• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.225-227
• /
• 2006

As rail steel at a crossing area must undergo much higher loading than those at regular railway, Mn-alloyed steel is normally used for its high load-carrying capability and reduced wear rate. However, as these Mn-alloyed steel is tend to have casting defects, manufacturing cost to produce defect-free Mn-alloyed steel becomes quite expensive. Therefore, in order to replace Mn-alloyed steel, we performed build-up welding using CH-90 and investigated regarding to wear characteristics of build-up weld metal.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.300-306
• /
• 2004

A laser welding has been made between sintered tip of Fe-Co-W and low carbon steel shank for the diamond saw blade. The welding characteristics and formation of defect has been investigated carefully for the weld fusion zone in different welding condition. Full penetration has been observed for the whole range of heat input investigated in the present work. Bead width and under-fill have been increased with the increase of heat input. With increasing of heat input small cavities were decreased while large cavities were increased. The ratio of total cavity area to the entire weld bead area was not changed significantly with change of heat input. Most of cavities were found near the tip, and supposed to be formed from the pore in the tip.

• Transactions of Materials Processing
• /
• v.9 no.1
• /
• pp.10-16
• /
• 2000

This research investigates microstructures and fatigue properties of the weldments of 6005A aluminum alloy developed for railroad vehicles. The samples were extruded into a truss structure and welded together using the gas metal arc welding process. The extruded sample showed a wide variation in grain size, possibly due to the frictional heating as well as the inghomogeneous metal flow in the extrusion die. The mechanical properties of the samples were affected by the mirocstructures. The fatigue strength of the welded structure was found to decrease significantly from that of the base metal. It was found that the fatigue characteristics of the welded structure were determined by the microstructure of the parent metal as well as weld defects such as porosities and the liquation cracks.

• International Journal of Naval Architecture and Ocean Engineering
• /
• v.7 no.4
• /
• pp.770-783
• /
• 2015

Lately, high production rate welding processes for Al alloys, which are used as LNG FPSO cargo containment system material, have been developed to overcome the limit of installation and high rework rates. In particular, plasma-metal inert gas (MIG) hybrid (PMH) welding can be used to obtain a higher deposition rate and lower porosity, while facilitating a cleaning effect by preheating and post heating the wire and the base metal. However, an asymmetric undercut and a black-colored deposit are created on the surface of PMH weld in Al alloys. For controlling the surface defect formation, the wire feeding speed and nozzle diameter in the PMH weld was investigated through arc phenomena with high-speed imaging and metallurgical analysis.

• Journal of Korean Society of Steel Construction
• /
• v.10 no.3 s.36
• /
• pp.423-435
• /
• 1998

In this paper fatigue strength reduction of butt weld with penetration defect, which can be seen frequently in the steel bridge, was assessed quantitatively. S-N curves were derived and investigated through the constant amplitude fatigue test of fully or partially penetrated welded specimen made of SWS490 steel. The fracture mechanical method was applied in order to calculate the remaining fatigue life of the partially penetrated butt welds. The fatigue limit of the fully penetrated butt welds was higher than that of category A in AASHTO's fatigue design curves, and the slope of S-N curves with 5.57 was stiffer than that of other result for welded part generally accepted as 3. The fatigue strength of the partially Penetrated butt weld was strongly influenced by the size of lack of penetration, D. It decreased drastically with increasing D from 3.9 to 14.7mm. Fracture behaviour of the partially penetrated butt weld is able to be explained obviously from the beach mark test that a semi-elliptical surface crack with small a/c ratio initiates at a internal weld root and propagates through the weld metal. To estimate the fatigue life of the partially penetrated butt weld with fracture mechanics, stress intensity factors K of 3-dimensional semi-elliptical crack were calculated by appling finite elements method and fracture mechanics parameters such as C and m were derived through the fatigue test of CT-specimen. As a result, the fatigue lives obtained by using the fracture mechanical method agreed well with the experimental results. The results were applied to Sung-Su bridge collapsed due to penetration defects in butt weld of vertical member.

• Journal of Institute of Control, Robotics and Systems
• /
• v.11 no.7
• /
• pp.595-601
• /
• 2005

A mobile robot system utilizing NDT (Non-Destructive Testing) method is designed and fabricated f3r automatic integrity evaluation of large sized industrial reservoirs and pipelines. The developed mobile robot can crawl over the outer surface of the industrial facilities even though the shape of the structures is various and unsymmetric. The robot detects defects such as pinholes, cracks and thickness reduction at the wall of the facilities using EMAT (Electro-Magnetic Acoustic Transducer). Image processing technology for weld line detection at the surface of the target and host programs including defect detecting algorithms are also developed. Automation of defect detection for these kinds of large facilities using mobile robots is helpful to prevent significant troubles of the structures without danger of human beings under harmful environment.

• Journal of Mechanical Science and Technology
• /
• v.15 no.1
• /
• pp.52-60
• /
• 2001

In this paper, as a new measurement method to estimate the change of material condition, the simplified ultrasonic CT system, which uses the information of three directions, that is, $90^{\circ}$, $+45^{\circ}C$and $-45^{\circ}C$ about inspection plane is proposed. Use of simplified CT system has two merits: Firstly, the measurement time is very short compared with general CT. Secondly, it can detect sensitively small defect in vertical or slant direction about inspection plane because the obtained image is CT image calculated from three directions. From these merits, this method can be considered as an effective method to evaluate material conditions. The basic performance of the proposed method was confirmed through several specimens with several simple defects. In order to confirm the applicability of actual NDT, several kinds of welded specimens are investigated. The result showed that the CT image obtained had good agreement with actual defect of specimens.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.6
• /
• pp.635-641
• /
• 2011

In ultrasonic testing of dissimilar metal welds, application of phased array technique in terms of incident beam focusing is not easy because of complicated material structures formed during the multi-pass welding process. Time reversal(TR) techniques can overcome some limitations of phased array since they are self-focusing that does not depend on the geometrical and physical properties of testing components. In this paper, we test the possibility of TR focusing on a defect within anisotropic, heterogeneous austenitic welds. A commercial simulation software is employed for TR focusing and imaging of a side-drilled hole. The performance of time reversed adaptive focal law is compared with those of calculated focal laws for both anisotropic and isotropic welds.

• 제어로봇시스템학회:학술대회논문집
• /
• 2004.08a
• /
• pp.1940-1944
• /
• 2004

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.75-78
• /
• 2001