It is pointed out that the color of composite resin is changing according to it's ploymerization and this color change is a harmful effect for the clinical satisfacion of composite resin restoration. The purpose of this study was to compare the changes of color of newly developed composite resins between before and after exposure of activating light. Five Compostie resins (8 shades) were employed: Palfique Estelite(UL, U, DY, G ; Tokuyama), Photo Clearfil A (US : Kuraray), Photo Clearfil Bright (US ; Kuraray), GC Graft LC(A3 ; GC), Silux Plus(U; 3M), Tristirnulus values of each material were determined before and after curing-light exposure by using a Micro Multi Photometer (MMP-1001, Nihon Denshoku Kogyo). The values were transformed into $L^*\;a^*\;b^*$ system and color changes of the resins were evaluated by the changes of $L^*$, $a^*$ and $b^*$ values for the individual shades. In addition, the effects of resin thickness and background color on color changes were also studied The finding were as follows: 1. Color changes of $L^*$, $a^*$ and $b^*$ values were recognized due to the light exposure for all products. The $b^*$ values of Palfique Estelite showed negligible changes for all shades. 2. The $b^*$ values were affected strongly by the background color, especially when decreasing the brightness on the background color.(Request original article reprints to Dr. Aoshima)

By the concerns of esthetic restoration were increased recently. many all ceramic crowns were developed. But they except In-Ceram Alumina were used only single crown. In-Ceram Alumina, developed by Dr. Sadon, was revealed to have high flexural Strength(450MPa). So it could be used not only anterior bridges but also posterior bridges. But In-Ceram Alumina was seen to be opaque, a little green color in transillumination light by high content of alumina oxide(85%). So new all ceramics with high strength and high translucence were needed. Spinell($MgAl_2O_3$) have a high melting point, high flexural strength, low heat conductivity, high light conductivity. In-Ceram Spinell offers glasslike light transmission by using the spinell cores instead of the alumina cores. And they have a high translucency like to natural tooth, an excellent margin integrity and a high strength(350MPa). The purposes of this study are 1) to know about the construction method of In-Ceram Spinell System, 2) to investigate the its clinical possibiliy through patients and literature reviews.