• Journal of Korean Ophthalmic Optics Society
• /
• v.8 no.2
• /
• pp.111-117
• /
• 2003

We collected the domestic and foreign half-mirror coating lens for sunglasses. Their reflectance is measured using Spectrophotometer in order to analysis their optical property and the result which is calculated using Macleod program was compared with measured reflectance. In addition, we designed the new half-mirror coating lens with gold color using TiN material and investigated the optical property of the new half-mirror coating lens. The results obtained from analysis of half-mirror coating lenses are as follow : Two-tone half-mirror coating with silver color is fabricated with [air|$SiO_2$(or $Al_2O_3$)|Cr|glass]. The role of $SiO_2$(or $Al_2O_3$) on Cr improve the hardness of the lens and the thickness of the $Al_2O_3$ with 10 nm is good to show the lens silver color. Incase of color half-mirror coating lens. Blue system is designed by [air|$SiO_2$(66.3)|$TiO_2$(129.0)|$SiO_2$(62.9)|$SiO_2$(26.0)|$TiO_2$(120.3)|$SiO_2$(9.1)|glass], gold system [air|$SiO_2$(60.6)|$TiO_2$(86.2)|$SiO_2$(13.5)|$TiO_2$(86.8)|$SiO_2$(214.38)|glass], green system[air|$SiO_2$(74.3)|$TiO_2$(75.8)|$SiO_2$(44.3)|$TiO_2$(11.6)|$SiO_2$(160.8)|$TiO_2$(12.9)|$SiO_2$(183.3)|$TiO_2$(143.8)|glass], silver system[air|$SiO_2$(21.2)|$TiO_2$(49.7)|$SiO_2$(149.3)|glass]. White half-mirror coating lens has [air|$SiO_2$(17 nm)|$TiO_2$(43 nm)(or $ZrO_2$)|$SiO_2$(87 nm)|polysiloxane($4.46{\mu}m$|glass or CR-19]. It has half-mirror coaling lens which has about 19% reflectance and about 80% transmittance in the range of visible light(400~700nm). we designed the new half-mirror coating lens with gold color, the (x, y) value of the CIE is almost similar to the CIE value of [air|$SiO_2$(170 nm)|TiN(15 nm)|glass].

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.505-512
• /
• 1998

In this study, two-layer thermal barrier coatings composed of plasma sprayed 0.3mm $ZrO_2(8wt% Y_2o_3)$ ceramic coating layer and O.lmm $NiCrAlCoY_20_3$ bond coating layer on AISI 316 were investigated microstructure of the coating, oxidation of the metallic bond coating and adhesive strength to evaluate the durability of coating layer after cyclic and isothermal test at 90$0^{\circ}C$. And quantitative phase analysis of $ZrO_2(8wt% Y_2o_3)$ ceramic coating was performed as a function of thermal exposure time using XRD technique. The results showed that the amount of m - 2rO, phase in the coating was slightly increased with increasing thermal exposure time at 90$0^{\circ}C$. The c/a ratio of t' - $ZrO_2$ in the as-sprayed coating was 1.0099 and slightly increased to 1.0115 after 100 hours heat treatment. It was believed that $Y_2O_3$ in high yttria tetragonaJ(t') was transformed to low yttria tetragonaJ(t) by $Y_2O_3$ diffusion with increasing thermal exposure time. The adhesive strength was gradually decreased as thermal exposure time increased. After the isothermal test, the failure predominantly occured in ceramic coating layer. On the other hand. the specimens after cyclic thermal test were mostly failed at bond coating/ceramic coating interface. The failure was oeeured by decreasing the bond strength between bond coating and oxide scale which were formed by oxidation of the metallic elements within bond coating and by thermal stress due to thermal expansion mismatches between the oxide scale and ceramic coating.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.377-381
• /
• 2014

