• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.1
• /
• pp.33-38
• /
• 2003

Highly homogeneous PZT powder was prepared by a partial oxalate method using chemicals of (Z $r_{0.53}$ $Ti_{0.47}$) $O_2$, Pb(N $o_3$)$_2$and (COOH)$_2$ㆍ2$H_2O$. N $b_2$ $O_{5}$ addition effect on microstructure and electrical properties of PZT ceramics was investigated. When the precursors were calcined at 71$0^{\circ}C$, a single perovskite phase was obtained. After sintering at 110$0^{\circ}C$, X-ray diffraction Patterns showed coexistence of rhombohedral and tetragonal phases regardless of the N $b_2$ $O_{5}$ content. As the content of N $b_2$ $O_{5}$ increased, grain size decreased but sintered density increased. The electromechanical coupling factor of kp and the piezoelectric constant of $d_{31}$ increased linearly with the content of N $b_2$ $O_{5}$, and those values reached 0.7 and -200, respectively, when 1.2 mol% of N $b_2$ $O_{5}$ is added. is added.ded.

• Journal of Korean Vacuum Science & Technology
• /
• v.6 no.1
• /
• pp.40-42
• /
• 2002

TiO$_2$/Fe$_2$O$_3$composite thin films were prepared on common glass substrates by sol-gel processing and dip-drawing method. The effect of Fe$_2$O$_3$content on the photocatalytic and hydrophilic properties of composite films was studied. The results indicate that the photocatalytic activities of composite TiO$_2$films are superior to that of pure TiO$_2$film, and the film containing 0.5% Fe$_2$O$_3$has the best photocatalytic activity. The hydrophilicity is difference with variant Fe$_2$O$_3$content, the films containing 0.05% ~0.1% Fe$_2$O$_3$have the best hydrophilicity and their contact angles are 0。.

• Korean journal of food and cookery science
• /
• v.10 no.3
• /
• pp.249-253
• /
• 1994

In this study, total dietary fiber contents, acid detergent fiber contents lignin, water binding capacity (WBC), iron binding capacity of ADF and rutin contents from Korean buckwheats were determined. Total dietary fiber (TDF) content was 3.14% in kyungbuk rice buckwheat, 5.65% in kangwon hull buckwheat and 3.35% in kangwon rice buckwheat. Acid detergent fiber (ADF) content was 2.47, 4.46 and 2.94%, respectively and lignin content was 1.14, 1.60 and 1.08% respectively. The water binding capacity of these three sample dietary fiber showed that TDF were in the range of 2.87~3.88 g %H_2O$/g DF and ADF were in the range of 4.62~5.26 g %H_2O$/g DF. The iron binding capacity of ADF at pH 5.0, 6.0, 7.0 were 79.11, 78.01, 46.16% in kyungbuk rice buckwheat, 70.63, 63.83, 53.60% in kangwon hull buckwheat and 77.67, 76.33, 50.25% in kangwon rice buckwheat. The rutin contents of these samples and their hulls were 13.54~16.41 mg/100 g groats and 12.13~14.24 mg/100 g in hulls. The rutin content of kyungbuk rice buckwheat was the highest.

• Korean Journal of Soil Science and Fertilizer
• /
• v.45 no.6
• /
• pp.1086-1093
• /
• 2012

This research was carried out to develop the correction method of VDI4630 method improving accuracy, and investigated the effects of carbonate ion ($CO_3{^{2-}}$) and reactant water ($H_2O$) on anaerobic organic biodegradability in VDI4630 method. Pig blood, pig intestine residue, pig digestive tract content, and cattle rumen content were experimented as waste biomasses. Chemical formulas of pig blood, pig intestine residue, pig digestive tract content, and cattle rumen content were $C_{3.78}H_{8.39}O_{1.46}N_1S_{0.01}$, $C_{9.69}H_{15.42}O_{2.85}N_1S_{0.03}$, $C_{25.17}H_{43.32}O_{15.04}N_1$, $C_{27.23}H_{42.38}O_{15.93}N_1S_{0.11}$, respectively. And amount of reactant moisture for the anaerobic degradation of organic materials were 0.336, 0.485, 0.227, 0.266 mol, respectively. In pig blood, pig intestine residue, pig digestive tract content, and cattle rumen content, anaerobic organic biodegradability presented as $B_u/B_{th}$ were 82.3, 81.5, 70.8, and 66.1%, and anaerobic organic biodegradability (AB) by VDI4630 method were 72.2, 87.8, 74.2, 62.0%, and that were significantly different with anaerobic organic biodegradability presented as $B_u/B_{th}$. The effects of carbonate ion and reactant water on anaerobic organic biodegradability were not significant, But Accuracy of anaerobic organic degradability was expected to able to be improved by the correction method of VDI4630 considering the carbonate ion at digestate and the reactant water quantified.

• Journal of the Korean Ceramic Society
• /
• v.41 no.1
• /
• pp.9-12
• /
• 2004

The effect of x wt% CuO-y wt% $V_2O_5$ content on the microwave properties of $(Pb_{0.45}Ca_{0.55})[(Fe_{0.5}Nb_{0.5})_{0.9}Sn_{0.1}]O_3$ (PCFNS) ceramics was investigated. In order to decrease the sintering temperature and use as a Low Temperature co-firing Ceramics (LTCC), CuO-$V_2O_5$ are added in the PCFNS. The bulk density, dielectric constant (${\varepsilon}_r$) and quality factor(Q${\cdot}f_0$) increased with increase in CuO content within a limited value. The microwave properties were degraded with increases in $V_2O_5$ content. The temperature coefficient of the resonant frequency (${\tau}_f$) of PCFNS was shifted to positive value abruptly with increasing the $V_2O_5$ content, while the ${\tau}_f$ was slightly shifted to positive value with increasing the CuO content. The optimized microwave properties, ${\varepsilon}_r$ = 88, Q${\cdot}f_0$ = 6100 (GHz), and ${\tau}_f$ = 18 ppm/$^{\circ}C$, were obtained in $(Pb_{0.45}Ca_{0.55})[(Fe_{0.5}Nb_{0.5})_{0.9}Sn_{0.1}]O_3$ with 0.2wt% CuO 0.05 wt% $V_2O_5$ and sintered at $1000^{\circ}C$ for 3 h. The relationship between the microstructure and microwave dielectric properties of ceramics was studied by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM)

