Abstract
Single visit monolithic restoration can be proceed with digital workflow which consist of intraoral scanning, dental CAD(computer aided design) and restoration milling with CAM(Computer aided manufacturing). While zirconia has more than 900MPa of flexural strength compared with 400MPa for lithium disilicate, shortened fabricating time of lithium disilicate is considered to be a better choice for fabricating single visit full contour monolithic restoration. However, new zirconia materials which are TZI C(Dentsply Sirona) and LUXEN Enamel(Dental Max), new induction heating method of sintering furnace, and new sintering protocols for MoSi2 heating elements sintering furnace offer significantly reduction of full contour monolithic zirconia restoration fabrication time with greater translucency. These new developments lead single visit zirconia restoration in reality.
당일수복 보철물 제작을 위해 디지털 프로세스 사용은 필수적이다. 이러한 디지털 프로세스는 구강스캔, 컴퓨터를 이용한 보철물을 디자인 과정(CAD)과 보철물을 가공하는 과정(CAM)을 포함한다. 지르코니아의 굴곡강도는 900Mpa로 리튬디실리케이트의 400MPa보다 더 단단하지만, 리튬디실리케이트를 이용한 보철물 기공시간이 지르코니아와 비교하여 더 짧기에 당일수복 보철물 제작시 리튬디실리케이트 사용이 선호되었다. 하지만, TZI C 와 LUXEN Enamel 와 같은 새로운 소재의 지르코니아가 출시되고, 새로운 소결방식이 개발되어 지르코니아 기공시간을 단축시킬수 있게 되었고, 높은 투명도의 풀지르코니아 크라운을 짧은 시간 안에 제작할 수 있게 되었다. 이러한 발전은 당일 풀지르코니아 보철수복을 현실로 이끌고 있다.