Abstract
In this paper, the (S $r_{0.85}$.C $a_{0.15}$)Ti $O_{3}$ of paraelectric grain boundary layer (GBL) ceramics were fabricated, and the analysis of microstructuye and the thermally stimulated current(TSC) were investigated for understanding effects of GBL's interfacial phenomenon on variations of electrical properties. As a result, the three peaks of .alpha., .alpha. and .betha. were obtained at the temperature of -20 [.deg. C], 20[.deg. C] and 80[.deg. C], respectively. The origins of these peaks are that the .alpha. peak observed at -20[.deg. C] looks like to be ascribed to the ionization excitation from donor level in the grain, and the .alpha.' peak observed at 20[.deg. C] appears to show up by detrap of the trapped carrier of border between the oxidation layer and the grain, and the .betha. peak observed at 80[.deg. C] seems to be resulted from hopping conduction of existing carrier in the trap site of the border between the oxidation and second phase. and second phase.