The effect of excess Bi contents on the ferroelectric properties of B $i_{3.25}$ L $a_{0.75}$ $Ti_3$ $O_{12}$ (BLT) thin films has been investigated. Bismuth lanthanum titanate thin films with excess Bi contents were prepared onto Pt/Ti/ $SiO_2$/Si substrate by metalorganic decomposition (MOD) technique. The structure and morphology of the films were analyzed using X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. From the XRD analysis, BLT thin films show polycrystalline structure and the layered-perovskite phase was obtained over 10% excess of Bi contents. As a result of ferroelectric characteristics related to the Bi content of the BLT thin film, the remanent polarization and dielectric constant decreased with increasing over Bi content of 10% excess. The BLT film with Bi content of 10% excess was measured to have a dielectric constant of 326 and dielectric loss of 0.024. The BLT thin films showed little polarization fatigue test up to 3.5$\times$10$^{9}$ bipolar switching cycling.