• Advances in materials Research
• /
• v.3 no.1
• /
• pp.259-269
• /
• 2014

The boron-nitrogen-containing phenol-formaldehyde resin (BNPFR)/$SiO_2$ nanocomposites (BNPFR/$SiO_2$) were synthesized in-situ, and structure of BNPFR/$SiO_2$ nanocomposites was characterized by FTIR, XRD and TEM. The loss modulus peak temperature $T_p$ of BNPFR/$SiO_2$ nanocomposites cured with different nano-$SiO_2$ content are determined by torsional braid analysis (TBA). The thermal degradation kinetics was investigated by thermogravimetric analysis (TGA). The results show that nano-$SiO_2$ particulate with about 50 nm diameter has a more uniformly distribution in the samples. The loss modulus peak temperature $T_p$ of BNPFR/$SiO_2$ nanocomposite is $214^{\circ}C$ when nano-$SiO_2$ content is 6 wt%. The start thermal degradation temperature $T_{di}$ is higher about $30^{\circ}C$ than pure BNPFR. The residual rate (%) of nanocomposites at $800^{\circ}C$ is above 40 % when nano-$SiO_2$ content is 9 %. The thermal degradation process is multistage decomposition and following first order.

• Journal of the Korean Chemical Society
• /
• v.62 no.4
• /
• pp.269-274
• /
• 2018

Surface renewable nano-$RuO_2$/poly(methyl methacrylate) polymeric composite pH electrodes were prepared. The composite electrode with 53 wt% of nano-$RuO_2$ showed similar good response characteristics to nano-$IrO_2$ composite electrode reported earlier. It showed response slope of -58.7 mV/pH, response time of <1 s, surface renewability of $-57.0{\pm}0.3mV/pH$ (n=5) and long time stability for a month as well as low interferences but high interferences by electrochemically active species like $I^-$ and $Fe(CN){_6}^{3-}$. However, the response slope and time became worse at higher pH than 9 compared to those of nano-$IrO_2$ composite electrodes possibly due to the difference of physical properties resulting from higher content of nano-$RuO_2$ in polymeric composite matrix.

• Korean Journal of Metals and Materials
• /
• v.50 no.2
• /
• pp.183-190
• /
• 2012

Hydrogen was generated by the reaction of metal hydride with water. The variation of hydrogen generation with the kind of powders (milled $MgH_2$, and $MgH_2$ milled with various contents of MgO, $MgCl_2$ or $Ni+Nb_2O_5$) was investigated. $MgH_2$ powder with a hydrogen content of 6.05 wt% from Aldrich Company was used. Hydrogen is generated by the reaction of Mg as well as $MgH_2$ with water, resulting in the formation of byproduct $Mg(OH)_2$. For about 5 min of reaction time, milled $95%MgH_2+5%MgO$ has the highest hydrogen generation rate among milled $MgH_2+x%MgO$ (x=0, 5, 10, 15 and 20) samples. Milled $90%MgH_2+10%MgCl_2$ has the highest hydrogen generation rate among all the samples.

• Journal of the Korean Ceramic Society
• /
• v.31 no.8
• /
• pp.934-940
• /
• 1994

Fibers of ZrO2-SiO2 system were prepared from the hydrolysis and condensation of Si(OC2H5)4 and Zr(OnC3H7)4 with different H2O/alkoxide molar ratios. It was found that fibers could be drawn in the viscosity range of 1~100 poise from HCl catalyzed solutions with lower water contents of the mole ratio H2O/alkoxide, r 2. The fibrous gels were converted into the corresponding oxide glass fibers by heating at 80$0^{\circ}C$. Mechanical test was performed on E, A and 20ZrO2-80SiO2 glass fibers reinforced cement in order to investigate the flexural strength. The flexural strength value of 20ZrO2-80SiO2 glass fibers reinforced cement was greater than those of E and A. The chemical durability of the fibers in alkaline solutions increased with ZrO2 content. The weight loss due to the corrosion by 2N-NaOH solutions at $25^{\circ}C$ for 160 hours was about 0.31$\times$10-2 mg/dm2 for the 20ZrO2-80SiO2 glass fibers, which was superior to that of Vycor glass.

• Resources Recycling
• /
• v.10 no.4
• /
• pp.48-57
• /
• 2001

The main consistent materials and main elements of the bottom ash in municipal solid waste incineration ash according to particle size were investigated and the environmental hazards were considered by investigating the content of dioxin and heavy metals in bottom ash and the concentration of heavy metals in its leachate. The main materials of bottom ash are glasses, ceramics, scraps of iron. As the particle size increases, their percentage weight also increases and their percentage weight was over 70% in 4 mesh~25 mm particle size fraction. The main elements of bottom ash are CaO, $SiO_2$, $Fe_2$$O_3$,$ A1_2$$O_3$and the content of CaO decreases and the content of $SiO_2$increases as particle size increases. The heavy metals accumulate in small particle size fraction. The concentration of heavy metals in each leachate by domestic leaching test is almost similar. As the aging period is prolonged, pH of bottom ash lowers gradually and the leached concentration of Cu and Pb diminishes.