proceedings of the IEEK Conference
• /
• 2000.11b
• /
• pp.221-224
• /
• 2000

We have successfully demonstrated metal-ferroel-ectric-insulator-semiconductor (MFIS) devices using Al/LiNbO$_{3}$/SiN/Si structure. The SiN thin films were made into metal -insulator- semiconductor (MIS) devices by thermal evaporation of aluminum source in a dot away on the surface. The interface property of MFIS from 1MHz & quasistatic C-V is good and the memory window width is about 1.5V at 0.2V/s signal voltage sweep rate. The gate leakage current density of MFIS capacitors using a aluminum electrode showed the least value of 1x10$^{-8}$ A/$\textrm{cm}^2$ order at the electric field of 300㎸/cm. And the XRD patterns shows the probability of applications of LN for MFIS devices for FeRAMs on amorphous SiN buffer layer.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.11
• /
• pp.765-770
• /
• 2001

Metal-ferroelectric-insulator- semiconductor(MFTS) devices by using rapid thermal annealed (RTA) LiNbO$_3$/AIN/Si(100) structures were successfully fabricated and demonstrated nonvolatile memory operations. Metal-insulator-semiconductor(MIS) C-V properties with high dielectric AIN thin films showed no hysteresis and good interface properties. The dielectric constant of the AIN film calculated from the capacitance at the accumulation region in the capacitance-voltage(C-V) characteristics was about 8. The C-V characteristics of MFIS capacitor showed a hysteresis loop due to the ferroelectric nature of the LiNbO$_3$ thin films. Typical dielectric constant value of LiNbO$_3$ film of MFIS device was about 23. The memory window width was about 1.2 V at the gate voltage of $\pm$5 V ranges. Typical gate leakage current density of the MFIS structure was the order of 10$^{-9}$ A/$\textrm{cm}^2$ at the range of within $\pm$500 kV/cm. The ferroelectric capacitors showed no polarization degradation up to about 10$^{11}$ switching cycles when subjected to symmetric bipolar voltage pulse(peak-to-peak 8 V, 50 % duty cycle) in the 500 kHz.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.655-658
• /
• 1989

The characteristics of proton-diffused $LiNbO_3$ optical waveguides with self-aligned $SiO_2$-cladding are reported. When the proton diffusion occurs, the $SiO_2$-cladding limits the lateral diffusion of protons by out-diffusion of protons in unclad region. Proton indiffusion in depth direction is promoted by inhibition of out-diffusion in clad region. Consequently, the mode profile in depth direction can be nealy symmetric. The extent of the proton exchange was observed by measuring the infrared absorption peak at about $3500cm^{-1}$. It is confirmed that proton diffusion with $SiO_2$-cladding has structural excellency.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.21-24
• /
• 1997

Ferroeletric LiNbO$_3$ thin films hale been prepared directly on Si(100) substrates by conventional RF magnetron spurttering system for nonvolatile memory applications. As-deposited films were performed RTA(Rapid Thermal Annealing) treatment in an oxygen atmosphere at 600 $^{\circ}C$ for 60 s. The rapid thermal annealed films were changed to poly-crystalline ferroelectric nature from amorphous of as-deposition. The resistivity of the ferroelectric LiNbO$_3$ film was increased from a typical vague of 1~2$\times$10$^{8}$ $\Omega$.cm before the annealing to about 1$\times$10$^{13}$ $\Omega$.cm at 500 kV/cm and reduce the interface state density of the LiNbO$_3$/Si(100) interface to about 1$\times$10$^{11}$ cm$^2$ . eV. Ferroelectric hysteresis measurements using a Sawyer-Tower circuit yielded remanent polarization (Pr) and coercive field (Ec) values of about 1.2 $\mu$C/cm$^2$ and 120 kV/cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.743-746
• /
• 2000

Metal-ferroelectric-insulator-semiconductor(MFIS) devices using Pt/$LiNbO_3$/Si structure were successfully fabricated. The dielectric constant of the AIN film calculated from the capacitance in the accumulation region in the capacitance-voltage(C-V) curve was about 8.2. The gate leakage current density of MIS devices using a aluminum electrode showed the least value of 1$\times$$1O^{-8}$A/$cm^2$ order at the electric field of 500kV/cm. The dielectric constant of $LiNbO_3$film on AIN/Si structure was about 23 derived from 1MHz capacitance-voltage (C-V) measurement and the resistivity of the film at the field of 500kV/cm was about 5.6$\times$ $1O^{13}$ $\Omega$.cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.235-238
• /
• 1998

Ferroelectric $LiNbO_3$ thin films were grown directly on Si(100) substrates by 13.55MHz RF magnetron sputtering system using a ceramic target ($Nb_2O_5/Li_2C0_3$ = 51.4/48.6). Because high temperature process have to avoided to prevent degradation of the interface (insulator/Si), $LiNbO_3$ thin films were deposited below $300^{\circ}C$. After as-deposited films were performed RTA treatments in an oxygen ambient at $600^{\circ}C$ for 60s, electrical measurements performed films before and after anneal treatment. In high field region, the leakage current density of the films after annealing was deceased about 4order and the resistivity of these was increased to about 5\times 10^{11} \Omega \cdot cm$ at 500kV/cm. In accumulation region of C-V curve, we calculated dielectric constant of thin film $LiNbO_3$ as 27.9 which is close to that of bulk value.