This study investigates the effects of multi-axial diagonal forging (MADF) processing number on the microstructures of AA1100 fabricated using MADF processes. The cast AA1100 was annealed at $400^{\circ}C$ for 3hrs in $N_2$ atmosphere and cut into $25mm^3$ cubes for the MADF processes. The MADF process consist of plane forging with a thickness reduction of 30% and a diagonal forging with a diagonal forging angle of 135 degrees. In order to analyze the microstructural variations based on the number of repetitions, 1, 2, 3 and 4 cycles of the MADF process were performed. AA1100 specimens were successfully deformed without cracking of the surface for up to 4 cycles of MADF. The grain size, average misorientation and average grain orientation spread (GOS) of MADF processed materials were analyzed using EBSD technique. The results showed that MADF process effectively refined the microstructure of AA1100 with an initial average grain size of $337.4{\mu}m$. The average grain sizes of specimens which were MADF processed for 2, 3, 4 cycles were refined to be $1.9{\mu}m$, $1.6{\mu}m$, $1.4{\mu}m$, respectively. The grain refinement appeared saturated when AA1100 got MADF processed over 2 cycles. When the specimen was subjected to two or more cycles of MADF, the degree of decrease in the average grain size drastically decreased with an increase in the number of cycle due to the softening phenomena such as dynamic recovery or dynamic recrystallization during processing.