• 한국전기전자재료학회논문지
• /
• 제13권7호
• /
• pp.592-597
• /
• 2000

In this study (B $a_{0.5}$/S $r_{0.5}$)Ti $O_3$[BST(50/50)] ceramic thin films were prepared by the Sol-Gel method BST(50/50) stock solution was made and spin-coated on the Indium Tin Oxide(ITO)/glass substrate at 4000 rpm for 30 seconds. The coated films were dried at 35$0^{\circ}C$ for 10 minutes and annealed at 650~75$0^{\circ}C$ for 1 hour. The microstructural properties of the BST(50/50) thin film were studied by the XRD and AFM. The ferroelectric perovskite phase was formed at the annealing condition of 75$0^{\circ}C$ for 1 hour. Dielectric constant and loss of this thin were 370, 3.7% at room temperature respectively. The polarization switching voltage showed the good value of 3V. The leakage current density of the BST(50/50) thin film was 10$^{-7A}$c $m^2$with applied voltage of 1.5V. BST(50/50) thin film capacitors having good dielectric and electrical properties are expecting for the application to the dielectric material of DRAM.RAM.M.

• 한국세라믹학회지
• /
• 제36권4호
• /
• pp.403-409
• /
• 1999

RF 마그네트론 스퍼터링방법으로 Pt/Ti/NON/Si 기판 위에 $Ba_{0.66}$$Sr_{0.38}$$TiO_{3}$(BST) 박막을 증착한 다음 유전 및 초전특성을 살펴보았다. BST 박막을 증착할 때 기판온도를 300~-$600^{\circ}C$로 변화시킨 결과 기판온도가 증가할수록 박막의 결정성과 입도가 증가하여 유전율과 초전계수가 증가하였다. 한편 하부전극인 Pt의 증착조건이 BST 박막의 몰성에 미치는 영향도 살펴보았다. Pt의 증착온도와 Pt의 미세구조와 결정성뿐만 아니라 상부에 형성된 BST 박막의 배향성에도 큰 영향을 미쳤으며, 그 결과 BST의 초전특성에도 큰 영향을 미쳤다. BST 박막과 Pt 하부전극의 증착조건을 적정화함으로써 본 연구에엇는 상온에서 초전계수가 240 $nCcm^{-2}K^{-1}$인 BST 박막을 얻었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.301-304
• /
• 2002

We investigated the structural and electrical properties of Ce-doped Ba($Zr_{0.2}Ti_{0.8}$)$O_3$(BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/$SiO_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/$O_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 m (RMS at $500^{\circ}C$, Ar:6 scrim, $O_2$:6 sccm). We have found that annealing procedure after top electrode deposit can reduce the dissipation factor.

• 한국전기전자재료학회논문지
• /
• 제16권5호
• /
• pp.361-364
• /
• 2003

It was investigated that the structural and electrical Properties of Ce-doped Ba(Zr$_{x}$Ti$_{1-x}$ )O$_3$ (BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/SiO$_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/O$_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 nm (RMS at 500 $^{\circ}C$, Ar:6 sccm, $O_2$:6 sccm). It was found that annealing procedure after top electrode deposit can reduce the dissipation factor.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2002년도 추계총회 및 연구발표회 초록집
• /
• pp.33.2-33
• /
• 2002

• 한국세라믹학회지
• /
• 제30권8호
• /
• pp.657-663
• /
• 1993

BaTiO3 sputtering targets of 3 inch diameter were prepared by sintering the CIP (Cold Isotatic Pressing) compacts at 136$0^{\circ}C$ for 3hrs. The apparent density and grain size were 97% and 30${\mu}{\textrm}{m}$, respectively. After BaTiO3 films were deposited on Si and Pt/Ti/SiO2/Si substrates using these targets, films were annealed at various conditions and the crystallization behavior, reaction with the substrate and the electrical properties were investigated. The films on both substrates required 5~20hrs furnace annealing for crystallization at the temperatures from $600^{\circ}C$ to 80$0^{\circ}C$. For the films on Si substrate, interaction between the film and the substrate was suppressed upt o $700^{\circ}C$ for 10 hrs and the relative dielectric constant was 30. As the annelaing temperature and time were increased, the relative dielectric constants of the films decreased due to the formation of silicate phases through the reaction with the substrate. For the BaTiO3 films on Pt/Ti/SiO2/Si substrate, the reaction with the substrate was further reduced when the annealing condition was identical to that for Si substrate, but the reaction between the layers in Pt electrode took place above $700^{\circ}C$. When the films were annealed at $600^{\circ}C$ where the stability of Pt electrode was sustained, relative dielectric constant was increased to 110 since the reaction with substrate was effectively reduced even for a longer annealing time and the crystallization was enhanced.

• 한국세라믹학회지
• /
• 제34권8호
• /
• pp.803-810
• /
• 1997

Ba0.5Sr0.5TiO3박막을 RF 마그네트론 스퍼터링법을 이용하여 Pt/Ti/SiO2/Si(100) 기판에 증착하였다 .누설전류에 영향을 주는 것으로 알려진 열처리 조건, dopant 효과 등을 평가하고자 이온반경이Ti와 유사하고 대부분이 Ti 자리를 치환하는 것으로 알려진 Nb와 Al을 각각 danor와 acceptor로 선택하여 BST 박막에 첨가한 후 누설전류를 측정하였다. 고온에서 in-situ 증착된 BST 박막은 거친 표면 형상을 보이며 낮은 전압에서 파괴가 발생하고, Nb 첨가로 누설전류가 증가하였다. 삼온 증착후 후열처리된 박막은 표면 형상도 평할도가 증가하였으며 in-situ로 제조된 박막에 비해 높은 파괴전압과 낮은 누설전류를 나타내었다. 특히 Al이 첨가된 BST 박막의 누설전류밀도는 ~10A/cm2로 도핑을 하지 않은 박막이나 Nb가 첨가된 박막에 비해 매우 낮은 누설전류밀도를 나타내었으며, 이는 산화로 인한 산소공공의 감소, 이동 가능한 hole의 감소와 후열처리과정중 계면 및 입계의 산화로 Schottky 장벽에 높아진 결과로 판단된다.

• Journal of Ceramic Processing Research
• /
• 제20권4호
• /
• pp.395-400
• /
• 2019

This study was conducted on the structural and electrical properties of (Ba0.7Sr0.3)TiO3 thin films prepared by the sol-gel and spin-coating methods in order to investigate their applicability to electrocaloric devices. All specimens showed a tetragonal crystal structure and lattice constants of a = 3.972 Å, c = 3.970 Å. The mean grain size of specimens sintered at 800 ℃ was about 30 nm, and the average thickness of 5 times coated specimens was 304~311 nm. In the specimen sintered at 750 ℃, The relative dielectric constant and loss of specimens measured at 20 ℃ were 230 and 0.130, respectively, while dependence of the dielectric constant on unit DC voltage was -8.163 %/V. The remanent polarization and coercive fields were 95.5 μC/㎠ and 161.3 kV/cm at 21 ℃, respectively. And, the highest electrocaloric property of 2.69 ℃ was observed when the electric field of 330 kV/cm was applied.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.133.2-133.2
• /
• 2000

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 추계총회 및 연구발표회 초록집
• /
• pp.96.1-96
• /
• 2003