This work describes the coloration, chemical stability of $SiO_2$ and $SnO_2$-coated blue $CoAl_2O_4$ pigment. The $CoAl_2O_4$, raw materials, were synthesized by a co-precipitation method and coated with silica ($SiO_2$) and tin oxide ($SnO_2$) using sol-gel method, respectively. To study phase and coloration of $CoAl_2O_4$, we prepared nano sized $CoAl_2O_4$ pigments which were coated $SiO_2$ and $SnO_2$ using tetraethylorthosilicate, $Na_2SiO_3$ and $Na_2SiO_3$ as a coating material. To determine the stability of the coated samples and their colloidal solutions under acidic and basic conditions, colloidal nanoparticle solutions with various pH values were prepared and monitored over time. Blue $CoAl_2O_4$ solutions were tuned yellow color under all acidic/basic conditions. On the other hand, the chemical stability of $SiO_2$ and $SnO_2$-coated $CoAl_2O_4$ solution were improved when all samples pH values, respectively. Phase stability under acidic/basic condition of the core-shell type $CoAl_2O_4$ powders were characterized by transmission electron microscope, X-ray diffraction, CIE $L^*a^*b^*$ color parameter measurements.

• Journal of the Korean Applied Science and Technology
• /
• v.23 no.3
• /
• pp.243-251
• /
• 2006

Field emission display(FED) is actively investigated in view of the development of full color flat-panel display, which can replace some cathode-ray tube(CRT). Thus, the development of new phosphors appropriate for FED is urgently needed and has been actively investigated. In this work, $SrTiO_3:Pr^{3+}$ phosphor was prepared by sol-gel method and the coating was applied by sol-gel method combined with sonication on these phosphor's surface into diluted precursor solution. It was found that very fine particles of coating material were formed on phosphor's surface. The luminescent intensity of $SrTiO_3:Pr^{3+}$ phosphor coated with $SiO_2$ and $Al_2O_3$ was considerably increased without any noticeable change in color chromaticity. The optimum concentration of coating material was found to be 1wt% and the optimum pH value of the solution was 10.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.339-344
• /
• 2017

Highly corrosion resistance performance of CrAlSiN coatings were obtained by applying ultrathin $Al_2O_3$ thin films using atomic layer deposition (ALD) method. CrAlSiN coatings were prepared on Cr adhesion layer/SUS304 substrates by a hybrid coating system of arc ion plating and high power impulse magnetron sputtering (HiPIMS) method. And, ultrathin $Al_2O_3$ passivation layer was deposited on the CrAlSiN/Cr adhesion layer/SUS304 sample to protect CrAlSiN coatings by encapsulating the whole surface defects of coating using ALD. Here, the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX) analysis revealed that the ALD $Al_2O_3$ thin films uniformly covered the inner and outer surface of CrAlSiN coatings. Also, the potentiodynamic and potentiostatic polarization test revealed that the corrosion protection properties of CrAlSiN coatings/Cr/SUS304 sample was greatly improved by ALD encapsulation with 50 nm-thick $Al_2O_3$ thin films, which implies that ALD-$Al_2O_3$ passivation layer can be used as an effect barrier layer of corrosion.

• Journal of the Korean Ceramic Society
• /
• v.38 no.7
• /
• pp.621-627
• /
• 2001

알루미나 졸에 평균 25nm의 TiO$_2$(Degussa P25) 광 촉매 분말을 분산하여 광촉매 코팅제를 제조하였다. 점도 약 24 cps를 가지 4.4 wt%의 알루미나 졸로부터 약 300nm 두께의 코팅막이 제조되었으며, 졸 점도의 증가에 비례하여 코팅막의 두께도 증가하였다. TiO$_2$광 촉매의 코팅용 바인더로 이용한 알루미나 졸의 결정형은 25~30$0^{\circ}C$에서 pseudo boehmite (AlOOH)이었으며, 50$0^{\circ}C$ 이상에서는 ${\gamma}$-Al$_2$O$_3$으로 전환되었다. AlOOH/TiO$_2$코팅막은 oleic acid와 humic acid에 대한 기상 및 수상 조건에서의 광 촉매 실험에서 우수한 유기물의 광분해 효능을 나타내었다. 아울러 EGI(Electro-Galvanized Iron)에 코팅된 AlOOH/TiO$_2$코팅막은 내식성 및 내지문성의 효과도 부수적으로 나타내었다.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.21 no.6
• /
• pp.64-69
• /
• 1984

