(The Research Center of Conservation Science for Cultural Heritage, Hanseo University)
One of resins, V-Flon is useful as a coating material because YK-D80, which is a solvent for V-Flon, is not highly volatile. However, it can not completely harden and can flow out when metal artifacts are joined and restored in the process of the treatment. Therefore, after the impregnation process in order to accelerate the hardening speed of a coating material, usually a dry oven was adopted. This study focused on finding the problems on the dry oven which is employed to increase the speed and investigating the most effective solvent and its composition by checking any change occurred depending on the concentration of solvents. Six different types of solvents were selected and samples were prepared in a manner that they were impregnated with solvents in three concentrations respectively (10%, 20%, 30%). To determine the condition of the samples, the stability evaluation was performed by measuring the change of color and the gloss, the thickness of coated layers, the corrosion after coating, the water resistance by contact angles. Through the comparative experiments between the natural drying and the artificial drying using a dry oven, it was found that when the dry oven is used, some problems are identified on the point of forming a uniform and stable layer because of the unstable data collected from the forced artificial dry. The experiments performed using 3 different concentration rates (10%, 20%, 30%) presented that in the case of 10% V-Flon in Xylene (using as a solvent), its layer was thin as well as it showed the high water-barrier property, which allows it to form the stably coated layer with the lower gloss and color change.
금속 유물 코팅제로 사용되는 V-Flon은 함께 사용되는 용제인 YK-D80의 늦은 휘발성으로 작업에는 용이하나, 후처리로 유물을 접합하거나 복원처리 시, 코팅제가 완전 경화되지 않고 흘러나오는 문제점이 발생한다. 따라서 함침처리 후에 코팅제의 경화 속도를 가속시키기 위해 열풍 건조기에서 경화시키는 경우가 대부분이다. 이러한 V-Flon의 용제 휘발 속도의 문제점을 보완하고자 적용시키는 열풍 건조에 대한 문제점을 알아보고, 용제와 농도에 따른 변화 정도를 살펴보아 가장 효과적인 용제와 그 조성을 찾고자 하였다. 6 종류의 용제를 선정하였고 농도는 10%, 20%, 30%의 세 가지 농도로 함침 처리하여 시편을 제작하였다. 그리고 시편의 상태를 알아보기 위해서 금속 표면의 색상 및 광택 변화, 코팅막 두께 측정, 코팅 후의 부식 실험, 접촉각을 통한 내수성 측정을 실시하여 코팅제의 안정성을 평가하였다. 자연 건조와 열풍 건조의 비교 실험 결과, 열풍 건조는 외부의 강제 건조로 데이터 값이 불안정하여 균일하고 안정한 코팅막 형성에는 문제가 있음을 확인할 수 있었으며, 용제의 농도에 따른 실험 결과 V-Flon을 Xylene 용제를 이용하여 10% 용액으로 제조하여 사용할 경우, 얇은 코팅막에도 불구하고 높은 수분 차단성을 가지고 있었으며, 낮은 광택과 색변화를 나타내는 안정된 코팅막을 형성할 수 있었다.