• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.761-768
• /
• 1995

Double layered BaTiO3 thin films with high dielectric constant as well as good insulating property were prepared for the application to low voltage driving thin film electroluminescent (TFEL) device. BaTiO3 thin films were formed by rf-magnetron sputtering technique. Amorphous and polycrystalline BaTiO3 thin films were deposited at the substrate temperatures of room temperature and 55$0^{\circ}C$, respectively. Two kinds of films prepared under these conditions showed high resistivity and high dielectric constant. The figure of merit (=$\varepsilon$r$\times$Eb.d) of polycrystalline BaTiO3 thin film was very high (8.43$\mu$C/$\textrm{cm}^2$). The polycrystalline BaTiO3 showed a substantial amount of leakage current (I), under the high electric field above 0.5 MV/cm. The double layered BaTiO3 thin film, i.e., amorphous BaTiO3 layer coated polycrystalline BaTiO3 thin film, was prepared by the new stacking method and showed very good dielectric and insulating properties. It showed a high dielectric constant fo 95 and leakage current density of 25 nA/$\textrm{cm}^2$ (0.3MV/cm) with the figure of merit of 20$\mu$C/$\textrm{cm}^2$. The leakage current density in the double layered BaTiO3 was much smaller than that in polycrystalline BaTiO3 under the high electric field. The saturated brightness of the devices using double layered BaTiO3 was about 220cd/$m^2$. Threshold voltage of TFEL devices fabricated on double layered BaTiO3 decreased by 50V compared to the EL devices fabricated on amorphous BaTiO3.

• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.1038-1044
• /
• 1996

The variations of sintering and electrical characteristics of semiconducting BaTiO3 ceramics with sintering agents added were investigated comparing the case of BaB2O4 addition to BN and TiO2 addition. When BaB2O4 added in BaTiO3 ceramics the densitifcation of specimen could be acheived more easily and recvealed the better PTCR characteristics than BN and TiO2 addition. As increase of addition of BaB2O4 in BaTiO3 spec imens the slope of resistivity jump also increased but the temperature of maximum resistivity decreased, It was supposed that addition of BaB2O4 led to increase of Ns (acceptor state density) value at grain boundaries.

• Korean Journal of Crystallography
• /
• v.10 no.1
• /
• pp.56-65
• /
• 1999

수열법을 이용하여 미세한 BaTiO3 분말을 합성하였다. Ti원으로 두 종류의 TiO2 gel을 사용하였으며 그 크기와 모양을 BaTiO3 합성에 주는 영향을 고찰하였다. 구형의 단분산 TiO2 gel을 사용하여 Ba(NO3)2 수용액에서 수열 합성한 BaTiO3 분말은 입자크기도 균일하였으며 응집이 일어나지 않아않았다. 비교적 낮은 pH에서 구형 TiO2 gel을 사용하여 합성한 BaTiO3 분말은 구형을 그대로 유지하였지만 높은 pH에서 합성한 BaTiO3 분말은 그 구형이 분해되었다. KOH양이 많아지고, 합성시간이 길어짐에 따라 합성된 BaTiO3 분말의 크기는 커졌으며 그 c/a 값도 증가하였다.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.214-222
• /
• 1996

The effect of physicochemical properties of organic solvent and dispersant among organic solvent dispersant binder and plasticizer which are used as processing additives in MLCC fabrication process on the dispersion of BaTiO3 was studied. The steric and electrostatic stabilization mechanisms in dispersion of BaTiO3 in organic media were evaluated respectively. The sttability of BaTiO3 achieved bysteric stabilization was dependent on the fraction of surface coverage of dispersant adsorption on BaTiO3. The electrostatic repulsive forces of BaTiO3 particles dispersed in orgainc media was found to be appreciabley great and dependent mainly on the kinds of organic solvent used. The mechanism affecting the stability of BaTiO3 was studied by the method of rheologi-cal behaviors of BaTiO3 suspension.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.8
• /
• pp.1068-1074
• /
• 1995

Effect of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ addition on the phase changes and microwave dielectric properties of BaTi $O_{3}$-3Ti $O_{2}$ ceramics were investigated. Addition of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ to BaTi $O_{3}$-3Ti $O_{2}$ resulted in the formation of Ba $Ti_{4}$$O_{9}$, $Ba_{2}$ $Ti_{9}$ $O_{20}$, Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_{3}$, and Ti $O_{2}$ phases. Ba $Ti_{4}$$O_{9}$ phase was gradually transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$. This was identified by XRD and microstructure. As the Ba $Ti_{4}$$O_{9}$ phase transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$ phase, the dielectric constant increased to 37.5. Q*f$_{o}$ value was 40000 at x=0.04, and the temperature coefficient of resonant frequency was +10ppm/.deg. C.C.. C.C.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.6
• /
• pp.495-500
• /
• 2009

The ceramic($BaTiO_3$)-polymer(epoxy) composites have been widely investigated as dielectric materials for embedded capacitors in printed circuit boards (PCBs). The dielectric properties of $BaTiO_3$/epoxy composites prepared using the agglomerated $BaTiO_3$ particles were investigated in the present study. The dielectric constants of the composites prepared using the agglomerated $BaTiO_3$ particles were about 2 times higher than those of the composites with the dispersed $BaTiO_3$ particles. The insulation resistance of the composites prepared using the agglomerated $BaTiO_3$ particles were lower than those of the composites with dispersed $BaTiO_3$ particles. As a result, there is tradeoff between high dielectric constant and insulation resistance in the $BaTiO_3$/epoxy composites. So it is important to select proper agglomerated or dispersed $BaTiO_3$ particles in accordance with needs.

