• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.3
• /
• pp.328-331
• /
• 2024

This research explores the development of [100]-textured barium titanate (BaTiO₃, BT) ceramics using sodium bismuth titanate (Na_0.5Bi_4.5Ti₄O₁₅, NBiT) templates, aimed at leveraging the inherent high dielectric property of BT. However, the attempted texturing was unsuccessful, primarily due to bismuth diffusion from the NBiT templates into the BT matrix below the sintering temperature, at 1,000℃. Systematical exploration about the cause of the failure is involved and alternative approaches are proposed in detail to overcome the challenge. These findings contribute to the understanding of techniques and conditions for textured ceramic fabrication and highlight the need for further research in this area.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.159-163
• /
• 2002

A single phase perovskite relaxor ferroelectric PMN-PT-BT was prepared by a single calcination and the modified mixed oxide process. It was accomplished by ball-milling PbO, $Nb_2O_5,\;Ti(OC_3H_7)_4,\;BaCO_3,\;and\;Mg(NO_3)_2$ instead of MgO, removing the solvent, and then followed by calcination at 900$^{\circ}C$ for 2h. The specimen sintered at 1100$^{\circ}C$/2h showed the sintered density of 7.83 g/$cm^3$, room temperature dielectric constant of 22000, and dielectric loss of 2.5%. Addition of 1.0 mole% (0.3 wt%) of Ag as $AgNO_3$ and followed by calcination at 550$^{\circ}C$/2h lowered the sintering temperature to 900$^{\circ}C$. It still showed the sintered density of 7.88 g/$cm^3$, room temperature dielectric constant of 20000 and dielectric loss of 2.4%.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1549-1550
• /
• 2013

• Proceedings of the Korean Magnestics Society Conference
• /
• 2012.05a
• /
• pp.81-81
• /
• 2012

• Korean Journal of Materials Research
• /
• v.13 no.12
• /
• pp.846-849
• /
• 2003

Doping effect of various ions in Bi-layered ferroelectric $SrBi_2$$Nb_2$$O_{9}$ (SBN) ceramics was studied. Undoped SBN ceramic and SBN ceramics doped with $Ba^{2＋}$, $Pb^{2＋}$,$ Ca^{2＋}$ , $Bi^{3＋}$ , $La^{3＋}$ , $Ti^{4＋}$ , $Mo^{6＋}$ , and $W^{6＋}$ ions were made by a solid state reaction. Dielectric constants were measured with temperature. Ferroelectric transition temperature decreased with $Pb^{2＋}$ , $Ba^{2＋}$ , $La^{3＋}$ doping, but the transition temperature increased with $Ca^{2＋}$ , $Bi^{3＋}$ , $Ti^{4＋}$, $Mo^{6＋}$ , or$ W^{6＋}$ ionic doping. These results show that the ion size plays an important role in the ferroelectricity of SBN ceramic.

• The Journal of the Petrological Society of Korea
• /
• v.11 no.1
• /
• pp.1-16
• /
• 2002

The study area is mostly composed of Precambrian Gyeonggi gneiss complex, Jurassic Daebo granites, Cretaceous tonalite and dykes, and so on. On the basis of field survey and mineral assemblage, the granites can be divided into three types; biotite granite (Gb), garnet biotite granite (Ggb) and two mica granite (Gtm). They predominantly belong to monzo-granites from the modes. Field relationship and K-Ar mica age data in the surrounding area suggest that intrusive sequences are older in order of Gtm, Ggb and Gb. Gb and Ggb, major study targets, occur as medium-coarse grained rocks, and show light grey and light grey-light pink colors, respectively. Mineral constituents are almost similar except for opaque in Gb and garmet in Ggb. Gb and Ggb have felsic, peraluminous, subalkaline and calc alkaline natures. In Harker diagram, both rocks show moderately negative trends of $TiO_2$, MgO, CaO, $Al_2O_3$, $Fe_2O_3$(t), $K_2O$ and $P_2O_5$ as $SiO_2$ contents increase. Among them, $TiO_2$, MgO and CaO show two linear trends. From the trends and the linear patterns in AFM, Sr-Ba and Rb-Ba-Sr relations, it is likely that they were originated from the same granitic magma and Ggb was differentiated later than Gb. REE concentrations normalized to chondrite value have trends of parallel LREE enrichment and HREE depletion. One data of Ggb showing a gradually enriched HREE trend may be caused by garnet accompaniment. Ggb have more negative Eu anomalies than Gb, suggesting that plagioclase fractionation in Ggb have occurred much stronger than that in Gb. In modal (Qz+Af) vs. Op, Gb and Ggb belong to magnetite-series and ilmenite-series, respectively. From the EPMA results, opaques of Gb are magnetite and ilmenite, and those of Ggb are magnetite-free ilmenite or not observed. Bimodal distribution of magnetic susceptibility reveals two different granites of Gb (332.6 ${mu}SI$) and Ggb (2.3 ${mu}SI$). Based on the paleomagnetic analysis as well as modal analysis, the main susceptibilities of Gb and Ggb reside in magnetite and mafic minerals, respectively. They belong to S-type granite of non-magnetic granite by susceptibility value. In addition, $SiO_2$ contents, $K_2O/Na_2O$, A/CNK molar ratio and ACF diagram support that they all belong to S-type granites.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.1
• /
• pp.1-4
• /
• 2015

