Dielectric and Piezoelectric Characteristics of Low Temperature PMN-PZT Ceramics with the amount of PFW substitution

PFW치환에 따른 저온소결 PMN-PZT 세라믹스의 유전 및 압전 특성

In this study, in order to develop multilayer piezoelectric transformer, PMN-PZT ceramics were fabricated according to PFW substitution using $Li_2CO_3-CaCO_3$ as sintering aids and their dielectric and piezoelectric characteristics were investigated. As increasing the amount of PFW substitution, density was slightly increased due to the increased sinterability. At the 1[mol%] PFW substituted PMN-PZT ceramic sintered at 950[$^{\circ}C$], density, dielectric constant $\varepsilon_r$, electromechanical coupling factor kp, mechanical quality factor Qm and piezoelectric $d_{33}$ constant showed the optimum value of 7.761[$g/cm^3$], 1251, 0.479, 1425 and 282[pC/N], respectively.