• Fibers and Polymers
• /
• 제3권4호
• /
• pp.153-158
• /
• 2002

A series of waterborne polyurethanes (WBPU) were prepared from 4,4-dicyclohexylmethane diisocyanate ($H_{12}$MDI),2,2-bis(hydroxylmethyl) propionic acid (DMPA), othylenediarnine (EDA), triethylamine (TEA), and triblock glycol [TBG, ($\varepsilon$-caprolactone)$_{4.5}$-poly(tetramethylene ether) glycol (MW= 2000)-($\varepsilon$-caprolactone)$_{4.5}$: $(CL)_{4.5}$-PTMG-$(CL)_{4.5}$, MW=3000] as a soft segment. Two melting peaks of TBG at about 14$^{\circ}C$ and 38$^{\circ}C$ were observed indicating the presence of two different crystalline domains composed of CL and PTMG dominant component. The effect of soft segment content (60-75 wt%) on the colloidal properties of dispersion, and thermal and mechanical properties of WBPU films, the water vapor permeability (WVP) and water resistance (WR) of WBPU-coated Nylon fabrics, and the adhesive strength of WBPU- coated layer and Nylon fabrics was investigated. As soft segment contents increased, the water vapor permeability of WBPU- coated Nylon fabrics increased from 3615 to 4502 g/$m^2$day, however, the water resistances decreased from 1300 to 500 mm$H_2$O.O.

• 한국염색가공학회지
• /
• 제30권1호
• /
• pp.9-19
• /
• 2018

To prepare bio-inspired antifouling coating materials having similar structure with lotus, self-crosslinkable waterborne polyurethanes emulsions containing paraffin wax (CWPU/P0, 0.25, 0.5, 1.0, 1.5, 2.0, the number indicated the wt% of wax) were prepared by an emulsifier-free/solvent free prepolymer mixing process. The as-polymerized CWPU/P emulsions containing 0 - 1.00wt% of paraffin wax were found to be stable after 4 months, however, CWPU/P emulsions containing 1.50 and 2.00wt% of paraffin wax were unstable within 1 month storage. Considering the stability of emulsions, the optimum paraffin wax content was found to be about 1wt% to obtain stable antifouling coating emulsion material. The surface topology of CWPU/P film samples was characterized by atomic force microscopy (AFM). This study examined the effect of paraffin wax content on the surface roughness, water contact angle/surface energy, water swelling, light transmittance and tensile properties of CWPU/P film samples.

• 폴리머
• /
• 제37권2호
• /
• pp.167-176
• /
• 2013

디올 성분으로 폴리(테트라메틸렌 글리콜)(PTMG)과 함께 말단에 히드록시에틸기를 갖는 폴리디메틸실록산(PDMS-OH)을 혼합하여 사용하면서, 이소시아네이트 화합물로 이소포론 디이소시아네이트를, 수분산성을 부여하기 위해 디메틸올 프로피온산을, 가교제로 트리메틸올프로판을, 사슬연장제로 부탄디올을 사용하여 실록산 성분을 포함하는 선형 및 가교형 수분산성 폴리우레탄(WPU-Si)을 합성하였다. PTMG와 PDMS-OH 혼합 비율을 달리하여 합성한 선형 및 가교형 WPU-Si 에멀젼의 안정성을 분석하였고, 이들을 필름으로 제조하여 표면 특성과 $T_g$, 인장 강신도 변화를 분석하였다. PDMS 함량이 많아질수록 시료의 소수성이 증가하고 $T_g$가 높아졌으며, 파단 인장강도는 증가하고 파단 신장률은 감소하였다.

• 폴리머
• /
• 제33권2호
• /
• pp.175-182
• /
• 2009

Isophorone diisocyanate(IPDI)를 이소시아네이트 화합물로 사용하고, poly (tetramethylene glycol)(PTMG)과 polycarbonate diol(PCD)을 혼합한 폴리올을 사용하여 선형 수분산성 폴리우레탄(WPU)을 합성하고, 이들을 필름으로 캐스팅하여 폴리카보네이트(PC) 함량 변화에 따른 기계적 특성과 염색성, 내알칼리성 변화를 분석하였다. WPU 필름에 PC 성분의 함량이 증가함에 따라 인장강도는 증가하고 파단신도는 감소하였으며, 분산염료에 대한 겉보기 염착량이 감소하였지만, 내알칼리성은 영향이 없었다. 합성한 WPU 용액을 PET 섬유 인공피혁용 함침가공제로 사용한 결과, PTMG 만을 폴리올로 사용한 WPU 수지로 처리한 경우보다 인공괴혁의 마찰견뢰도, 일광견뢰도, 내세탁성 등 염색견뢰도를 크게 증가시킬 수 있었다.

