Measurement of Complex Sound Pressure Reflection Coefficient Using Standing Wave Tube

正常波管을 利用한 複素反射係數의 測定

The reflection coefficients of the sound absorbing materials are obtained from the standing wave ratio in the standin wave tube. This method is rather laborious to find the sound pressure maximum and minimum. We devised new method for determination of the complex reflection coefficients of the materials. The sound pressures and the phases are measured at least three points along the axis of the tube. The complex reflection coefficients are determined from the measured values by least square method. The measured results for the glasswool with thickness of 5cm and density of $50kg/m^3$ and the steel plate with thickness of 1.5cm are in good agreement with those of the conventional method. It is possible to measure the complex reflection coefficients at low frequencies with short standing wave tube and to interface with the personal computer which is very useful for the handling of amount of samples.

建策材料의 複素反射係數로 測定하기 爲해 새로운 方法을 指示하였다. 旣存의 方法인 正常波管內에서 正常波比를 測定하여 反射係數를 計算할 境遇, 管內에서 音壓의 最大값과 最小값을 精密하게 測定하기 爲해서는 많은 努力을 기울여야 하면 特히 많은 試料를 取扱할 때 境過 매우 번거로운 作業이 된다. 本 論文에서는 이러한 短點을 補完하기 爲해 任意의 세 位置에서 音壓과 位相 및 各 測定점까지의 距離를 測定한 後 最小自乘法에 의해 複素反射係數를 測定하는 方法을 考案하였다. 이 方法으로 두께 5cm, 密度 $50kg/m^3$인 유리纖維와 두께 1.5cm 인 鋼부反에 대한 複素反射係數를 測定한 結果와 旣存의 方法으로 測定한 結果가 잘 一致하는 것을 實驗으로 確認하였다. 또한 이 方法은 길이가 짧은 正常波管으로도 低周波의 反射係數를 測定할 수 있는 長點이 있을 뿐만 아니라 컴퓨터와 interface가 가능하기 때문에 특히 試料를 取扱하는 境遇 效果的으로 使用될 수 있을 것을 期待된다.