Polymer coating for controlled release of biostimulants from Biostimulant balls

생물활성촉진제의 용출율 제어를 위한 폴리머 코팅

We prepared biostimulant balls using sea sediment mixed with biostimulants viz acetate, nitrate and sulfate. The Biostimulant balls were coated with Cellulose Acetate (CA) and Polysulfone (PS) to control the release of the biostimulants. SEM images showed that CA coating was porous and irregular in the inside and very uniform and tight like beehive while PS coating was the same in the inside and outside and not porous. Biostimulants release was found to be high in sea water compared to distilled water. The release of nitrate was higher compared to sulfate. In turbulent environment the release of bionutrients was 50% higher than static environment.

오염물질이 처리된 해양저질을 이용하여 황산염, 질산염 및 아세테이트 등의 생물활성물질을 첨가하여 생물활성촉진볼을 제작하였으며, 셀룰로스 아세테이트 코팅(CA)과 폴리설펀 코팅(PS) 방법으로 표면을 처리하여 생물활성촉진물질의 용출율을 조절하고자 하였다. SEM 분석으로 평가한 생물활성촉진제의 형태적 특성은 CA의 경우, 내부코팅층은 비교적 큰 공극이 다소 존재하였으며, 외부 코팅층은 균일하고 촘촘한 벌집모양의 공극이 분포되어있었고, PS의 경우, 내부코팅층과 외부코팅층의 모양이 동일하고, 무공극층이 형성된 것으로 나타났다. 코팅방법에 따른 생물활성촉진물질의 용출율은 증류수조건에서보다 해수조건에서 다소 높았고, 질산염이 황산염에 배해 다소 빨리 용출되었으며, 정체조건에 비해 난류조건에서 약 50%이상 높았다.