• Corrosion Science and Technology
• /
• v.22 no.2
• /
• pp.90-98
• /
• 2023

In this study, cobalt oxide (Co₃O₄) and cobalt-doped magnetite (CoFe₂O₄) nanoparticles were synthesized by a hydrothermal method. They were then used as corrosion inhibitors for corrosion protection of AA2024-T3 aluminum alloys. These obtained nanoparticles were characterized by x-ray diffraction, field-emission scanning electron microscopy, and Zeta potential measurements. Corrosion inhibition activities of Co₃O₄ and CoFe₂O₄ nanoparticles were determined by performing electrochemical measurements for bare AA2024-T3 aluminum alloys in 0.05 M NaCl + 0.1 M Na₂SO₄ solution containing Co₃O₄ or CoFe₂O₄ nanoparticles. Corrosion protection for AA2024-T3 aluminum alloys by a water-based epoxy with or without the synthesized Co₃O₄ or CoFe₂O₄ nanoparticles was investigated by electrochemical impedance spectroscopy during immersion in 0.1 M NaCl solution. The corrosion protection of epoxy coating deposited on the AA2024-T3 surface was improved by incorporating Co₃O₄ or CoFe₂O₄ nanoparticles in the coating. The corrosion protection performance of the epoxy coating containing CoFe₂O₄ was higher than that of the epoxy coating containing Co₃O₄.

• Journal of the Korean Ceramic Society
• /
• v.43 no.8 s.291
• /
• pp.498-503
• /
• 2006

A gas turbine blade with thermal barrier ceramic coating is operated at high temperature to increase engine efficiency. Recently, thermal barrier characteristics have been improved by advanced coating technology through microstructure control and increase of adhesion force of the coating layer. More advanced coating materials, rare earth zircon ate ceramics have been studied for replacing YSZ coatings as thermal barrier coatings. In this study, $La_2O_3,\;HfO_2,\;CeO_2,\;Gd_2O_3$ and pure or yttria stabilized zirconia were prepared. Microstructure analysis and the evaluation of mechanical properties such as Hertzian indentation and hardness test were performed.

• Journal of the Semiconductor & Display Technology
• /
• v.23 no.1
• /
• pp.88-91
• /
• 2024

The europium doped yttrium oxide (Y₂O₃:Eu³⁺) thin film was formed on a Si substrate by the conventional spin-coating process followed by rapid thermal annealing (RTA) treatment. The spinning profiles such as rotation speed, acceleration and holding times were controlled during the spin-coating process for the best condition of the Y₂O₃:Eu³⁺ thin film. The RTA treatment was conducted for several temperature in order to crystallize the spin coated film. The Y₂O₃:Eu³⁺ thin film presented best performance in the conditions of 4000 rpm, 30 s and 10 s of rotation speed, acceleration time and holding time, respectively, at a fixed RTA temperature of 900 ℃.

• Journal of Hydrogen and New Energy
• /
• v.21 no.6
• /
• pp.500-506
• /
• 2010

The metal monolith catalyst coated with 15wt% Ni/$MgAl_2O_4$ is applied to the natural gas steam reforming for hydrogen production. To address the improvement of adherence between metal monolith and catalyst coating layer, the pre-calcination temperature as well as the coating conditions of $Al_2O_3$ sol are optimized. When the Fe-Cr alloy monolith is pre-calcined at $900^{\circ}C$ for 6 h, $Al_2O_3$ layer was formed uniformly on the entire surface of the metal substrate. It is seen that the formation of $Al_2O_3$ layer on the monolith surface is essential for the uniform coating of $Al_2O_3$ sol onto the monolith substrate. The monolith catalyst coated with 10wt% $Al_2O_3$ sol shows high $CH_4$ conversion and good thermal stability as compared with the monolith catalyst without $Al_2O_3$ sol coating under severe reaction conditions with high GHSV of 30,000 $h^{-1}$ at $700^{\circ}C$. In addition, the metal monolith catalyst shows higher catalytic activity and better thermal conductivity than 15wt% Ni/$MgAl_2O_4$ pellet catalyst.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.9
• /
• pp.1737-1741
• /
• 2008

The electrochemical and thermal stability of $LiNi_{0.8}Co_{0.16}Al_{0.04}O_2$ were studied before and after $Co_3(PO_4)_2$ coating. Different to conventional coating material such as $ZrO_2$ or AlPO4, the coating layer was not detected clearly by TEM analysis, indicating that the $Co_3(PO_4)_2$ nanoparticles effectively reacted with surface impurities such as $Li_2CO_3$. The coated sample showed similar capacity at a low C rate condition. However, the rate capability was significantly improved by the coating effect. It is associated with a decrease of impedance after coating because impedance can act as a major barrier for overall cell performances in high C rate cycling. In the DSC profile of the charged sample, exothermic peaks were shifted to high temperatures and heat generation was reduced after coating, indicating the thermal reaction between electrode and electrolyte was sucessfully suppressed by $Co_3(PO_4)_2$ nanoparticle coating.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.12
• /
• pp.3083-3093
• /
• 1993

