The fabrication of ITO/p-InP solar cells

ITO/p-InP 태양전지 제작

  • 맹경호 (㈜포스코 홀스) ;
  • 김선태 (대전산업대학교 재료공학과) ;
  • 송복신 (광운대학교 전자재료공학과) ;
  • 문동찬 (광운대학교 전자재료공학과)
  • Published : 1994.05.01

Abstract

ITO(Indium Tin Oxide) film with thickness of 1500.angs. was prepared by an e-beam evaporator onto a glass and a p-type InP wafer (100) LEC grown Zn-doped p=2.3*10$\^$16/cm$\^$-3/), in which the components of ITO used for evaporation source were hot pressed pellets 1 mole% ln$\_$2/O$\_$3/+9 mole% SnO$\_$2/, and evaporated in O$\_$2/ ambient. The optimum conditions to preparation of ITO thin film were the substrate temperature of 350.deg. C, the injected oxygen pressure of 2*10$\^$-4/ torr, and the evaporation speed of 0.2-0.3.angs./sec, respectively. In these optimum conditions, the resistivity and the carrier concentration were 5.3*10$\^$-3/ .ohm.-cm, 6.5*10$\^$20/cm$\^$-3/, and the transmittance was over 80%. From the results of J-V measurements in ITO/p-InP structure solar cells, the higher pressure of injected oxygen, the more open circuit voltage. The efficiency of ITO/p-InP solar cell without the grid line contact, prepared by the optimum evaporation conditions, was 7.19%. By using the grid line contact, the efficiency, the open circuit voltage, the short circuit current density, the fill factor, the series resistance, and the shunt resistance were 8.5%, 0.47V, 29.48 mAcm$\^$-2/ , 61.35%, 3.ohm., and 26.6k.ohm., respectively.

Keywords