(111)-oriented and random oriented $Pb_{0.8}Ba_{0.2}ZrO_3$ (PBZ) perovskite relaxor ferroelectric thin films were fabricated on Pt(111)/$TiO_x$/$SiO_2$/Si substrate by sol-gel method. Nano-scaled antiferroelectric and ferroelectric two-phase coexisted in both (111)-oriented and random oriented PBZ thin film. High dielectric tunability (${\eta}=75%$, E = 560 kV/cm) and figure-of-merit (FOM ~ 236) at room temperature was obtained in (111)-oriented thin film. Meanwhile, giant electrocaloric effect (ECE) (${\Delta}T=45.3K$ and ${\Delta}S=46.9JK^{-1}kg^{-1}$ at $598kVcm^{-1}$) at room temperature (290 K), rather than at its Curie temperature (408 K), was observed in random oriented $Pb_{0.8}Ba_{0.2}ZrO_3$ (PBZ) thin film, which makes it a promising material for the application to cooling systems near room temperature. The giant ECE as well as high dielectric tunability are attributed to the coexistence of AFE and FE phases and field-induced nano-scaled AFE to FE phase transition.

• Journal of the Korean Magnetics Society
• /
• v.18 no.4
• /
• pp.136-141
• /
• 2008

In this study, the magnetic(static and high-frequency) and microwave absorbing properties have been investigated in Ru-Co substituted M-hexaferrites($BaFe_{12-2x}Ru_xCo_xO_{19}$). The powders and sintered specimens were prepared by conventional ceramic processing technique. With the calcined powders, the composite specimens were prepared using the silicone rubber as a matrix material. The substitution ratio of Ru-Co to obtain in-plane magnetic anisotropy, thus having the minimum coercivity, is much smaller (about x=0.3) than the previously reported Ti-Co substituted specimen. Owing to this low substitution, the specimen has a large value of saturation magnetization($M_s$=65 emu/g). Ferromagnetic resonance behavior and microwave absorbing frequency band is strongly influnced by the coercvity which can be controlled by Ru-Co substitution ratio. It is found that the M-hexaferrites with planar magnetic anisotropy by doping Ru-Co in both sintered and composite form have superior microwave absorbing properties in GHz frequency range.

• Korean Journal of Materials Research
• /
• v.29 no.8
• /
• pp.469-476
• /
• 2019

A lead-free bulk ceramic having a chemical formula $Ba_{0.8}Ca_{0.2}(Ti_{0.8}Zr_{0.1}Ce_{0.1})O_3$ (further termed as BCTZCO) is synthesized using mixed oxide route. The structural, dielectric, impedance, and conductivity properties, as well as the modulus of the synthesized sample are discussed in the present work. Analysis of X-ray diffraction data obtained at room temperature reveals the existence of some impurity phases. The natural surface morphology shows close packing of grains with few voids. Attempts have been made to study the (a) effect of microstructures containing grains, grain boundaries, and electrodes on impedance and capacitive characteristics, (b) relationship between properties and crystal structure, and (c) nature of the relaxation mechanism of the prepared samples. The relationship between the structure and physical properties is established. The frequency and temperature dependence of the dielectric properties reveal that this complex system has a high dielectric constant and low tangent loss. An analysis of impedance and related parameters illuminates the contributions of grains. The activation energy is determined for only the high temperature region in the temperature dependent AC conductivity graph. Deviation from the Debye behavior is seen in the Nyquist plot at different temperatures. The relaxation mechanism and the electrical transport properties in the sample are investigated with the help of various spectroscopic (i.e., dielectric, modulus, and impedance) techniques. This lead free sample will serve as a base for device engineering.

• Journal of the Korean Ceramic Society
• /
• v.21 no.1
• /
• pp.60-66
• /
• 1984

During the metallization in the manufacturing of the ceramic capacitor at the boundary layer between Pd or Pt electrode and $BaTiO_3$-dielectric reactions were analysed. For the study of the reaction Electron Spin Resonance (ESR) Method was used. With the aid of ESR an increased of the concentration of the paramagnetic $Ti^{3+}$-Centers on the metallizing process could be seen. It meaned a reduction effect although the metallization was accomplished under oxidation atmosphere. Therefore it could be regarded as a reaction at the boundary layer. In order to investigate the reaction ad double octahedral model was compared and the increase of the $Ti^{3+}$-concentration was studied.