Formation and Characterization of Red Phosphor Nano Powders

적색 형광체 나노 분말의 합성 및 특성 평가

  • Received : 2007.08.03
  • Accepted : 2007.11.01
  • Published : 2008.02.10
Download PDF
⟨ Previous Next ⟩

Abstract

Nano-sized phosphor powders were synthesized by the liquid phase method to confirm the size and morphology. By using the process, red phosphor particles with a size of 80 nm were obtained. The characteristic comparison of $Y_2O_3:Eu^{3+}$ and $YBO_3:Eu^{3+}$ was carried out and, as a result, $YBO_3:Eu^{3+}$ powders using boric salt showed an aggregated morphology and lower PL performance compared to $Y_2O_3:Eu^{3+}$.

나노 형광체 합성에 있어서 입자 형상 및 입자 크기의 변화를 알아보기 위해 액상법으로 진행하였으며, 이를 바탕으로 최종적으로 약 80 nm급의 적색 나노 형광체의 합성이 가능하였다. 합성된 두 가지의 $Y_2O_3:Eu^{3+}$와 $YBO_3:Eu^{3+}$ 적색 나노 분말의 특성 평가를 비교하였으며, 그 결과 붕산염을 사용한 $YBO_3:Eu^{3+}$ 형광체 분말이 형상 면에서 약간의 응집이 발생하였으며, PL 특성 면에서도 $Y_2O_3:Eu^{3+}$ 대비 낮은 형광성을 보여주었다.

Keywords

Acknowledgement

Supported by : 에너지 관리공단

References

  1. C. R. Ronda and B. M. J. Smets, J. Electrochem. Soc., 136, 570 (1989) https://doi.org/10.1149/1.2096684
  2. S. Oshio, K. Kitamura, T. Shigeta, S. Horii, T. Matsuoka, S. Tanaka, and T. Kanda, J. Electrochem. Soc., 146, 392 (1999) https://doi.org/10.1149/1.1391620
  3. C. R. Ronda, J. Alloys Comp., 225, 534 (1995) https://doi.org/10.1016/0925-8388(94)07065-2
  4. J. M. P. J. Verstegen, D. Radielovic, and L. E. Vrenken, J. Electrochem. Soc., 121, 1627 (1974) https://doi.org/10.1149/1.2401757
  5. H. Yamamoto, J. SID., 4, 165 (1996)
  6. J. C. Park, H. K. Moon, D. K. Kim, S. H. Byeon, B. C. Kim, and K. S. Suh, Appl. Phys. Lett., 77, 2161 (2000)
  7. Y. Pan, Q. Su, H. Xu, T. Chen, W. Ge, C. Yang, and M. Wu, J. Solid State Chem., 174, 69 (2003) https://doi.org/10.1016/S0022-4596(03)00175-0
  8. H. S. Rho, C. H. Lee, H. S. Yoon, Y. C. Kang, H. D. Park, and S. B. Park, HWAHAK KONGHAK, 40, 752 (2002)
  9. D. Ravichandran, R. Roy, W. B. White, and S. Erdei, J. Mater. Res., 12, 819 (1997) https://doi.org/10.1557/JMR.1997.0119
  10. T. R. N. Kutty, R. Jagannathan, and R. P. Rao, Mat. Res. Bull., 25, 1355 (1990) https://doi.org/10.1016/0025-5408(90)90217-P
  11. D. S. Bae, K. S. Han, S. B. Cho, and S. H. Choi, J. Kor. Association of Crystal Growth, 7, 167 (1997)
  12. S. B. Cho, S. Venigalla, and J. H. Adair, J. Am. Ceram. Soc., 79, 88 (1996) https://doi.org/10.1111/j.1151-2916.1996.tb07884.x