• Elastomers and Composites
• /
• 제36권4호
• /
• pp.262-267
• /
• 2001

내전압 특성과 항균성을 갖는 절연 고무장갑을 제조하기 위해 천연고무 라텍스 (NRL)와 수분산성 폴리우레탄 (PU) 그리고 4급 아민 키토산 (4N-chitosan)을 배합하여 침지법으로 제조하였다. 절연 고무장갑의 기계적인 특성은 폴리우레탄 함량이 증가할수록 인장강도는 증가하였으나 신장율은 저하되었으며, 노화후 인장강도 및 신장율의 잔존율은 폴리우레탄 함량 증가에 따라 증가하였다. 또한, 리칭시간이 증가할수록 내전압 특성이 증가하였으며, 3시간의 리칭시간에서 10000V의 내전압 성능을 나타내었다. 고무장갑에 4N-chitosan을 첨가한 결과 균이 거의 생존하지 않았다.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 2003년도 봄 학술발표회 논문집
• /
• pp.289-290
• /
• 2003

Polymer blending constitutes a most useful method for the improvement or modification of the physicochemical properties of polymeric materials. So polymer blends have gained an increasing interest in both industrial and scientific fields. Some of the polymer blends exhibit unusual properties, unexpected from homopolymers. An important property of a polymer blend is the miscibility of its component, because it affects the mechanical properties, the morphology, its permeability and dogradation [1,2]. (omitted)

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 2003년도 봄 학술발표회 논문집
• /
• pp.287-288
• /
• 2003

Polyurethane(PU) materials have been generally used in the automobile, paint, furniture, adhesive, and textile industries. The use of Waterborne PU was motivated form the environmental point of view, i.e. reduction of solvent emissions into the atmosphere(volatile organic compounds, VOC)[1]. Generally speaking, phase change materials (PCM) have the capability of absorbing or releasing thermal energy to reduce or eliminate heat transfer at the temperature range of the particular temperature stabilizing material[2]. (omitted)

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 2003년도 봄 학술발표회 논문집
• /
• pp.33-35
• /
• 2003

Over the last 30 years, water-swellable and water-insoluble hydrogels have been extensively investigated and developed, leading to a large family of materials which have found use in a wide range of biomedical applications such as carriers of soft tissues, wound healing, ophthalmological applications, membranes for artificial kidney, and materials for blood compatible and other medical devices[1-3]. (omitted)

• 접착 및 계면
• /
• 제22권2호
• /
• pp.39-46
• /
• 2021

가지형 구조의 3-Methyl-1,5-pentanediol (MPD)을 함유한 폴리에스테르 폴리올 및 폴리카보네이트 폴리올을 이용하여 수분산 폴리우레탄(WPU)을 합성하였다. 물리적 특성 비교를 위하여 1,4-butanediol (BD)과 adipic acid로부터 얻어진 폴리에스테르 폴리올 및 1,6-hexane diol (HD)/ 1,4-butanediol (BD)로부터 얻어진 폴리카보네이트 폴리올을 이용하여 수분산 폴리우레탄 수지를 합성하였다. 본 연구는 폴리올 분자구조(소프트 세그먼트의 분자구조)가 WPU의 물리적 특성에 미치는 영향을 조사하였으며, MPD가 함유된 폴리올을 이용하여 합성된 WPU의 경우가 MPD를 함유하지 않은 경우보다 100% 탄성률 및 인장 강도는 낮게 나타났으며, 신장률은 높게 나타났다. MPD 성분을 함유한 WPU 필름의 투명도는 MPD 성분을 함유하지 않은 WPU 필름보다 광 투광도가 우수함을 알 수 있었다.

• 청정기술
• /
• 제24권3호
• /
• pp.190-197
• /
• 2018

3-Methyl-1,5-pentanediol (MPD)/1,6-hexane diol (HD)/1,4-butanediol (BD)과 adipic acid (A)로부터 얻어진 에스터 폴리올(A/BD/MPD 및 A/BD)과 카보네이트 폴리올(C/HD/MPD, C/HD, C/BD)과 에터 폴리올 [poly(tetramethylene oxide glycol), PTMG]과 같은 3 종류의 폴리올을 사용한 수 분산 폴리우레탄(WPU) 에멀젼(평균 입도: 59 ~ 71 nm)을 제조하였다. 본 연구는 폴리올 분자구조(소프트 세그먼트의 분자구조)가 WPU의 특성에 미치는 영향에 대하여 초점을 맞추었다. 소프트 세그먼트 Tg (Tgs), 100% 탄성률 및 인장강도는 카보네이트 폴리올을 사용한 경우가 가장 높고 그 다음이 에스터 폴리올이며 에터 폴리올이 가장 낮게 나타났으나, 신도의 경우는 이와 반대의 경향을 나타내었다. 그리고 MPD가 함유된 폴리올을 이용하여 합성된 WPU의 경우가 MPD를 함유하지 않은 경우보다 Tgs, 100% 탄성률 및 강도는 낮고 신장률은 보다 높게 나타났다. MPD 성분을 함유한 WPU 필름의 투명도는 MPD 성분을 함유하지 않은 WPU 필름보다 광 투광도 및 투명도가 우수함을 알 수 있었으며, 카보네이트 폴리올 기반의 WPU 필름의 광 투광도 및 투명도가 에스터 폴리올 및 에터 폴리올 기반의 WPU 필름보다 약간 우수함을 알 수 있었다.