Friction and wear at ceramic coated surfaces of aluminum alloy were experimentally studied using a Ring-on-Block wear test machine. Ceramic materials coated on aluminum alloy surfaces were WC, CrC, $Al_{2}O_{3}$ by a plasma spray; and $Al_{2}O_{3}$,$Al_{2}SiO_{5}$, $Na_{2}B_{4}O_{7}$,$Na_{4}P_{2}O_{7}$, and $Al_{2}O_{3}-ZrO_{2}$ composite coating by an Anodic Spark Depositon. They were tested under the sliding wet contact and compared with aluminum alloys and steels. Test results showed that ceramic coated surfaces, in general, have better anti-wear property than those of aluminum alloys due to increase in the surface hardness ; however, they also showed higher coefficients of friction and changes in wear mechanisms, resulting in brittle fractures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.12
• /
• pp.788-793
• /
• 2017

Electrical behaviors of plasma-sprayed $Al_2O_3-TiO_2$ coatings have been investigated in terms of their $TiO_2$ content. On increasing the $TiO_2$ content from 6 to 30 wt%, the DC electrical conductivity increased by several orders of magnitude. From impedance spectroscopy analysis, the total conductivity of the grains and grain boundaries and their respective activation energies were determined without the electrode effects that could impede ionic transfer. An electron transference number was also estimated, ranging between 6.5% and 7.3% for 13 wt% $TiO_2$ and between 0.4% and 0.7% for 30 wt% $TiO_2$ in the coating. Because of the high electronic contribution to the total conductivity, the $Al_2O_3-TiO_2$ coating could be a new candidate material to obtain superior electrical conductivity as well as corrosion and wear resistances.

• Journal of Surface Science and Engineering
• /
• v.29 no.6
• /
• pp.607-614
• /
• 1996

Yttrium(Y) coating was incorporated by ion-plating method either directly on the TiAl substrate or after pack aluminizing on TiAl to improve the oxidation resistance of TiAl alloy. After Y-coating, heat treatment at low oxygen partial pressure was carried out. Performance of various coating was evaluated by isothermal and cyclic oxidation tests. A simple Y-coating without pack aluminizing can give a detrimental effect on the. oxidation resistance of TiAl alloy, because it enhances formation of $TiO_2$. On the other hand, a composite coating of aluminide-yttrium has shown excellent oxidation resistance. A continuous protective $Al_2O_3$ scale is formed on the aluminized TiAl, and Y-coating improves $Al_2O_3$ scale adherence and substantially prevents depletion of Al in the aluminide-coating layer.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.410-416
• /
• 2015

Recently, a new $Y_2O_3$ coating deposited using the EB-PVD method has been developed for erosion resistant applications in fluorocarbon plasma environments. In this study, surface crack formation in the $Y_2O_3$ coating has been analyzed in terms of residual stress and elastic modulus. The coating, deposited on silicon substrate at temperatures higher than $600^{\circ}C$, showed itself to be sound, without surface cracks. When the residual stress of the coating was measured using the Stoney formula, it was found to be considerably lower than the value calculated using the elastic modulus and thermal expansion coefficient of bulk $Y_2O_3$. In addition, amorphous $SiO_2$ and crystalline $Al_2O_3$ coatings were similarly prepared and their residual stresses were compared to the calculated values. From nano-indentation measurement, the elastic modulus of the $Y_2O_3$ coating in the direction parallel to the coating surface was found to be lower than that in the normal direction. The lower modulus in the parallel direction was confirmed independently using the load-deflection curves of a micro-cantilever made of $Y_2O_3$ coating and from the average residual stress-temperature curve of the coated sample. The elastic modulus in these experiments was around 33 ~ 35 GPa, which is much lower than that of a sintered bulk sample. Thus, this low elastic modulus, which may come from the columnar feather-like structure of the coating, contributed to decreasing the average residual tensile stress. Finally, in terms of toughness and thermal cycling stability, the implications of the lowered elastic modulus are discussed.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.11
• /
• pp.2584-2588
• /
• 2009

The effect of $LaF_3$ coating on the structural and electrochemical properties of $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_{2}$ cathodes was investigated using XRD, SEM, TEM, and a cycler. The coating layer consisted of nano-sized particles attached nonuniformly to the surface of pristine powder. Despite the surface coating treatment, phase difference by $LaF_3$ coating was not detected. The discharge capacities of coated electrodes were a little lower than that of pristine sample at a 1 C rate. However, as the C rate increases, the capacity retention of the coated sample becomes obviously superior to that of the pristine sample. The cyclic performances of the electrodes in the voltage range of 4.8 $\sim$ 3.0 V were also improved by the surface coating. Such enhancement is attributed to the presence of the $LaF_3$ coating layer, which effectively suppressd the reaction between electrodes and electrolytes on the surface of the $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_{2}$ electrode.