• Korean Journal of Materials Research
• /
• v.21 no.9
• /
• pp.509-514
• /
• 2011

In this study, optical emission spectroscopy was used to monitor the plasma produced during the RF magnetron sputtering of a $BaTiO_3$ target. The intensities of chemical species were measured by real time monitoring with various discharge parameters such as RF power, pressure, and discharge gas. The emission lines of elemental and ionized species from $BaTiO_3$ and Ti targets were analyzed to evaluate the film composition and the optimized growth conditions for $BaTiO_3$ films. The emissions from Ar(I, II), Ba(I, II) and Ti(I) were found during sputtering of the $BaTiO_3$ target in Ar atmosphere. With increasing RF power, all the line intensities increased because the electron density increased with increasing RF power. When the Ar pressure increased, the Ba(II) and Ti(I) line intensity increased, but the $Ar^+$ line intensity decreased with increasing pressure. This result shows that high pressure is of greater benefit for the ionization of Ba than for that of Ar. Oxygen depressed the intensity of the plasma more than Ar did. When the Ar/$O_2$ ratio decreased, the intensity of Ba decreased more sharply than that of Ti. This result indicates that the plasma composition strongly depends on the discharge gas atmosphere. When the oxygen increased, the Ba/Ti ratio and the thickness of the films decreased. The emission spectra showed consistent variation with applied power to the Ti target during co-sputtering of the $BaTiO_3$ and Ti targets. The co-sputtered films showed a Ba/Ti ratio of 1.05 to 0.73 with applied power to the Ti target. The films with different Ba/Ti ratios showed changes in grain size. Ti excess films annealed at $600^{\circ}C$ did not show the second phase such as $BaTi_2O_5$ and $TiO_2$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.1005-1011
• /
• 1994

The three different composition of BaTi4O9, Ba2Ti9O20 and BaTi5O11 were prepared by coprecipitation process, and then the dielectric properties of these compounds were measured at low microwave frequencies. The powder showing high level of purity was synthesised by the coprecipition reaction of BaCl2 and TiCl4 where (NH4)2CO3 and NH4OH were used as a deflocculent. Followings are the result of this study: 1. The sintering temperature increased with increasing TiO2 content. 2. BaTi4O9 powder were synthesized as a single phase by this processing technique, but the resultant Ba2Ti9O20 and BaTi5O11 phase existed with Ba2Ti9O20 and BaTi5O11 phases. 3. Single phase BaTi4O9 showed high dielectric constant value of 35, high Q value of 8100.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.181-187
• /
• 1997

The layered BaTiO3 thin films with a high dielectric constant of polycrystalline BaTiO3 and a good in-sulating property of amorphous BaTiO3 were prepared. And their electrical properties were characterized with stacking methods. The BaTiO3 thin films were prepared by rf-magnetron sputtering technique using a ceramic target on Indium-doped Tin oxide coated glasses. A new stacking method resulted in higher dielec-tric constant, capacitance per unit area, and breakdown strength than those prepared by a conventional stacking method; the new method continuously decrease the substrate temperature after initial deposition of a polycrystalline BaTiO3 layer. The observed high dielectric constant could be explained only by a mul-tilayered amorphous/microcrystalline/polycrystalline structure, which was confirmed indirectly by AES depth profile.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.1
• /
• pp.87-96
• /
• 2004

Polymer/ceramic composites are the most promising embedded capacitor material for organic substrates application. Predicting the effective dielectric constant of polymer/ceramic composites is very important for design of composite materials. In this paper, we measured the dielectric constant of epoxy/$BaTiO_3$ composite embedded capacitor films with various $BaTiO_3$ particles loading for 5 different sizes $BaTiO_3$ powders. Experimental data were fitted to several theoretical equations to find the equation useful for the prediction of the effective dielectric constant of polymer/ceramic composites and also to estimate the dielectric constant of $BaTiO_3$ powders. The Lichtenecker equation and the Jayasundere-Smith equation were useful for the prediction of the effective dielectric constant of epoxy/$BaTiO_3$ composites. And calculated dielectric constants of the $BaTiO_3$ powders were in the range of 100 to 600, which were lower than those of $BaTiO_3$ bulk ceramics.