he deposition and analysis of ITO thin film by DC magnetron sputter at room temperature

DC 마그네트론 스펏터를 이용한 ITO 박막의 실온 증착 및 특성 분석

  • Kim, Howoon (Dept. of Aviations Information & Communication Engineering, Kyungwoon University) ;
  • Yun, Jung-Oh (Dept. of Aviations Information & Communication Engineering, Kyungwoon University)
  • Received : 2020.02.14
  • Accepted : 2020.03.25
  • Published : 2020.03.31

Abstract

In this study, the characteristics of ITO thin film was investigated to finding a low cost and highly transparent electrodes for display of mobile communication devices. The ITO film was deposited by DC magnetron sputter. The experimental conditions were changed as follows: 1. ambient pressure changed 1 to 3 mTorr with 1mTorr step, 2. bias electric voltage changed with 10V step. The chamber was pumped out by rotary pump until 10-3Torr then the diffusion pump was used to lower the pressure of 10-6Torr. The results shows us the film growth was obvious when the bias voltage was larger than 300V, but the overall thickness tendency was existed: the more voltage is the thicker thickness. At 330V bias voltage condition, the deposition rate was the largest and apparent grain was showed.

최근 휴대용 통신기기와 스마트 디스플레이의 결합은 휴대가 용이하고 이동을 하면서 모든 작업을 할 수 있다. 이에 본 논문에서는 휴대용 통신기기에서 저가격의 높은 투명전극을 찾기 위해 여러 가지 ITO(Indium Tin Oxide) 박막에 대해 연구하였다. ITO 박막은 DC 마그네트론 스펏터를 사용하였으며 1 분위기압을 1mTorr 증가 간격으로, 2 바이어스 전압은 10V 간격으로 변화시켜 측정하였다. 두께와 굴절율은 일립소미터를 사용하였으며 막의 단면과 표면의 형상은 주사전자현미경을 사용하여 조사하였다. 분석 결과를 통해 바이어스 전압이 300V 이상일 경우에 명확한 증착이 나타났으며 추가로 전압이 증가함에 따라 전체적으로 증착률이 증가하였다. 330V 조건에서 증착률이 가장 높았으며 뚜렷한 결정립이 관찰되었다.

Keywords

References

  1. Ajinkya Bhorde, et al. "Room Temperature Synthesis of Transparent and Conducting Indium Tin Oxide Films with High Mobility and Figure of Merit by RF-Magnetron Sputtering," Journal of Electronic Materials, Vol.48, Issue11, pp.7192-7202, 2019. DOI: 10.1007/s11664-019-07533-8
  2. F. Djeffal, et al. "Effects of annealing temperature and ITO intermediate thin-layer on electrical proprieties of Au/p-Si structure deposited by RF magnetron sputtering," Superlattices and Microstructures, Vol.128, pp.382-391, 2019. DOI: 10.1016/j.spmi.2019.02.015
  3. Se-Il Kim, Yong-Min Kang, Se-Hee Kwon, Tae-Dong Jung, Seung-Ho Lee, Pung-keun Song, "Characteristics of ITO:Ce/PET Films for Flexible Display Applications," J. Kor. Inst. Surf. Eng. Vol.42, No.6, pp.276-279, 2009. DOI: 10.5695/JKISE.2009.42.6.276
  4. Jin Yeol Kim, Sun Ig Hong, "Influence of ITO Thickness on the Deformation and Cracking Behaviors of ITO/PET Sheets," Korean J. Mater. Res. Vol.19, No.1, pp.1-6, 2009. DOI: 10.3740/MRSK.2009.19.1.001
  5. Soo-Sun Lee, Na-Ri Lee, Kyeong-Il Kim, and Tae-Whan Hong, "Environmental Impacts Assessment of ITO (Indium Tin Oxide) Using Material Life Cycle Assessment," CLEAN TECHNOLOGY, Vol.18, No.1, pp.69-75, 2012. DOI: 10.7464/ksct.2012.18.1.069
  6. Won-Ho Jang et al, Electronic Display, SungAnDang Publisher, 2002.3.
  7. Yeong-Lee Kim, Cheol-Hyeon An, Si-U Gang, Dong-Chan Kim, Bo-Hyeon Gong, Won-Seok Han, Sang-Uk Jeon, Hyeong-Gyun Jo, "High temperature ZnO thin film deposition by sputtering to improve crystal propery," Proceedings of the Korean Institute of Surface Engineering Conference, pp.163-164, 2007.
  8. Seog-Sun Nam, "Expansion and Application of Publication Contents in the Era of Smart Media," The Journal of the Korea Contents Association, Vol.9, No.3, pp.12-17, 2014. DOI: 10.20924/CCTHBL.2011.9.3.012
  9. Young-Ho Son, Seung-Hoon Choi, Joong-Jin Park, Myoung-Hyo Jung, Youngjune Hur, In Soo Kim, "Fabrication and Study of Transparent Conductive Films ZnO(Al) and ZnO(AlGa) by DC Magnetron Sputtering," Journal of the Korean Vacuum, Vol. 22, No.3, pp.119, 2013. DOI: 10.5757/JKVS.2013.22.3.119
  10. Dae-Han Seo, Sung-Yong Chun, "A Comparative Study of CrN Coatings Deposited by DC and Inductively Coupled Plasma Magnetron Sputtering," J. Korean Inst. Surf. Eng. Vol.45, No.3, 2012. DOI: 10.5695/JKISE.2012.45.3.123
  11. Sung-Yong Chun, Se-Chul Kim, "A Comparative Study of Nanocrystalline TiAlN Coatings Fabricated by Direct Current and Inductively Coupled Plasma Assisted Magnetron Sputtering," Journal of the Korean Ceramic Society, Vol.51, No.5, pp.375-379, 2014. DOI: 10.4191/kcers.2014.51.5.375
  12. Sang-Won Park, Sung-Yong Chun, "A Comparative Study of CrN Coatings Deposited by DC and Pulsed DC Asymmetric Bipolar Sputtering for a Polymer Electrolyte Membrane Fuel Cell (PEMFC) Metallic Bipolar Plate," Journal of the Korean Ceramic Society, Vol.50, No.6, pp.390-395, 2013. DOI: 10.4191/kcers.2013.50.6.390
  13. C. David, et al. "Highly conductive and transparent ITO films deposited at low temperatures by pulsed DC magnetron sputtering from ceramic and metallic rotary targets," Surface and Coatings Technology, Volume, Vol.314, No.25 pp.113-117, 2017. DOI: 10.1016/j.surfcoat.2016.09.022
  14. Yilei Lu, et al. "Comparative study of AZO and ITO thin film sputtered at different temperatures and their application in Cu2ZnSnS4 solar cells," Journal of Materials Science: Materials in Electronics, Vol.29, Issue20, pp.17525-17532, 2018. DOI: 10.1007/s10854-018-9853-y
  15. A. Alyamani, N. Mustapha, "Effects of high dose gamma irradiation on ITO thin film properties," Thin Solid Films, Vol.611, pp.27-32, 2016. DOI: 10.1016/j.tsf.2016.05.022