We found that the maximum efficiency of Al-MIS (p-Si) solar ceil was shown at 80$\AA$ thickness of Al-film which was deposited with slower velocity than 0.6$\AA$/sec. It was coated with ZnS and SiO for Anti-Reflecting. In single coating, ZnS and SiO film had maximum Isc at 570 and 690 A thickness, respectively. We confirmed that these results agreed well with the quarter coating condition; n1d1=λ/4. In double coating, we held the one layer with its optimum thickness in single coating and controlled the other layer. The maximum value of Isc in this case was almost the same with it in single coating but was maintained its value in so wide range of thickness. Keeping the relation; n1d1=n2d2 as another way, we made the total thickness of film thinner to 70-90% of the sum of each optimum thickness in single coating. In this case Isc was higher value than 20% of it in any other previous case and was retained so wide range of thickness.

• Corrosion Science and Technology
• /
• v.21 no.3
• /
• pp.221-229
• /
• 2022

To understand effects of cooling rates of coating layer on microstructures and corrosion behaviors of hot-dip alloy coated steel sheets (Zn-5%Al-2%Mg) in a neutral aqueous condition with chloride ion, a range of experimental and analytical methods were used in this study. Results showed that a faster cooling rate during solidification decreased the fraction of primary Zn, and increased the fraction of Zn-Al phase. In addition, interlamellar spacing became refined under a faster cooling rate. These modifications of the coating structure had higher open circuit potentials (OCP) with smaller anodic and cathodic current densities in the electrochemical potentiodynamic polarization. Surface analyses after a salt spray test showed that the increase in the Zn-Al phase in the coating formed under a faster cooling rate might have contributed to the formation of simonkolleite (Zn₅(OH)₈Cl₂·H₂O) and hydrotalcite (ZnAl₂(OH)₆Cl₂·H₂O) with a protective nature on the corroded outer surface, thus delaying the formation of red rust.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.9
• /
• pp.121-126
• /
• 2009

Stainless steel 316L (STS 316L) is widely used as a material of biopsy needle. However it has a side effect that tissue can be damaged by electrochemical operation between tissue and STS 316L. Many studies have been made on the ceramic coating of biopsy needle to reduce the side effect. In this study, STS 316L was coated with three bioceramics, $Al_2O_3$, $SiO_2$ and $ZrO_2$ using a RF magnetron sputtering method. The effects of ceramic coating on the electrical conductivity and coating strength of ceramic-coated STS 316L were investigated. The results showed that the electrical conductivity of ceramic-coated STS 316L was much lower than that of uncoated STS 316L. The coating strength of $ZrO_2$-coated STS 316L was 30% and 70% higher, respectively than those of $Al_2O_3$-coated STS 316L and $SiO_2_3$-coated STS 316L.

• Journal of the Korean Society of Combustion
• /
• v.11 no.2
• /
• pp.7-14
• /
• 2006

Catalytic combustion is one of the suitable methods for micro power source due to high energy density and it can be applied to micro structured chamber without consideration of quenching since it is flameless combustion. Catalyst loading in the micro structured combustion chamber is one of the most important issues in the development of micro catalytic combustors. In this research, to coat catalyst on the chamber wall, two methods were investigated. First, $Al_2O_3$ was selected as a support of Pt and $Pt/Al_2O_3$ was synthesized through the alumina sol-gel procedure. To improve the coating thickness and adhesion between catalyst and substrate, heat resistant and water solvable organic-inorganic hybrid binder was used. Porous silicon was also investigated as a catalyst support for platinum. Through the parametric studies of current density and etching time, fabrication process of $1{\sim}2{\mu}m$ of diameter and about $25{\mu}m$ depth pores was confirmed. Coated substrates were test in the micro channel combustor which was fabricated by the wet etching and machining of SUS 304. Using $Pt/Al_2O_3$ coated substrate and Pt coated porous silicon substrate, conversion rate of fuel was over 95 % for $H_2/Air$ premixed gas.