Recycle of the Glass fiber Obtained from the Roving Cloth of FRP II: Study for the Physical Properties of fiber-reinforced Concrete

폐 FRP 선박의 로빙층에서 분리한 유리섬유의 재활용 II: 섬유강화 콘크리트의 물성에 관한 연구

Recycling glass fiber, 'F-fiber,' was obtained by the separation of the roving layer from waste FRP and the concrete products or structures were considered for its application. Experiment was carried out for the bending strength of aggregate (2.45 of cement) by weight and F-fiber (density of 1.45, volume ratio to all of the aggregate and the cement). Whereas the specimen containing 1% F-fiber showed the bending strength 23% higher than that without F-fiber after curing far 28 days, the one with 0.5% F-fiber did not give any change. It could be found, therefore, that the minimum mixing amount should be larger than 0.5% fur the strength reinforcement. One of the reinforcing concrete product, bench flume, containing 1% F-fiber showed 21% increment of bending strength In contrast to that without F-fiber.

폐FRP의 로빙층을 매트층과 수지로부터 분리하여 섬유 형태의 'F섬유'를 얻었으며, 이것의 용도로 콘크리트 제품 또는 구조물을 고려하였다. 골재는 시멘트의 2.45 배(무게비)로 하고 F섬유(밀도 1.45)는 시멘트와 골재의 부피비로 계산하여 만든 공시체에 대한 휨강도를 실험하였다. 1%의 F섬유를 갖는 것이 양생한 지 28일째 되었을 때 넣지 않은 것에 비해 23%의 강도 증가를 보였다. 그러나 0.5%를 포함한 공시체의 경우는 강도의 변화를 보이지 않음으로써 강도 보강용으로 쓰일 수 있는 최소 혼입량이 0.5% 보다는 크다는 것을 알았다. 철근 콘크리트 시제품인 벤치 플룸의 경우 1% F섬유를 포함할 때 포함하지 않은 것에 비해 휨강도가 21%증가하였다.